Heterojunction bipolar transistor (HBT) is of great interest for the application to microwave power and analog circuits. As known, decreasing bandgap energy of the base layer in HBT can result in a smaller turn-on vol...Heterojunction bipolar transistor (HBT) is of great interest for the application to microwave power and analog circuits. As known, decreasing bandgap energy of the base layer in HBT can result in a smaller turn-on voltage. Using InGaAs as a base material in GaAs HBT is a possible approach to achieve the aim. In this work, a novel InGaP/InGaAs/GaAs double heterojunction bipolar transistor (DHBT) structure with an InGaAs base was designed and grown by gas source molecular beam epitaxy (GSMBE). High-quality InGaAs/GaAs hetero epi-layers and a good doping figure were obtained through optimizing the layer structure and the growth condition. The DHBT devices of a 120 μm×120 μm emitter area were fabricated by normal process and the good DC performance was obtained. A breakdown voltage of 10 V and an offset voltage of just 0.4 V were achieved. These results indicate that the InGaP/InGaAs/GaAs DHBT is suitable for low power-dissipation and high power applications.展开更多
利用深能级瞬态谱(DLTS)研究了气源分子束外延(GSMBE)生长的InP1-xBix材料中深能级中心的性质。在未有意掺杂的InP中测量到一个多数载流子深能级中心E1,E1的能级位置为Ec-0.38 e V,俘获截面为1.87×10^(-15)cm^2。在未有意掺杂的InP...利用深能级瞬态谱(DLTS)研究了气源分子束外延(GSMBE)生长的InP1-xBix材料中深能级中心的性质。在未有意掺杂的InP中测量到一个多数载流子深能级中心E1,E1的能级位置为Ec-0.38 e V,俘获截面为1.87×10^(-15)cm^2。在未有意掺杂的InP0.9751Bi0.0249中测量到一个少数载流子深能级中心H1,H1的能级位置为Ev+0.31 eV,俘获截面为2.87×10^(-17)cm^2。深中心E1应该起源于本征反位缺陷PIn,深中心H1可能来源于形成的Bi原子对或者更复杂的与Bi相关的团簇。明确这些缺陷的起源对于InPBi材料在器件应用方面具有重要的意义。展开更多
文摘Heterojunction bipolar transistor (HBT) is of great interest for the application to microwave power and analog circuits. As known, decreasing bandgap energy of the base layer in HBT can result in a smaller turn-on voltage. Using InGaAs as a base material in GaAs HBT is a possible approach to achieve the aim. In this work, a novel InGaP/InGaAs/GaAs double heterojunction bipolar transistor (DHBT) structure with an InGaAs base was designed and grown by gas source molecular beam epitaxy (GSMBE). High-quality InGaAs/GaAs hetero epi-layers and a good doping figure were obtained through optimizing the layer structure and the growth condition. The DHBT devices of a 120 μm×120 μm emitter area were fabricated by normal process and the good DC performance was obtained. A breakdown voltage of 10 V and an offset voltage of just 0.4 V were achieved. These results indicate that the InGaP/InGaAs/GaAs DHBT is suitable for low power-dissipation and high power applications.
文摘利用深能级瞬态谱(DLTS)研究了气源分子束外延(GSMBE)生长的InP1-xBix材料中深能级中心的性质。在未有意掺杂的InP中测量到一个多数载流子深能级中心E1,E1的能级位置为Ec-0.38 e V,俘获截面为1.87×10^(-15)cm^2。在未有意掺杂的InP0.9751Bi0.0249中测量到一个少数载流子深能级中心H1,H1的能级位置为Ev+0.31 eV,俘获截面为2.87×10^(-17)cm^2。深中心E1应该起源于本征反位缺陷PIn,深中心H1可能来源于形成的Bi原子对或者更复杂的与Bi相关的团簇。明确这些缺陷的起源对于InPBi材料在器件应用方面具有重要的意义。