Since the traditional Miner rule ignores the influence of the load sequence on the fatigue life, the fuzzy rules are used to analyze the fuzziness of the fatigue damage caused by the stress nearby the fatigue limit un...Since the traditional Miner rule ignores the influence of the load sequence on the fatigue life, the fuzzy rules are used to analyze the fuzziness of the fatigue damage caused by the stress nearby the fatigue limit under different load sequences. The improved fuzzy Miner rule can reflect the influence of the load sequence on the fatigue life. Results of the example show that the prediction error can be reduced from 61.6% to 21.7%.展开更多
Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic load...Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic loading was proposed. The specimens of aluminum alloy LY12-CZ soaked in corrosive liquid for different times were tested under the constant amplitude cyclic loading to obtain S-N curves. The test was carried out to verify the proposed cumulative fatigue damage rule under the different combinations among corrosion time, loading level, and the cycle numbers. It was shown that the predicted residual fatigue lives showed a good agreement with the experimental results and the proposed rule was simple and can be easily adopted.展开更多
Firstly, constant amplitude P-S_a-S_m-N_c surface family is established.Secondly, four basic assumptions, i.e., monotonically increasing, non-coupling, separability andnonintersecting of fatigue damage accumulation ar...Firstly, constant amplitude P-S_a-S_m-N_c surface family is established.Secondly, four basic assumptions, i.e., monotonically increasing, non-coupling, separability andnonintersecting of fatigue damage accumulation are proposed from the viewpoint of both damagemechanics and fracture mechanics. Then the individual isodamage D-S_a-S_m-N surface under constantamplitude loading is constructed and the two-dimensional individual Miner's rule is derived.Consequently, the two-dimensional probabilistic Miner's rule (TPMiner) is established and proved fora population subjected to variable amplitude loading. Finally, with successfully experimentverification, TPMiner proves be to very useful and feasible in fatigue reliability theory.展开更多
基金the National Natural Science Foundation of China(60472118)~~
文摘Since the traditional Miner rule ignores the influence of the load sequence on the fatigue life, the fuzzy rules are used to analyze the fuzziness of the fatigue damage caused by the stress nearby the fatigue limit under different load sequences. The improved fuzzy Miner rule can reflect the influence of the load sequence on the fatigue life. Results of the example show that the prediction error can be reduced from 61.6% to 21.7%.
基金supported by the National Natural Science Foundation of China(No.10377007)
文摘Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic loading was proposed. The specimens of aluminum alloy LY12-CZ soaked in corrosive liquid for different times were tested under the constant amplitude cyclic loading to obtain S-N curves. The test was carried out to verify the proposed cumulative fatigue damage rule under the different combinations among corrosion time, loading level, and the cycle numbers. It was shown that the predicted residual fatigue lives showed a good agreement with the experimental results and the proposed rule was simple and can be easily adopted.
基金This project is supported by National Natural Science Foundation of China(No.59605010,No.59979015)Selected from Proceedings of 2000 the First International Conference on Mechanical Engineering
文摘Firstly, constant amplitude P-S_a-S_m-N_c surface family is established.Secondly, four basic assumptions, i.e., monotonically increasing, non-coupling, separability andnonintersecting of fatigue damage accumulation are proposed from the viewpoint of both damagemechanics and fracture mechanics. Then the individual isodamage D-S_a-S_m-N surface under constantamplitude loading is constructed and the two-dimensional individual Miner's rule is derived.Consequently, the two-dimensional probabilistic Miner's rule (TPMiner) is established and proved fora population subjected to variable amplitude loading. Finally, with successfully experimentverification, TPMiner proves be to very useful and feasible in fatigue reliability theory.