Effect of Heat Treatment on Microstructure and Mechanical Properties of Multiscale SiC_p Hybrid Reinforced 6061 Aluminum Matrix Composites

The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp), submicron silicon carbide particles(1 μm Si Cp) and Ti particles were studied. The Al/Si Cp composite powder was prepared by high-energy ball milling, and then cold-pressed, sintered, hotextruded, and then heat-treated with different solution temperatures and aging times for the extruded composites. Optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy(EDS), X-ray diffractometer(XRD) and extrusion testing were used to analyze and test the microstructure and mechanical properties of aluminum matrix composites. The results show that after the multi-stage solid solution at 530 ℃×2 h+535 ℃×2 h+540 ℃×2 h, the particles are mainly equiaxed grains and uniformly distributed. There is no reinforcement agglomeration, and the surface is dense and the insoluble phase is basically dissolved. In the matrix, the strengthening effect is good, and the hardness and compressive strength are 179.43 HV and 680.42 MPa, respectively. Under this solution process, when the aluminum matrix composites are aged at 170 ℃ for 10 h, the hardness and compressive strength can reach their peaks and increase to 195.82 HV and 721.48 MPa, respectively.

In-situ homogeneous synthesis of carbon nanotubes on aluminum matrix and properties of their composites

Using nickel catalyst supported on aluminum powders, carbon nanotubes （CNTs） were successfully synthesized in aluminum powders by in-situ chemical vapor deposition at 650 ℃. Structural characterization revealed that the as-grown CNTs possessed higher graphitization degree and straight graphite shell. By this approach, more homogeneous dispersion of CNTs in aluminum powders was achieved compared with the traditional mechanical mixture methods. Using the in-situ synthesized CNTs/Al composite powders and powder metallurgy process, CNTs/Al bulk composites were prepared. Performance testing showed that the mechanical properties and dimensional stability of the composites were improved obviously, which was attributed to the superior dispersion of CNTs in aluminum matrix and the strong interfacial bonding between CNTs and matrix.

A review of particulate-reinforced aluminum matrix composites fabricated by selective laser melting

Selective laser melting(SLM)is an emerging layer-wise additive manufacturing technique that can generate complex components with high performance.Particulate-reinforced aluminum matrix composites(PAMCs)are important materials for various applications due to the combined properties of Al matrix and reinforcements.Considering the advantages of SLM technology and PAMCs,the novel SLM PAMCs have been developed and researched in recent years.Therefore,the current research progress about the SLM PAMCs is reviewed.Firstly,special attention is paid to the solidification behavior of SLM PAMCs.Secondly,the important issues about the design and fabrication of high-performance SLM PAMCs,including the selection of reinforcement,the influence of parameters on the processing and microstructure,the defect evolution and phase control,are highlighted and discussed comprehensively.Thirdly,the performance and strengthening mechanism of SLM PAMCs are systematically figured out.Finally,future directions are pointed out on the advancement of high-performance SLM PAMCs.

Wear performance of in-situ aluminum matrix composite after micro-arc oxidation

An attempt was made to modify the surface of in-situ aluminium matrix composite （AMC） by micro-arc oxidation （MAO）. In the microstructure of AMC, CuAl2 reinforcements were generated by introducing 15% CuO into the aluminium melt. AMC was hot forged, homogenised, quenched and artificially aged before the MAO in a KOH, KF and Na2SiO3-containing electrolyte. After the MAO process the surface of the AMC was covered with Al2O3 coating having an effective thickness of about 15μm. Appearance of crack and/or delamination free zones at the periphery of the indent after the Rockwell C adhesion test indicated good adhesion between the composite and the Al2O3 coating. During dry sliding wear tests, this adherent Al2O3coating resisted the destructive action of the Al2O3 ball and provided about 15 times enhancement in wear resistance as compared to the original state.

Review of recent trends in friction stir welding process of aluminum alloys and aluminum metal matrix composites

Welding is a vital component of several industries such as automotive,aerospace,robotics,and construction.Without welding,these industries utilize aluminum alloys for the manufacturing of many components or systems.However,fusion welding of aluminum alloys is challenging due to several factors,including the presence of non-heat-treatable alloys,porosity,solidification,and liquation of cracks.Many manufacturers adopt conventional in-air friction stir welding(FSW)to weld metallic alloys and dissimilar materials.Many researchers reported the drawbacks of this traditional in-air FSW technique in welding metallic and polymeric materials in general and aluminum alloys and aluminum matrix composites in specific.A number of FSW techniques were developed recently,such as underwater friction stir welding(UFSW),vibrational friction-stir welding(VFSW),and others,for welding of aluminum alloy joints to overcome the issues of welding using conventional FSW.Therefore,the main objective of this review is to summarize the recent trends in FSW process of aluminum alloys and aluminum metal matrix composites(Al MMCs).Also,it discusses the effect of welding parameters of the traditional and state-of-the-art developed FSW techniques on the welding quality and strength of aluminum alloys and Al MMCs.Comparison among the techniques and advantages and limitations of each are considered.The review suggests that VFSW is a viable option for welding aluminum joints due to its energy efficiency,economic cost,and versatile modifications that can be employed based on the application.This review also illustrated that significantly less attention has been paid to FSW of Al-MMCs and considerable attention is demanded to produce qualified joint.

