Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure

A fluorine-containing polyacrylate copolymer emulsion was synthesized by a seed emulsion polymerization method, in which methyl methacrylate （MMA） and butyl acrylate （BA） were used as main monomers and hexafluorobutyl methacrylate （HFMA） as fluorine-containing monomer. The structure and properties were characterized by Fourier transform infrared spectrum （FT-IR）, transmission electron microscopy （TEM）, particle size analysis, X-ray photoelectron spectroscopy （XPS）, contact angle （CA）, differential scanning calorimetry （DSC） and thermogravimetry （TG） analysis. The FTIR and TEM results showed that HFMA was effectively involved in the emulsion copolymerization, and the formed emulsion particles had a core-shell structure and a narrow particle size distribution. XPS and CA analysis revealed that a gradient concentration of fluorine existed in the depth profile of fluorine-containing emulsion film which was richer in fluorine and more hydrophobic in one side. DSC and TG analysis also showed that a clear core-shell structure existed in the fluorine-containing emulsion particles, and their film showed higher thermal stability than that of fluorine-free emulsion.

Trade-offs between ion-conducting and mechanical properties: The case of polyacrylate electrolytes

Polymer electrolytes(PEs)have been long recognized as the key materials to enable energy-dense batteries and render flexible energy devices practically viable,owing to their chemical and mechanical reliability.However,much of their promise is yet to be realized.The roomtemperature ion conductivity of existing PEs still falls short of the implementation criterion of 10^(-4) S cm^(-1) on the promise of acceptable mechanical properties,thereby precluding their practical application.The twin but inversely related duties of polymers,that is,functioning as both an ion-conducting medium and a structural backbone,underlie this issue but are less elucidated systematically.The polyacrylate(PA)family is among promising polymer matrices on account of ester polarity,electrode compatibility,chemical tunability,and mechanical durability.The extensive applicability of PA in plasticized gels,dry solids,and emerging composites makes PA-based PEs representative to illustrate the trade-off between ion conduction and mechanical strength.We herein seek to outline the stated long-standing conflict exemplified by PA-based PEs,focusing on crucial strategies toward balancing and reconciling the two mutually exclusive properties,with the intention of offering designing guidelines for next-generation PEs.

Quantitative lithium substitution of carboxyl hydrogens in polyacrylic acid binder enables robust SiO electrodes with durable lithium storage stability

The design of advanced binders plays a critical role in stabilizing the cycling performance of large-volume-effect silicon monoxide(SiO)anodes.For the classic polyacrylic acid(PAA)binder,the self-association of-COOH groups in PAA leads to the formation of intramolecular and intermolecular hydrogen bonds,greatly weakening the bonding force of the binder to SiO surface.However,strengthening the binder-material interaction from the perspective of binder molecular regulation poses a significant challenge.Herein,a modified PAA-Li_(x)(0.25≤x≤1)binder with prominent mechanical properties and adhesion strength is specifically synthesized for SiO anodes by quantitatively substituting the carboxylic hydrogen with lithium.The appropriate lithium substitution(x=0.25)not only effectively increases the number of hydrogen bonds between the PAA binder and SiO surface owing to charge repulsion effect between ions,but also guarantees moderate entanglement between PAA-Li_x molecular chains through the ion-dipole interaction.As such,the PAA-Li_(0.25)/SiO electrode exhibits exceptional mechanical properties and the lowest volume change,as well as the optimum cycling(1237.3 mA h g^(-1)after 100cycles at 0.1 C)and rate performance(1000.6 mA h g^(-1)at 1 C),significantly outperforming the electrode using pristine PAA binder.This work paves the way for quantitative regulation of binders at the molecular level.

Adsorption of sodium polyacrylate at interface of dicalcium silicate-sodium aluminate solution

The adsorption isotherm of sodium polyacrylate on dicalcium silicate（2CaO-SiO2） in sodium aluminate solution at 80 ℃ was studied.The type of surface adsorption of sodium polyacrylate is saturated adsorption,and the adsorption behavior belongs to L-type,according with the monolayer adsorption model of Langmuir equation.The surface coverage of sodium polyacrylate is 1.06 mol/μm2.The relation curve between the surface pressure and the molecular area of adsorption film was obtained by Gibbs formula.The variation of interfacial energy caused by adsorption as well as the relationship between the relation curve and the type of adsorption was discussed.

