In order to overcome the limitations of low adhesion strength and poor thermal-shock resistance of pure ceramic coatings, Cu-Al2O3 gradient coatings were fabricated by plasma spraying. The microstructure and distribut...In order to overcome the limitations of low adhesion strength and poor thermal-shock resistance of pure ceramic coatings, Cu-Al2O3 gradient coatings were fabricated by plasma spraying. The microstructure and distribution of Cu-Al2O3 gradient coatings were analyzed. The adhesion strength, thermal-shock resistance and porosity of the coatings were tested. The results show that the composition of the gradient coatings has a gradient distribution along the thickness of coatings. As copper has a relatively low melting point and the molten copper has good wettability on the surface of Al2O3, it can be melted sufficiently and could fill the interstices and pores among the spraying particles effectively, thus improves the adhesion strength, thermal shock resistance and reduces the porosity. The adhesion strength of the gradient coating is 15.2 MPa which is two times of that of the double-layer structure coating.展开更多
To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And e...To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And effect of Y2O3 content on gradient bioceramic composite coating was studied. The experimental results indicate that adding rare earth can refine grain. Different rare earth contents affect formation of HA and β-TCP in bioceramic coating. When the content of rare earth ranges from 0.4% to 0.6%, the active extent of rare earth in synthesizing HA and β-TCP is the best, which indicates that “monosodium glutamate” effect of rare earth plays a dominant role. However, when rare earth content is up to 0.8%, the amount of synthesizing HA and β-TCP in coating conversely goes down, which demonstrates that rare earth gradually losts its catalysis in manufacturing HA and β-TCP.展开更多
The metal and nano-ceramic composite coatings were formed on gray cast iron surface by electrodepositon method.The Ni-Co was used as metal matrix,and the nano-Al2O3 was chosen as second-phase particulates.The gradient...The metal and nano-ceramic composite coatings were formed on gray cast iron surface by electrodepositon method.The Ni-Co was used as metal matrix,and the nano-Al2O3 was chosen as second-phase particulates.The gradient structure of biology material was the model to avoid bad interface bonding and stress distribution,therefore the gradient composite coating was prepared.The morphology of composite coatings was flatter and the microstructure was more com-pact than the pure Ni-Co coatings.Effect of pH value on surface morphology was analyzed,which some microcracks appeared when pH value was greater than 5.The content of codeposition na-no-Al2O3 reached a maximum value at pH value of 3-4,at the same time the properties including mi-crohardness and wear-resistance were analyzed.The result indicated that the mirohardness reached a maximum value and the wear loss volume was less at pH value 3-4.展开更多
Gradient thermal barrier coatings (GTBCs) produced by co-deposition of mixtures ofAl-Al2 O3-YSZ onto metallic bond coat exhibited longer lifetimes than the two-layeredTBCs. The finite element method (FEM) numerical mo...Gradient thermal barrier coatings (GTBCs) produced by co-deposition of mixtures ofAl-Al2 O3-YSZ onto metallic bond coat exhibited longer lifetimes than the two-layeredTBCs. The finite element method (FEM) numerical models were used to investigatestress and strain states in the GTBCs and traditional two-layered TBCs as they cooledto 750℃ from a stress-free state at 850℃.展开更多
Coherent gradient sensing (CGS) method can be used to measure the slope of a reflective surface, and has the merits of full-field, non-contact, and real-time measurement. In this study, the thermal stress field of t...Coherent gradient sensing (CGS) method can be used to measure the slope of a reflective surface, and has the merits of full-field, non-contact, and real-time measurement. In this study, the thermal stress field of thermal barrier coating (TBC) structures is measured by CGS method. Two kinds of powders were sprayed onto Ni-based alloy using a plasma spraying method to obtain two groups of film-substrate specimens. The specimens were then heated with an oxy-acetylene flame. The resulting thermal mismatch between the film and substrate led to out-of-plane deformation of the specimen. The deformation was measured by the reflective CGS method and the thermal stress field of the structure was obtained through calibration with the help of finite element analysis. Both the experiment and numerical results showed that the thermal stress field of TBC structures can be successfully measured by CGS method.展开更多
The material design is used to direct the magnetron cosputtering process. At first, according to the particularity of functionally gradient coat (FGC) the thermal elastic stress analysis for FGC was carried out based ...The material design is used to direct the magnetron cosputtering process. At first, according to the particularity of functionally gradient coat (FGC) the thermal elastic stress analysis for FGC was carried out based on the plane stress hypothesis. It is obtained that the peak value of plane thermal stress within FGC is only determined by the physical properties of materials of FGC and substrate, the composition distribution coefficient only influences the distribution and trend of plane thermal stress. And the plane thermal stress criterion for design of FGC was presented. Then the plane thermal stress of diamond like carbon/titanium alloy FGC was calculated.展开更多
文摘In order to overcome the limitations of low adhesion strength and poor thermal-shock resistance of pure ceramic coatings, Cu-Al2O3 gradient coatings were fabricated by plasma spraying. The microstructure and distribution of Cu-Al2O3 gradient coatings were analyzed. The adhesion strength, thermal-shock resistance and porosity of the coatings were tested. The results show that the composition of the gradient coatings has a gradient distribution along the thickness of coatings. As copper has a relatively low melting point and the molten copper has good wettability on the surface of Al2O3, it can be melted sufficiently and could fill the interstices and pores among the spraying particles effectively, thus improves the adhesion strength, thermal shock resistance and reduces the porosity. The adhesion strength of the gradient coating is 15.2 MPa which is two times of that of the double-layer structure coating.
