The metal and nano-ceramic composite coatings were formed on gray cast iron surface by electrodepositon method.The Ni-Co was used as metal matrix,and the nano-Al2O3 was chosen as second-phase particulates.The gradient...The metal and nano-ceramic composite coatings were formed on gray cast iron surface by electrodepositon method.The Ni-Co was used as metal matrix,and the nano-Al2O3 was chosen as second-phase particulates.The gradient structure of biology material was the model to avoid bad interface bonding and stress distribution,therefore the gradient composite coating was prepared.The morphology of composite coatings was flatter and the microstructure was more com-pact than the pure Ni-Co coatings.Effect of pH value on surface morphology was analyzed,which some microcracks appeared when pH value was greater than 5.The content of codeposition na-no-Al2O3 reached a maximum value at pH value of 3-4,at the same time the properties including mi-crohardness and wear-resistance were analyzed.The result indicated that the mirohardness reached a maximum value and the wear loss volume was less at pH value 3-4.展开更多
基金Funded by the National Natural Science Foundation of China(No.50635030)the National Basic Research of China (No.2007CB616913)
文摘The metal and nano-ceramic composite coatings were formed on gray cast iron surface by electrodepositon method.The Ni-Co was used as metal matrix,and the nano-Al2O3 was chosen as second-phase particulates.The gradient structure of biology material was the model to avoid bad interface bonding and stress distribution,therefore the gradient composite coating was prepared.The morphology of composite coatings was flatter and the microstructure was more com-pact than the pure Ni-Co coatings.Effect of pH value on surface morphology was analyzed,which some microcracks appeared when pH value was greater than 5.The content of codeposition na-no-Al2O3 reached a maximum value at pH value of 3-4,at the same time the properties including mi-crohardness and wear-resistance were analyzed.The result indicated that the mirohardness reached a maximum value and the wear loss volume was less at pH value 3-4.