On the liquid-phase technology of carbon fiber/aluminum matrix composites

The main problems with the liquid-phase technology of carbon fiber/aluminum matrix composites include poor wetting of the fiber with liquid aluminum and formation of aluminum carbide on the fibers’surface.This paper aims to solve these problems.The theoretical and experimental dependence of porosity on the applied pressure were determined.The possibility of obtaining a carbon fiber/aluminum matrix composite wire with a strength value of about 1500 MPa was shown.The correlation among the strength of the carbon fiber reinforced aluminum matrix composite,the fracture surface,and the degradation of the carbon fiber surface was discussed.

In-situ fabrication of particulate reinforced aluminum matrix composites under high-frequency pulsed electromagnetic field

Pulsed magnetic field is generated when imposing pulse signal on high-frequency magnetic field. Distribution of the inner magnetic intensity in induction coils tends to be uniform. Furthermore oscillation and disturbance phenomena appear in the melt. In. situ Al2O3 and Al3Zr particulate reinforced aluminum matrix composites have been synthesized by direct melt reaction using AlZr（CO3）2 components under a foreign field. The size of reinforced particulates is 2-3 μm. They are well distributed in the matrix. Thermodynamic and kinetic analysis show that high-frequency pulsed magnetic field accelerates heat and mass transfer processes and improves the kinetic condition of in-situ fabrication.

Interface and thermal expansion of carbon fiber reinforced aluminum matrix composites

Two kinds of unidirectional PAN M40 carbon fiber （55%, volume fraction） reinforced 6061Al and 5A06Al composites were fabricated by the squeeze-casting technology and their interface structure and thermal expansion properties were investigated. Results showed that the combination between aluminum alloy and fibers was well in two composites and interface reaction in M40/5A06Al composite was weaker than that in M40/6061Al composite. Coefficients of thermal expansion （CTE） of M40/Al composites varied approximately from （1.45-2.68）×10^-6 K^-1 to （0.35-1.44）×10^-6 K^-1 between 20℃ and 450℃, and decreased slowly with the increase of temperature. In addition, the CTE of M40/6061Al composite was lower than that of M40/SA06Al composite. It was observed that fibers were protruded significantly from the matrix after thermal expansion, which demonstrated the existence of interface sliding between fiber and matrix during the thermal expansion. It was believed that weak interracial reaction resulted in a higher CTE. It was found that the experimental CTEs were closer to the predicted values by Schapery model.

Compressive response and microstructural evolution of in-situ TiB_(2)particle-reinforced 7075 aluminum matrix composite

The hot forming behavior,failure mechanism,and microstructure evolution of in-situ TiB_(2)particle-reinforced 7075 aluminum matrix composite were investigated by isothermal compression test under different deformation conditions of deformation temperatures of 300−450℃ and strain rates of 0.001^(−1)s^(−1).The results demonstrate that the failure behavior of the composite exhibits both particle fracture and interface debonding at low temperature and high strain rate,and dimple rupture of the matrix at high temperature and low strain rate.Full dynamic recrystallization,which improves the composite formability,occurs under conditions of high temperature(450℃)and low strain rate(0.001 s^(−1));the grain size of the matrix after hot compression was significantly smaller than that of traditional 7075Al and ex-situ particle reinforced 7075Al matrix composite.Based on the flow stress curves,a constitutive model describing the relationship of the flow stress,true strain,strain rate and temperature was proposed.Furthermore,the processing maps based on both the dynamic material modeling(DMM)and modified DMM(MDMM)were established to analyze flow instability domain of the composite and optimize hot forming processing parameters.The optimum processing domain was determined at temperatures of 425−450℃ and strain rates of 0.001−0.01 s^(−1),in which the fine grain microstructure can be gained and particle crack and interface debonding can be avoided.

