Structure Design and Properties of Three-Layer Particleboard Based on High Voltage Electrostatic Field(HVEF)

In this study,the effects of three different particle sizes of wood wastes(A=–8+12 mesh;B=–12+20 mesh;C=–20+30 mesh)and factory shavings(D)on the properties of particleboard were investigated.According to the test results,three-layer particleboard was designed.Particleboard face layers made with mixture of A,B,and C.The core layer made with D.The ratio of core layer to face layers is 50:50.Three-layer particleboard were fabricated with 12%urea-formaldehyde(UF)resins and three different high voltage electrostatic field intensities(0 kv,30 kv,60 kv).The internal bond(IB)strength,modulus of rupture(MOR),modulus of elasticity(MOE),thickness swelling(TS),and water absorption(WA)of particleboard were evaluated.The density distribution of the three-layer particleboard were examined by vertical density profiles(VDP),and the bonding mechanism and functional groups changes in the particles were analyzed by FTIR analysis.The results showed that HVEF treatment intensity play a remarkable role in properties of particleboard.The particleboard with higher electrostatic field intensities treatment has higher MOE,MOR,IB,and TS.Under HVEF treatment(60 kv),the MOR,modulus of MOE,and IB of three-layer particleboard were 23.61 N/mm^(2),2787.09 N/mm^(2),and 0.86 N/mm^(2),respectively.FTIR indicated that the surface activity of wood particles was increased electric field treatment.