Detection of Frost-Resistance Property of Large-Size Concrete Based on Impact-Echo Method
1
作者 Qi Feng Zhengyue Ren Dan Wang 《Structural Durability & Health Monitoring》 EI 2023年第1期71-88,共18页
The dynamic elasticity modulus(Ed)is the most commonly used indexes for nondestructive testing to represent the internal damage of hydraulic concrete.Samples with a specific size is required when the transverse resona... The dynamic elasticity modulus(Ed)is the most commonly used indexes for nondestructive testing to represent the internal damage of hydraulic concrete.Samples with a specific size is required when the transverse resonance method was used to detect the Ed,resulting in a limitation for field tests.The impact-echo method can make up defects of traditional detection methods for frost-resistance testing,such as the evaluation via the loss of mass or strength.The feasibility of the impact-echo method to obtain the relative Ed is explored to detect the frost-resistance property of large-volume hydraulic concretes on site.Results show that the impact-echo method can replace the traditional resonance frequency method to evaluate the frost resistance of concrete,and has advantages of high accuracy,easy to operate,and not affecting by the aggregate size and size effect of samples.The dynamic elastic modulus of concrete detected by the impact-echo method has little difference with that obtained by the traditional resonance method.The one-dimensional elastic wave velocity of concrete has a good linear correlation with the transverse resonance frequency.The freeze-thaw damage occurred from the surface to the inner layer,and the surface is expected to be the most vulnerable part for the freeze-thaw damage.It is expected to monitor and track the degradation of the frost resistance of an actual structure by frequently detecting the P-wave velocity on site,which avoids coring again. 展开更多
关键词 Impact-echo method frost-resistance property dynamic elastic modulus ED elastic wave velocity transverse resonance frequency
下载PDF
Mechanical and Frost-resistance Properties of Rural Area Building Waste Hollow Bricks 被引量:1
2
作者 刘军 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2010年第6期1017-1021,共5页
Serving as recycled coarse aggregate,the pretreated rural building waste was added into the concrete hollow bricks in the varying replacement of 0,20%,40%,60%,80% and 100%.By testing its compressive strength,flexural ... Serving as recycled coarse aggregate,the pretreated rural building waste was added into the concrete hollow bricks in the varying replacement of 0,20%,40%,60%,80% and 100%.By testing its compressive strength,flexural strength,mass and strength loss after freeze-thaw cycles,the impact of the different replacement on mechanical and frost-resistance properties of concrete hollow bricks was presented through SEM analysis.The experimental results show that,with the increase in recycled coarse aggregate replacement rate,the mechanical and frost-resistance properties show a downward trend;when the replacement rate is 40%,28 d compressive strength and flexural strength of concrete hollow brick demonstrate the good peak value which meet the requirement of the national standard for ordinary small concrete hollow bricks;the interfacial structures of the pretreated recycled concrete is more complicated than those of concrete made of natural aggregate,but the former enjoys better interface bonding and tight structure. 展开更多
关键词 replacement rate waste clay brick mechanical properties frost-resistance properties MICROSTRUCTURE
下载PDF
The Frost-resisting Durability of High Strength Self-Compacting Pervious Concrete in Deicing Salt Environment 被引量:10
3
作者 封金财 ZONG Ningwen +3 位作者 ZHU Pinghua 刘惠 YAO Lan GENG Jiang 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2020年第1期167-175,共9页
A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%,... A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment. 展开更多
关键词 high strength SELF-COMPACTING pervious concrete top-bottom interconnected pores heavy loading road frost-resisting DURABILITY DEICING salt ENVIRONMENT
下载PDF
Utilization of Dredged River Sediment in Preparing Autoclaved Aerated Concrete Blocks
4
作者 Kai Zhang Qunshan Wei +5 位作者 Shuai Jiang Zhemin Shen Yanxia Zhang Rui Tang Aiwu Yang Christopher WKChow 《Journal of Renewable Materials》 SCIE EI 2022年第11期2989-3008,共20页
In this study,the dredged river sediment,soft texture and fine particles,is mixed with other materials and transformed into eco-friendly autoclaved aerated concrete(hereinafter referred to as AAC)blocks.The results in... In this study,the dredged river sediment,soft texture and fine particles,is mixed with other materials and transformed into eco-friendly autoclaved aerated concrete(hereinafter referred to as AAC)blocks.The results indicated the bricks produced under the conditions of 30%–34%dredged river sediment,24%cement,10%quick lime,30%fly ash,2%gypsum and 0.09%aluminum powder with 0.5 water to material ratio,2.2 MPa autoclave pressure and 6 h autoclave time,the average compressive strength of 4.5 MPa and average dry density of 716.56 kg/m³were obtained,the two parameters(strength&density)both met the requirement of national industry standard.At the same time,the contents of dredged river sediment,cement,lime,fly ash,gypsum and aluminum powder were 15%,48%,20%,15%,2%and 0.09%,respectively,and the non-AAC block made of 0.5 water to material ratio,the average compressive strength of 3.1 MPa and average dry density of 924.19 kg/m³were obtained,the two parameters(strength&density)also met the requirement of national industry standard.In addition,the AAC block’s phase composition and morphology were micro-analyzed by SEM and XRD,the main substances in AAC block were found to be tobermorite and CSH,Among them,the chemical bond between Si-O-Si and Al-O-Al is broken,Al-O-Si is regenerated,Al substituted tobermorite with better strength is formed,and the compressive strength of AAC is further improved. 展开更多
关键词 Autoclaved aerated concrete dredged river sediment compressive strength frost-resistance moisture content MICROSTRUCTURE