SYNTHESIS AND APPLICATION OF NEW DETERGENT BUILDER POLYACRYLATE SODIUM

The low molecular weight polyacrylate sodium (PAA Na) detergent builder was synthesized with K 2S 2O 8 as initiator in a neutral aqueous medium. The influences of reaction conditions on the viscosity average molecular weight were studied. The critical value of synthetic PAA Na inhibiting the precipitation of CaCO 3 was determined and compared with that of other common builders. It is confirmed from SEM graphs that PAA Na can make CaCO 3 crystal defective. Washing tests show synthetic PAA Na can partially replace sodium tripolyphosphate (STPP) and is a potential polymeric detergent builder in low phosphate powder detergents.

QSPR Study on the Glass Transition Temperature of Polyacrylates

Structural parameters of 22 polyacrylic compounds were computed at two levels using Hartree-Fock and DFT methods. Based on the experimental data of glass transition temperature （Tg）, four-parameter （energy of the lowest unoccupied molecular orbital （ELoMO）, the highest positive charge （Qmax^＋）, dipole moments（μ） and the next highest occupied molecular orbital （ENLOMO）） dependent equations were developed using structural parameters as theoretical descriptors. Especially, Tg dependent equation calculated at the HF/6-31G（d） level is more advantageous than others in view of their correlation and predictive abilities. This dependent equation was validated by variance inflation factors （VIF） and t-test methods.

Influence of Carboxyl Groups on the Particle Size and Rheological Properties of Polyacrylate Latices

The PAL was synthesized with BA,MMA and some monomers containing carboxyl groups（for example,acrylic acid（AA） and methacrylic acid（MAA）） as co-monomers by semi-continuous seeded emulsion polymerization technique.The influences of alkalinization temperature,the feeding manner of AA or MAA on the particles size,rheological properties and carboxyl distribution of the latex were discussed,and the rheological mechanism was analyzed.The experimental results show that the PAL system has preferable viscosity and particle size when the alkalinization temperature is 50 ℃.Different distribution of carboxyl group in the particles and different resultant rheological properties are obtained by different feeding manner of AA or MAA into the system.The TEM images show that the particle is a smooth globe with carboxyl group concentrating on the surface and stabilized with electric double layer and nonionic adsorbed layer.The concentration of carboxyl functional group on the surface of particles can be achieved by the specific polymerization technique.The rheologyical properties are determined by accretion of particle volume and variation of the two phase volume ratio resulted from the carboxyl group spreading layer.

SYNTHESIS, CROSSLINKING MECHANISM AND PROPERTIES OF A POLYACRYLATE/POLYURETHANE COMPOSITE COATING

A polyacrylate/polyurethane (P(A)/P(U)) composite coating has been prepared by crosslinking an acetoacetylated polyacrylate with a vinylic group terminated polyurethane at room temperature. A model Michael reaction between ethyl acetoacetate (EAA) and methyl acrylate (MA) was designed to study the crosslinking mechanism. It was found that the two active hydrogen atoms in acetoacetyl group can both add to vinylic groups and the yield of mono-and bis-adducts are much affected by the molar ratio of acetoacetyl to vinylic groups. Higher crosslinking degree and better properties could be obtained with decreasing the molar ratio of the two active groups from 1/1 to 0.6/1 in the composite coatings.

Properties of Polyacrylate Latex Prepared Under Different Emulsified Systems

The polyacrylate latexes were synthesized via pre-emulsified and semi-continuous seeded emulsion polymerization technology when conventional surfactant or polymerizable surfactant was used as emulsifiers. The resultant latexes and their films were characterized with the contact angle determinator and rheometer. Effect of the polymerizable surfactant on water resistance, stability and rheology of the latex was studied. Results show that the water resistance of film is increased first then decreased with the increase of the amount of the polymerizable surfactant. There exists the optimum value of the amount of the polymerizable surfactant for the water resistance of the film. In comparison with the latex prepared with the conventional surfactant, both the mechanical stability and the freezing-thaw stability of the latex are improved when the polymerizable surfactant is used during the course of the emulsion polymerization. The resultant latex has rheological properties of pseudo-plastic fluid and belongs to non-Newtonian fluid.