Ballistic performance of tungsten particle/metallic glass matrix composite long rod

In the present manuscript numerical analysis on the ballistic performance of a tungsten particle/metallic glass matrix(WP/MG) composite rod is conducted by integrating with related experimental investigations. In the corresponding finite element method(FEM) simulations a modified coupled thermomechanical constitutive model is employed to describe the mechanical properties of metallic glass(MG)matrix, and geometrical models of the WP/MG composite rod are established based on its inner structure. The deformation and failure characteristics of the rod and target materials are analyzed in detail,and the influences of various factors on the ballistic performance of the WP/MG composite long rod are discussed. Related analysis demonstrates that the penetrating performance of the WP/MG rod is similar to that of the tungsten fiber/metallic glass matrix(WF/MG) composite long rod, i.e., a "self-sharpening" behavior also occurs during the penetration process, and correspondingly its penetrating capability is better than that of the tungsten heavy alloy(WHA) rod. However, the mass erosion manner of the WP/MG rod is different and the erosion is relatively severe, thus its penetrating capability is a little lower compared with that of the WF/MG one. Moreover, the impact velocity and the target strength have significant influences on the ballistic performance of the WP/MG composite rod, whereas the effect of initial nose shape is very little.

Microstructure and mechanical properties characterization of AA6061/TiC aluminum matrix composites synthesized by in situ reaction of silicon carbide and potassium fluotitanate

Aluminum alloys AA6061 reinforced with various amounts （0, 2.5% and 5%, mass fraction） of TiC particles were synthesized by the in situ reaction of inorganic salt K2TiF6 and ceramic particle SiC with molten aluminum. The casting was carried out at an elevated temperature and held for a longer duration to decompose SiC to release carbon atoms. X-ray diffraction patterns of the prepared AMCs clearly revealed the formation of TiC particles without the occurrence of any other intermetallic compounds. The microstructure of the prepared AA6061/TiC AMCs was studied using field emission scanning electron microscope （FESEM） and electron backscatter diffraction （EBSD）. The in situ formed TiC particles were characterized with homogeneous distribution, clear interface, good bonding and various shapes such as cubic, spherical and hexagonal. EBSD maps showed the grain refinement action of TiC particles on the produced composites. The formation of TiC particles boosted the microhardness and ultimate tensile strength （UTS） of the AMCs.

Effect of thermal-cooling cycle treatment on thermal expansion behavior of particulate reinforced aluminum matrix composites

Two micron SiC particles with angular and spherical shape and the sub-micron Al2O3 particles with spherical shape were introduced to reinforce 6061 aluminium by squeeze casting technology. Microstructures and effect of thermal-cooling cycle treatment （TCCT） on the thermal expansion behaviors of three composites were investigated. The results show that the composites are free of porosity and SiC/Al2O3 particles are distributed uniformly. Inflections at about 300℃ are observed in coefficient of thermal expansion （CTE） versus temperature curves of two SiCp/Al composites, and this characteristic is not affected by TCCT. The TCCT has significant effect on thermal expansion behavior of SiCp/Al composites and CTE of them after 3 cycles is lower than that of 1 or 5 cycles. However, no inflection is observed in Al2O3p/Al composite, while TCCT has effect on CTE of Al2O3p/Al composite. These results should be due to different relaxation behavior of internal stress in three composites.

Microstructure,mechanical and wear properties of aluminum borate whisker reinforced aluminum matrix composites

The microstructural features and the consequent mechanical properties were characterized in aluminium borate whisker(ABOw)(5, 10 and 15 wt.%) reinforced commercially-pure aluminium composites fabricated by conventional powder metallurgy technique. The aluminium powder and the whisker were effectively blended by a semi-powder metallurgy method. The blended powder mixtures were cold compacted and sintered at 600 ℃. The sintered composites were characterized for microstructural features by optical microscopy(OM), scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS), transmission electron microscopy(TEM) and X-ray diffraction(XRD) analysis. Porosity in the composites with variation in ABOw contents was determined. The effect of variation in content of ABOw on mechanical properties, viz. hardness, bending strength and compressive strength of the composites was evaluated. The dry sliding wear behaviour was evaluated at varying sliding distance at constant loads. Maximum flexural strength of 172 MPa and compressive strength of 324 MPa with improved hardness around HV 40.2 are obtained in composite with 10 wt.% ABOw. Further increase in ABOw content deteriorates the properties. A substantial increase in wear resistance is also observed with 10 wt.% ABOw. The excellent combination of mechanical properties of Al-10 wt.%ABOw composites is attributed to good interfacial bonds, less porosity and uniformity in the microstructure.

