The total conductivity of Li-biphenyl-1,2-dimethoxyethane solution（Li_xBp（DME）_（9.65）, Bp = biphenyl, DME = 1,2-dimethoxyethane, x = 0.25, 0.50, 1.00, 1.50, 2.00） is measured by impedance spectroscopy at a tempe...The total conductivity of Li-biphenyl-1,2-dimethoxyethane solution（Li_xBp（DME）_（9.65）, Bp = biphenyl, DME = 1,2-dimethoxyethane, x = 0.25, 0.50, 1.00, 1.50, 2.00） is measured by impedance spectroscopy at a temperature range from 0℃ to 40℃. The Li_（1.50）Bp（DME）_（9.65） has the highest total conductivity 10.7 m S/cm. The conductivity obeys Arrhenius law with the activation energy（E_（a（x=0.50））= 0.014 eV, E_（a（x=1.00））= 0.046 eV）. The ionic conductivity and electronic conductivity of Li_xBp（DME）_（9.65） solutions are investigated at 20℃ using the isothermal transient ionic current（ITIC） technique with an ion-blocking stainless steal electrode. The ionic conductivity and electronic conductivity of Li_（1.00）Bp（DME）_（9.65） are measured as 4.5 mS/cm and 6.6 mS/cm, respectively. The Li_（1.00）Bp（DME）_（9.65） solution is tested as an anode material of half liquid lithium ion battery due to the coexistence of electronic conductivity and ionic conductivity. The lithium iron phosphate（LFP） and Li_（1.5）Al_（0.5）Ti_（1.5）（PO_4）_3（LATP） are chosen to be the counter electrode and electrolyte, respectively. The assembled cell is cycled in the voltage range of 2.2 V-3.75 V at a current density of 50 mA/g. The potential of Li_（1.00）Bp（DME）_（9.65） solution is about 0.3 V vs. Li~＋/Li, which indicates the solution has a strong reducibility. The Li_（1.00）Bp（DME）_（9.65） solution is also used to prelithiate the anode material with low first efficiency, such as hard carbon, soft carbon and silicon.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant No.52315206)the Ministry of Science and Technology of China(Grant No.2016YFB0100100)the Beijing Municipal Science and Technology Commission,China(Grant No.D151100003115003)
文摘The total conductivity of Li-biphenyl-1,2-dimethoxyethane solution（Li_xBp（DME）_（9.65）, Bp = biphenyl, DME = 1,2-dimethoxyethane, x = 0.25, 0.50, 1.00, 1.50, 2.00） is measured by impedance spectroscopy at a temperature range from 0℃ to 40℃. The Li_（1.50）Bp（DME）_（9.65） has the highest total conductivity 10.7 m S/cm. The conductivity obeys Arrhenius law with the activation energy（E_（a（x=0.50））= 0.014 eV, E_（a（x=1.00））= 0.046 eV）. The ionic conductivity and electronic conductivity of Li_xBp（DME）_（9.65） solutions are investigated at 20℃ using the isothermal transient ionic current（ITIC） technique with an ion-blocking stainless steal electrode. The ionic conductivity and electronic conductivity of Li_（1.00）Bp（DME）_（9.65） are measured as 4.5 mS/cm and 6.6 mS/cm, respectively. The Li_（1.00）Bp（DME）_（9.65） solution is tested as an anode material of half liquid lithium ion battery due to the coexistence of electronic conductivity and ionic conductivity. The lithium iron phosphate（LFP） and Li_（1.5）Al_（0.5）Ti_（1.5）（PO_4）_3（LATP） are chosen to be the counter electrode and electrolyte, respectively. The assembled cell is cycled in the voltage range of 2.2 V-3.75 V at a current density of 50 mA/g. The potential of Li_（1.00）Bp（DME）_（9.65） solution is about 0.3 V vs. Li~＋/Li, which indicates the solution has a strong reducibility. The Li_（1.00）Bp（DME）_（9.65） solution is also used to prelithiate the anode material with low first efficiency, such as hard carbon, soft carbon and silicon.