Investigation on the Use of the Weakly Basic Polyacrylate Anion-Exchanger Amberlite IRA-68 for Sorption and Separation of Iminodiacetate Complexes of Rare Earth Elements

Based on the determined affinity series of rare earth element complexes with IMDA for the anion-exchangers, purification of macroquantities of Nd 3+ from Y 3+, Sm 3+ from Ho 3+, La 3+ from Nd 3+ and La 3+ from Pr 3+ on the weakly basic gel anion-exchanger Amberlite IRA-68 was studied. Using the presented method on 1 L of Amberlite IRA-68 in the acetate form, it is possible to obtain about 240 g Nd 2O 3 purified from Y 2O 3. Great difference in affinity of La 3+ and Nd 3+ as well as Pr 3+ complexes for this anion-exchanger in the acetate form indicates the possibility of applying this process for purification of lanthanum on the increased scale. On 1 L of Amberilte IRA-68 in the acetate form it is possible to obtain about 1125 g La 2O 3 purified from Nd 2O 3. On the basis of these results it can be assumed that unique properties of polyacrylate anion-exchangers enable their application for separation of rare earth elements.

Determination of Ni^(2+) in Waters with Sodium Polyacrylate as a Binding Phase in Diffusive Gradients in Thin-films

An aqueous solution containing sodium polyacrylate（PAAS） was used in diffusive gradient in thin-films technique（DGT） to measure DGT-labile Ni2＋ concentrations.The DGT devices（PAAS DGT） were validated in four types of solutions,including synthetic river water containing metal ions with complexing EDTA or that without complexing EDTA,natural river water（Ling River,Jinzhou,China） spiked with Ni2＋,and an industrial wastewater （Jinzhou,China）.Results show that only free metal ions were measured by PAAS DGT,recovery=97.36% in the solutions containing only free metal ions,recovery=49.62% in a solution with metal/EDTA molar ratio of 2：1 and recovery=0 in the solutions with metal/EDTA molar ratios of 1：1 and 1：2.These indicated that the complexes of Ni-EDTA were DGT-inert.The DGT performance in spiked river water（recovery=18.24%） and in industrial wastewater（recovery=12.25%） were investigated,which indicated that the measurement of metals by this DGT device did not include the humic substances complexed fractions of metals.The binding properties of PAAS DGT for Ni2＋ were investigated under different conditions of pH value and ionic strength.Conditional stability constants（lgK） of PAAS-Ni complexes were also evaluated.

Studies on the Morphology of Natural Rubber/Polyacrylate Interpenetrating Polymer Networks

The interpenetrating polymer network(IPN) systems have attracted a lot of attention because of their unique two-phase structure and properties. There have been many publications concerning the IPNs in which poly (isoprene) (PIP) or polyacrylates (PAC) is formed as one of the networks.In the present study, Four serles of natural rubber(NR)/PAC IPNs were prepared and their morphologies were investigated with dynamic mechanics analysis(DMA) and transmission electron microscopy (TEM).

Research progress on preparation and purification of fluorine-containing chemicals in lithium-ion batteries

With the development of digital products,electric vehicles and energy storage technology,electronic chemicals play an increasingly prominent role in the field of new energy such as lithium-ion batteries.Electronic chemicals have attracted extensive attention in various fields.Characteristics of high-end electronic chemicals are high purity and low impurity content,which requires a very strict separation and purification process.At present,crystallization is a key technology for their separation and purification of electronic chemicals.In this work,the representative fluorine-containing compounds in cathode and anode materials,separator and electrolyte of lithium-ion batteries are introduced.The latest technologies for the preparation and purification of four kinds of fluorine-containing battery chemicals by crystallization technology are reviewed.In addition,the research prospects and suggestions are put forward for the separation of fluorine-containing battery chemicals.