Effect of aluminum borate whisker coating on interface and mechanical properties of 6061Al matrix composites

Copper coating was deposited on the surface of aluminum borate whisker by an electroless plating method.This method was used to modify the interfacial property of squeeze-casting aluminum borate whisker reinforced 6061Al matrix composite.Interface observation indicates that the spinel reaction(MgAl2O4) is hindered by the copper coating,and the difference in interfacial reaction degree affects the tensile property and aging behavior of the composite.For the composite with less spinel reaction(MgAl2O4),its peak-aging process are postponed due to less depletion of magnesium.On the fracture surface of copper-coated composite dimples and fractures of whiskers are more,but on the fracture surface of uncoated composite pull-out of whiskers are more than that on the coated one.In uncoated composite the fracture generally originates from the near-interface-region.

Graphene-reinforced aluminum matrix composites prepared by spark plasma sintering

Graphene-reinforced 7055 aluminum alloy composites with different contents of graphene were prepared by spark plasma sintering（SPS）. The structure and mechanical properties of the composites were investigated. Testing results show that the hardness, compressive strength, and yield strength of the composites are improved with the addition of 1wt% graphene. A clean, strong interface is formed between the metal matrix and graphene via metallurgical bonding on atomic scale. Harmful aluminum carbide（Al_4C_3） is not formed during SPS processing. Further addition of graphene（above 1wt%） results in the deterioration in mechanical properties of the composites. The agglomeration of graphene plates is exacerbated with increasing graphene content, which is the main reason for this deterioration.

Microstructure and Tensile Properties of Yttria Coated-Alumina Particulates Reinforced Aluminum Matrix Composites

The liquid-phase coating method was used to deposit Y2O3 ceramic on the surface of α-Al2O3. The coated-Al2O3p/6061AI composites were produced using squeeze casting technology. The microstructure and tensile properties of the composites were analysed and studied. The results showed that the coated AI2O3 particles are able to disperse homogeneously in the aluminum liquid. The microstructure of the composites is more even in comparison with that of as-received powders. The tensile testing indicated that mechanical properties of the coated-AI2O3p/6061AI composites are better than those of uncoated particles. In the composite with 30% volume fraction, the tensile strength, yield strength as well as elongation is increased by 29.8%, 38.4% and 10.3%, respectively. The SEM analysis of fracture indicated that the dimples of the coated-Al2O3p/6061Al composites are more even.

Prediction of influence of process parameters on tensile strength of AA6061/TiC aluminum matrix composites produced using stir casting

Stir casting was used to produce AA6061/15%TiC （mass fraction） aluminum matrix composites （AMCs）. An empirical relationship was developed to predict the effect of stir casting parameters on the ultimate tensile strength （UTS） of AA6061/TiC AMCs. A central composite rotatable design consisting of four factors and five levels was used to minimize the number of experiments, i.e., castings. The factors considered were stirring speed, stirring time, blade angle and casting temperature. The effect of those factors on the UTS of AA6061/TiC AMCs was derived using the developed empirical relationship and elucidated using microstructural characterization. Each factor significantly influenced the UTS. The variation in the UTS was attributed to porosity content, cluster formation, segregation of TiC particles at the grain boundaries and homogenous distribution in the aluminum matrix.

Aluminum matrix composites reinforced by molybdenum-coated carbon nanotubes

To extend the application of carbon nanotubes （CNTs） and explore novel aluminum matrix composites,CNTs were coated by molybdenum layers using metal organic chemical vapor deposition,and then Mo-coated CNT （Mo-CNT）/Al composites were prepared by the combination processes of powder mixing and spark plasma sintering.The influences of powder mixing and Mo-CNT content on the mechanical properties and electrical conductivity of the composites were investigated.The results show that magnetic stirring is better than mechanical milling for mixing the Mo-CNTs and Al powders.The electrical conductivity of the composites decreases with increasing Mo-CNT content.When the Mo-CNT content is 0.5wt%,the tensile strength and hardness of Mo-CNT/Al reach their maximum values.The tensile strength of 0.5wt% Mo-CNT/Al increases by 29.9%,while the electrical conductivity only decreases by 7.1%,relative to sintered pure Al.The phase analysis of Mo-CNT/Al composites reveals that there is no formation of Al carbide in the composites.

Effect of Welding Paramenter on Joint Property of Aluminum Matrix Composite in Liquid-Phase-Impacting Diffusion Welding

In this paper, a new method for welding SiCp/101A was put forward. It is LPI (liquid-phase-impacting) diffusionwelding. Through LPI diffusion welding SiCp/101A aluminum, the effect of welding parameters on the weldedjoint property was investigated, and the optimal welding parameters were brought forward at the same time. Themicrostructure of joint was analyzed by means of optical-microscope, scanning electron microscope in order to studythe relationship between the macro-properties of joint and the microstructure. The results show that LPI diffusionwelding could be used for welding aluminum matrix composites SiCp/101A successfully.

Aluminum matrix composites reinforced by in situ Al_2O_3 and Al_3Zr particles fabricated via magnetochemistry reaction

Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.