Non-UV germicidal activity of fresh TiO_2 and Ag/TiO_2

Fresh TiO2 was found to possess a strong germicidal activity even without UV irradiation. Live Yeast （Saccharomyces cerevisiae） cells in contact with fresh TiO2 were found deformed and dead after 15min contact. The cause of germicidal activity was discussed from the observed cell deformation, lysis and increased absorption at 1680 cm^-1 in FT-IR spectra of the affected cells, which proved the oxidizing effect of fresh TiO2 to cells. The deformation caused by the stretching of cell wail and pressure built-up inside the cell, led to cell burst and release of intracellular materials. The degree of cell deformation was found positively related with the wetting property of TiO2. Cells are negatively charged, for Gram-negative cell （thinner ceil wail）, a higher germicidal effect was observed than Gram-positive cells. The germicidal effect of TiO2 gradually decreased after exposure to air at room temperature, as the wetting property decreased. This kind of germicidal activity was more effective compared to other germicidal process such as UVA/TiO2 or Ag＋. This shed light on designing new germicidal material either maintained by visible light irradiation, or by oxidation effect generated by reactive oxygen species.

Non-UV based germicidal activity of metal-doped TiO_2 coating on solid surfaces

A stain-based screening method was developed to screen different catalyst coatings for their germicidal activity. A Baclight dead/live bacteria viability kit （invitrogen, molecular probes） was used for staining the cell. The screening was carried out following a standard procedure. This included loading cell suspension to solid surface and maintaining contact for 30 min, then staining with a mixture containing dyes. The stained cells were observed using an epifluorescent microscope and photographed with a CCD camera under UV. Metal-doped TiO2 coatings on AI plates were prepared and tested for non-UV germicidal activity without using UV. It was tested using model microorganisms such as Bakers Yeast （Saccharomyces cerevisiae）, Bacillus subtilis, Pseudomonas putida, and Escherichia coli. On the basis of the germicidal activity of catalyst and the degree of damage caused to the cells, the stained cells may appear green （viable）, green with red or yellow nuclei and yellow （compromised） or red （nonviable）. According to their stained color, cells were counted to calculate the percentage of dead, live, and compromised cells. Compromised cells are cells that grow very slowly after reculturing indicating a degree of reversible cell damage. Screening the germicidal activity using this staining method is accurate and efficient, and requires less time than the culture-based method. A modification to the procedure for measuring germicidal activity of rough surfaces or fibrous coatings was developed. Both TiO2 and metal-doped TiO2 （Ag, Pt, Au, Cu） possess non-UV based germicidal activity. The germicidal activity of TiO2 was found to be related with its wetting property and can be improved by UV irradiation before testing. It is not greatly affected by contact time, indicating a fast acting germicidal activity.