基金Project supported by Governor's Foundation of Guizhou Province (2004-07)
文摘To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And effect of Y2O3 content on gradient bioceramic composite coating was studied. The experimental results indicate that adding rare earth can refine grain. Different rare earth contents affect formation of HA and β-TCP in bioceramic coating. When the content of rare earth ranges from 0.4% to 0.6%, the active extent of rare earth in synthesizing HA and β-TCP is the best, which indicates that “monosodium glutamate” effect of rare earth plays a dominant role. However, when rare earth content is up to 0.8%, the amount of synthesizing HA and β-TCP in coating conversely goes down, which demonstrates that rare earth gradually losts its catalysis in manufacturing HA and β-TCP.
基金Funded by the National Natural Science Foundation of China(No.50635030)the National Basic Research of China (No.2007CB616913)
文摘The metal and nano-ceramic composite coatings were formed on gray cast iron surface by electrodepositon method.The Ni-Co was used as metal matrix,and the nano-Al2O3 was chosen as second-phase particulates.The gradient structure of biology material was the model to avoid bad interface bonding and stress distribution,therefore the gradient composite coating was prepared.The morphology of composite coatings was flatter and the microstructure was more com-pact than the pure Ni-Co coatings.Effect of pH value on surface morphology was analyzed,which some microcracks appeared when pH value was greater than 5.The content of codeposition na-no-Al2O3 reached a maximum value at pH value of 3-4,at the same time the properties including mi-crohardness and wear-resistance were analyzed.The result indicated that the mirohardness reached a maximum value and the wear loss volume was less at pH value 3-4.
基金sponsored by the National Natural Science Foundation of China(NSFC)Specialized Research Fund for the Doctoral Program of Higher Education of China(SRFDP).
文摘Gradient thermal barrier coatings (GTBCs) produced by co-deposition of mixtures ofAl-Al2 O3-YSZ onto metallic bond coat exhibited longer lifetimes than the two-layeredTBCs. The finite element method (FEM) numerical models were used to investigatestress and strain states in the GTBCs and traditional two-layered TBCs as they cooledto 750℃ from a stress-free state at 850℃.
基金financial support from the National Natural Science Foundation of China(11672153,11232008,and11227801)
文摘Coherent gradient sensing (CGS) method can be used to measure the slope of a reflective surface, and has the merits of full-field, non-contact, and real-time measurement. In this study, the thermal stress field of thermal barrier coating (TBC) structures is measured by CGS method. Two kinds of powders were sprayed onto Ni-based alloy using a plasma spraying method to obtain two groups of film-substrate specimens. The specimens were then heated with an oxy-acetylene flame. The resulting thermal mismatch between the film and substrate led to out-of-plane deformation of the specimen. The deformation was measured by the reflective CGS method and the thermal stress field of the structure was obtained through calibration with the help of finite element analysis. Both the experiment and numerical results showed that the thermal stress field of TBC structures can be successfully measured by CGS method.
文摘The material design is used to direct the magnetron cosputtering process. At first, according to the particularity of functionally gradient coat (FGC) the thermal elastic stress analysis for FGC was carried out based on the plane stress hypothesis. It is obtained that the peak value of plane thermal stress within FGC is only determined by the physical properties of materials of FGC and substrate, the composition distribution coefficient only influences the distribution and trend of plane thermal stress. And the plane thermal stress criterion for design of FGC was presented. Then the plane thermal stress of diamond like carbon/titanium alloy FGC was calculated.