Effects of Chemical Composition and Microstructure on Exudation of Fused Cast AZS Refractory Materials

The fused cast alumina-zirconia-silica(AZS)refractory is an indispensable material of the glass melting furnace,because of its outstanding corrosion resistance and low pollution to glass production.The exudation is one important index to evaluate the performance of fused cast AZS refractory products.In order to study the effects of chemical composition and microstructure on the exudation of fused cast AZS refractory materials,three types of fused-cast AZS refractory bricks(AZS33#,AZS36#and AZS41#)were selected from several companies as the research object,and their composition,bulk density,apparent porosity,the value of exudation,static corrosion rate and microstructure were discussed.The results show that the chemical composition,especially the content of SiO2 and Na2O,and the distribution of zirconia would greatly affect the content and viscosity of glass phase,thus affecting the glass exudation.This work will provide technical reference for the development of low exudation AZS refractories.

熔铸AZS砖溶蚀的显微结构

借助扫描电镜、能谱仪和X射线衍射研究了玻璃熔窑池壁用熔铸Al2O3–ZrO2–SiO2(AZS)大砖蚀变后残砖的显微结构变化。在玻璃液?砖间界面后形成了一厚度<1mm的蚀变层,而在25mm的厚度层内显微结构变化不大。蚀变层液相基质吸收了较多的Na2O,CaO,K2O,共晶体的刚玉基晶完全溶解并生成霞石。共晶中的细晶斜锆石呈分散状晶体分布于液相基质中,意味着斜锆石不易溶解。展示了一些新生相的细微形貌特征。

熔铸AZS耐火材料冷却过程的热应力研究

熔铸AZS材料是一类非常重要的耐火材料,在其制备过程中常常因为热应力过大而损坏。运用有限元法模拟AZS铸件冷却过程中的热应力场,分别研究了加设保温层、铸模材料的热导率以及热对流系数对热应力的影响。计算结果表明:在铸模与砂箱之间加设保温层能够有效降低铸件本身的热应力;改变铸模材质的热导率不仅影响热应力的峰值,而且影响峰值出现的早晚以及高应力水平维持的时间长短;热对流系数对应力峰值以及峰值出现时间早晚的影响都不明显,只影响高应力水平维持的时间长短。

电熔铸锆刚玉砖玻璃相中铁钛铝硼的物理状态研究

利用电子自旋共振谱(EsR)、荧光X射线化学位移法和红外光谱等实验方法,分析了电熔铬刚玉砖(简称AZS)玻璃相中铁、钛的价态以及Fe^(3+),Al^(3+),B^(3+)的配位态随氧化程度的变化规律。采用ESR谱研究了AZS砖的氧化程度,并从玻璃结构的角度探讨了氧化程度影响玻璃相抗高温渗出性能的原因。

国产33~#熔铸AZS砖在平板玻璃液中损毁的研究

本文应用化学分析、偏光显微镜、扫描电镜、电子探引及X射线衍射分析等研究了国产33#熔铸AZS砖在平板玻璃液中的侵蚀层.并在1 500℃无玻璃液侵蚀条件下,进行了模似实验,考察了原砖的晶相变化规律.结果表明:33#熔铸AZS砖的损毁实质上是多晶相材料的溶解过程.斜锆石集合体形态不理想是国产砖损毁过快的主要原因.