In order to develop a fabric with excellent flame resistance function,antistatic function,moisture absorption and breathability,the polysulfonamide(PSA)fiber and the flame retardant viscose(FRV)fiber were blended.Mean...In order to develop a fabric with excellent flame resistance function,antistatic function,moisture absorption and breathability,the polysulfonamide(PSA)fiber and the flame retardant viscose(FRV)fiber were blended.Meanwhile,the conductive filaments were used as the core yarn,and then they were made into the core-spun yarn and the fabric at different blending ratios of PSA/FRV.The effects of the blending ratio of PSA/FRV on the mechanical properties and the evenness of the yarn were studied.The effects of the blending ratio of PSA/FRV on mechanical properties,flame retardant properties,antistatic properties,moisture permeability and drape of the fabric were analyzed.With the increase of the blending ratios of PSA/FRV,the strength and the elongation of the core-spun yarn increased firstly and then decreased.Moreover,the evenness of the core-spun yarn was improved,the fabric strength increased firstly and then decreased,the flame resistance decreased,and the antistatic performance improved.These results provide an important basis for the preparation and wide application of fabrics made of PSA/FRV/conductive filament.展开更多
In this research, the flame retardancy of neat alginate fiber, flame retardant viscose fiber (FRV) and alginate/FRV (50/50) blending fibers were investigated by vertical burning and cone calorimeter tests. The ver...In this research, the flame retardancy of neat alginate fiber, flame retardant viscose fiber (FRV) and alginate/FRV (50/50) blending fibers were investigated by vertical burning and cone calorimeter tests. The vertical burning test showed that the afterflame time of alginate fiber was 0 s, but alginate presented serious smoldering behavior with the afterglow time of 605 s and damaged length of 85 mm, while the afterglow time of FRV was 0 s. When the FRV was incorporated into alginate with the weight ratio of 50/ 50, the afterglow time and damaged length were significantly reduced to 85 s and 35 mm, indicating the smoldering of alginate can be effectively decreased. The morphology and chemical structure of the alginate residual demonstrated that it was seriously destroyed during smoldering process, which was ascribed to its relative low initial thermal degradation temperature. Based on the thermal properties analysis, alginate and FRV fibers shared the concurrence of rapid degradation in the same temperature region of 250-300 ℃, through which, the compact and stable char formed by FRV can prevent the heat transmission and suppress the smoldering of alginate. Further, the cone calorimeter results demonstrated that the time to ignition (TTI) significantly increased and peak heat release rate (PHRR) decreased for alginate/FRV (50/50) compared with FRV. With this research, a new method to overcome the smoldering of alginate was proposed by blending with FRV展开更多
基金Open Fund Project of Clothing Engineering Research Center of Zhejiang Province(Zhejiang Sci-Tech University,China)(No.2019FZKF04)Transformation of Scientific and Technological Achievements Programs of Higher Education Institutions in Shanxi Province,China(TSTAP)(No.2020CG014)+2 种基金the MOE(Ministry of Education in China)Project of Humanities and Social Sciences(No.18YJC760051)2017 Shanxi Philosophy and Social Science Project,China(No.201702)Program for the Philosophy and Social Sciences Research(PSSR)of Higher Learning Institutions of Shanxi Province,China(No.201803060)。
文摘In order to develop a fabric with excellent flame resistance function,antistatic function,moisture absorption and breathability,the polysulfonamide(PSA)fiber and the flame retardant viscose(FRV)fiber were blended.Meanwhile,the conductive filaments were used as the core yarn,and then they were made into the core-spun yarn and the fabric at different blending ratios of PSA/FRV.The effects of the blending ratio of PSA/FRV on the mechanical properties and the evenness of the yarn were studied.The effects of the blending ratio of PSA/FRV on mechanical properties,flame retardant properties,antistatic properties,moisture permeability and drape of the fabric were analyzed.With the increase of the blending ratios of PSA/FRV,the strength and the elongation of the core-spun yarn increased firstly and then decreased.Moreover,the evenness of the core-spun yarn was improved,the fabric strength increased firstly and then decreased,the flame resistance decreased,and the antistatic performance improved.These results provide an important basis for the preparation and wide application of fabrics made of PSA/FRV/conductive filament.
基金supported by the Fundamental Research Funds for the Central Universities(No. CUSF-DH-D2016012)
文摘In this research, the flame retardancy of neat alginate fiber, flame retardant viscose fiber (FRV) and alginate/FRV (50/50) blending fibers were investigated by vertical burning and cone calorimeter tests. The vertical burning test showed that the afterflame time of alginate fiber was 0 s, but alginate presented serious smoldering behavior with the afterglow time of 605 s and damaged length of 85 mm, while the afterglow time of FRV was 0 s. When the FRV was incorporated into alginate with the weight ratio of 50/ 50, the afterglow time and damaged length were significantly reduced to 85 s and 35 mm, indicating the smoldering of alginate can be effectively decreased. The morphology and chemical structure of the alginate residual demonstrated that it was seriously destroyed during smoldering process, which was ascribed to its relative low initial thermal degradation temperature. Based on the thermal properties analysis, alginate and FRV fibers shared the concurrence of rapid degradation in the same temperature region of 250-300 ℃, through which, the compact and stable char formed by FRV can prevent the heat transmission and suppress the smoldering of alginate. Further, the cone calorimeter results demonstrated that the time to ignition (TTI) significantly increased and peak heat release rate (PHRR) decreased for alginate/FRV (50/50) compared with FRV. With this research, a new method to overcome the smoldering of alginate was proposed by blending with FRV