The effect of Fe_(2)O_(3) on the formation of micro glass beads(MGBs)under air staged combustion was studied.The experimental temperature was 1450℃,and Hegang bituminous coal was used as the experimental object.X⁃ray...The effect of Fe_(2)O_(3) on the formation of micro glass beads(MGBs)under air staged combustion was studied.The experimental temperature was 1450℃,and Hegang bituminous coal was used as the experimental object.X⁃ray diffractometer(XRD),ash fusion tester,viscosity formula and scanning electron microscopy(SEM)were used to analyze the fly ash.Nano Measurer 1.2 software was used to measure the diameter of MGBs.The results showed that with the increase of Fe_(2)O_(3) in Hegang coal,the glass phase in fly ash first increased and then decreased.When the amount of Fe_(2)O_(3) was 15%,the content of the glass phase was the highest,which was 51.26%.The ash melting point first decreased and then increased,while the viscosity gradually decreased and the particles gradually became spherical.With the increase of Fe_(2)O_(3),the proportion of MGBs with particle size less than 10μm increased gradually.From the above results,it can be concluded that the addition of Fe_(2)O_(3) is conducive to the formation of MGBs and the reduction of particle size.展开更多
High-reflectivity micro-glass bead, as a kind of retro-reflective material, is widely used in reflective fabric or film and other reflective coatings. But it is rarely used in coated paper. The retro-reflective theory...High-reflectivity micro-glass bead, as a kind of retro-reflective material, is widely used in reflective fabric or film and other reflective coatings. But it is rarely used in coated paper. The retro-reflective theory of micro-bead is described. Also the effect of size of micro-bead, dosage of binder and different color layers on reflective properties of coated paper are discussed in this article. The results show that its retro-reflective efficiency is good, equally to reflective fabric or film when the micro-glass bead is used in coated paper.展开更多
基金Sponsored by the Natural Science Foundation of Shandong Province (Grant No. ZR2020ME190)the Shandong Key Research and Development Plan (Grant No. 2019GSF109004)。
文摘The effect of Fe_(2)O_(3) on the formation of micro glass beads(MGBs)under air staged combustion was studied.The experimental temperature was 1450℃,and Hegang bituminous coal was used as the experimental object.X⁃ray diffractometer(XRD),ash fusion tester,viscosity formula and scanning electron microscopy(SEM)were used to analyze the fly ash.Nano Measurer 1.2 software was used to measure the diameter of MGBs.The results showed that with the increase of Fe_(2)O_(3) in Hegang coal,the glass phase in fly ash first increased and then decreased.When the amount of Fe_(2)O_(3) was 15%,the content of the glass phase was the highest,which was 51.26%.The ash melting point first decreased and then increased,while the viscosity gradually decreased and the particles gradually became spherical.With the increase of Fe_(2)O_(3),the proportion of MGBs with particle size less than 10μm increased gradually.From the above results,it can be concluded that the addition of Fe_(2)O_(3) is conducive to the formation of MGBs and the reduction of particle size.
文摘High-reflectivity micro-glass bead, as a kind of retro-reflective material, is widely used in reflective fabric or film and other reflective coatings. But it is rarely used in coated paper. The retro-reflective theory of micro-bead is described. Also the effect of size of micro-bead, dosage of binder and different color layers on reflective properties of coated paper are discussed in this article. The results show that its retro-reflective efficiency is good, equally to reflective fabric or film when the micro-glass bead is used in coated paper.