To find out the local buckling behaviors of glass fiber reinforced plastic(GFRP)-foam sandwich pipe suffering axial loading,a series of quasi-static axial compression tests are carried out in the laboratory.Comparing ...To find out the local buckling behaviors of glass fiber reinforced plastic(GFRP)-foam sandwich pipe suffering axial loading,a series of quasi-static axial compression tests are carried out in the laboratory.Comparing with the test data,systematic numerical analysis on the local buckling behavior of this sandwich pipe is also conducted,and the buckling failure mechanism is revealed.The influences of the key parameters on bearing capacity of the sandwich structure are discussed.Test and numerical results show that the local buckling failure of the GFRPfoam sandwich pipe is dominated basically by two typical modes,i.e.,the conjoint buckling and the layered buckling.Local buckling at the end,shear failure at the end and interface peeling failure are less efficient than the local buckling failure at the middle height,and ought to be restrained by appropriate structural measures.The local buckling bearing capacity increases linearly with the core density of the sandwich pipe structure.When the core density is relatively high(higher than 0.05 g/cm3),the effect of increasing the core density on improving the bearing efficiency is less on the specimens with a large ratio of the wall thickness to the radius than on those with a small one.Local layered buckling is another failure mode with lower bearing efficiency than the local conjoint buckling,and it can be restrained by increasing the core density to ensure the cooperation of the inner and the outer GFRP surface layer.The bearing capacity of the GFRP-foam sandwich pipe increases with the height-diameter ratio;however,the bearing efficiency decreases with this parameter.展开更多
基金supported by the National Key R&D Program of China(No.2017YFC0405103)the Natural Science Foundation of China(No. 51978166)the Construction System Science and Technology Guidance Project of Jiangsu(Nos.2017ZD131,2017ZD132).
文摘To find out the local buckling behaviors of glass fiber reinforced plastic(GFRP)-foam sandwich pipe suffering axial loading,a series of quasi-static axial compression tests are carried out in the laboratory.Comparing with the test data,systematic numerical analysis on the local buckling behavior of this sandwich pipe is also conducted,and the buckling failure mechanism is revealed.The influences of the key parameters on bearing capacity of the sandwich structure are discussed.Test and numerical results show that the local buckling failure of the GFRPfoam sandwich pipe is dominated basically by two typical modes,i.e.,the conjoint buckling and the layered buckling.Local buckling at the end,shear failure at the end and interface peeling failure are less efficient than the local buckling failure at the middle height,and ought to be restrained by appropriate structural measures.The local buckling bearing capacity increases linearly with the core density of the sandwich pipe structure.When the core density is relatively high(higher than 0.05 g/cm3),the effect of increasing the core density on improving the bearing efficiency is less on the specimens with a large ratio of the wall thickness to the radius than on those with a small one.Local layered buckling is another failure mode with lower bearing efficiency than the local conjoint buckling,and it can be restrained by increasing the core density to ensure the cooperation of the inner and the outer GFRP surface layer.The bearing capacity of the GFRP-foam sandwich pipe increases with the height-diameter ratio;however,the bearing efficiency decreases with this parameter.
文摘为评价埋地玻璃钢夹砂管涵洞的安全性,保障道路交通运输安全,本文以理论计算为基础,进行现场试验检测,综合分析地面车辆荷载和竖向土压力传至公路下的埋地玻璃钢纤维夹砂管上的作用力与管涵的受力变形特性,然后用回归预测模型计算1200 k N荷载下的力学参数值,验证管涵安全运营状况。结果表明,理论计算和现场试验进行比对,验证了车辆荷载作用下直径1.5 m、厚38 mm的玻璃钢夹砂管的安全可靠性,为玻璃钢夹砂管设计和施工提供科学理论依据。