STUDIES ON THE BLEND OF POLYACRYLATE EMULSIONS AND TACKIFIER RESIN EMULSIONS

A series of polyacrylate emulsions were blended with tackifier resin emulsions such as modified rosin emulsion, C5 resin and C9 resin emulsion. The miscibility of the polyacrylates and tackifier resins was investigated by means of SEM and visual observation. The phase diagrams of the miscibility change systematically with the polarity of polyacrylates and tackifier resins. The influence of the content of the tackifier resins on the adhesion properties of the; polyacrylate emulsions were also studied. The results show that the 180 degrees C peel strength is improved as the amount of the tackifier resin increases and comes to a maximum at a specific content. The ball tack property decreases slightly and the hold strength changes complicatedly as the tackifier resin increases.

SYNTHESIS AND CHARACTERIZATION OF A NOVEL FLUORINE-CONTAINING HYDROPHOBICALLY ASSOCIATING POLYMER

In this article, the synthesis and characterization of a novel fluoromonomer and its copolymer with acrylamide is reported. 2-perfluoroamyl-4-hydroxylquinoline 2 was synthesized from ethyl 2, 2-dihydroperfluoroheptanoate in high yields. The monomer 4 was then synthesized from 2 in two steps readily in high yields. Synthesis and characterization of copolymers of acrylamide (AM) and the fluoromonomer were investigated. The composition and intrinsic viscosity of these copolymers were studied. It was found that the rheological properties of aqueous solutions of polyacrylamide were modified significantly when a small proportion of the fluoromonomer 4 was incorporated on investigating the viscosity-concentration profiles, pseudoplasticity of these solutions and the effect of the presence of surfactant. These results could be explained by the hydrophobic association of the fluorocarbon segments in the aqueous solutions of these copolymers.

Design and Synthesis of Novel Fluorine-containing Acrylates

A series of novel fluorine-containing acrylates 6a-6g were synthesized via the condensation of ethyl cyanoacetate and trifluoroacetic anhydride, followed by chloridization and the coupling reaction with amines. These new compounds exhibited some biological activity as preliminary bioassay indicated. A plausible reaction mechanism was outlined and discussed.

Concentration and Temperature Dependence of Electrical Conductivity in Thermally Stable Chromium Polyacrylate

Electrical conductivity of chromium polyacrylate with dopant concentration 30, 40 and 50 wt-% of chromium has been measured over a broad range of temperatures (303 K to 383 K).The electrical conductivity shows dependence on temperature, as well as, level of doping. The conductivity is considered to be due to thermal hopping motion of localized charge carriers,which are believed to be polarons, in the temperature range 303 K to 323 K and for T>343 K,whereas. it is metal-like in the temperature range 323 K to 343 K

Damping properties of silicone rubber/polyacrylate sequential interpenetrating networks

Silicone rubber/polyacrylate sequential interpenetrating polymer networks(IPNs) were prepared by silicone rubber sheet dipped into the solution composed of different acrylate monomers and benzoyl peroxides(BPOs) for different time at room temperature and then acrylate polymerized at 80℃for 2 h. The molecular structure and damping properties of sequential IPNs were studied by means of FT-IR and dynamic mechanical analysis(DMA), respectively. The FT-IR spectrum shows that polyacrylate distributes unevenly along the thickness direction of IPNs, i.e. the concentration of polyacrylate decreases from the midst to the surface of the IPNs. The DMA shows that cold crystallization of silicone in the temperature range from -47℃to -30℃is reduced and loss factor of IPNs is improved after interpenetrating with polyacrylate. This suggestes that IPNs can be used as damping materials.

Michael Addition of Nitroalkanes to CF_3CCl_2COCH=CHPh: A Facile Route to Fluorine-containing γ-Nitro Ketones

Nitroalkanes react smoothly with CF_3CCl_2COCH=CHPh via Michael addition in the presence of inorganic bases such as KF/Al2O3 or K2CO3, giving fluorinecontaining γ-nitro ketones in good yields.

Synthesis and Characterization of Fluorine-containing Poly(ether ether ketone)s

Poly（ether ether ketone）s（PEEK） are a class of high performance engineering thermoplastics known for their excellent thermal, mechanical, and electrical properties. This class of advanced materials has currently received considerable attention for potential application in aerospace, electronics, automobile and other high technology fields. However, it is difficult for PEEK to be processed because of their high melting temperature and poor solubility.