Strength and plasticity improvement induced by strong grain refinement after Zr alloying in selective laser-melted AlSiMg1.4 alloy

In order to enhance the mechanical properties of the selective laser-melted(SLM) high-Mg content AlSiMg1.4 alloy,the Zr element was introduced.The influence of Zr alloying on the processability,microstructure,and mechanical properties of the alloy was systematically investigated through performing microstructure analysis and tensile testing.It was demonstrated that the SLM-fabricated AlSiMg1.4-Zr alloy exhibited high process stability with a relative density of over 99.5% at various process parameters.Besides,the strong grain refinement induced by the primary Al3Zr particle during the melt solidification process simultaneously enhanced both the strength and plasticity of the alloy.The values for the yield strength,ultimate tensile strength,and elongation of the SLM-fabricated AlSiMg1.4-Zr were(343±3) MPa,(485±4) MPa,and(10.2±0.2)%,respectively,demonstrating good strengthplasticity synergy in comparison to the AlSiMg1.4 and other Al-Si-based alloys fabricated by SLM.

Grain refinement of Mg-Ca alloys by native MgO particles

In Mg-Ca alloys the grain refining mechanism,in particular regarding the role of nucleant substrates,remains the object of debates.Although native MgO is being recognised as a nucleating substrate accounting for grain refinement of Mg alloys,the possible interactions of MgO with alloying elements that may alter the nucleation potency have not been elucidated yet.Herein,we design casting experiments of Mg-xCa alloys varied qualitatively in number density of native MgO,which are then comprehensively studied by advanced electron microscopy.The results show that grain refinement is enhanced as the particle number density of MgO increases.The native MgO particles are modified by interfacial layers due to the co-segregation of Ca and N solute atoms at the MgO/Mg interface.Using aberration-corrected scanning transmission electron microscopy and electron energy loss spectroscopy,we reveal the nature of these Ca/N interfacial layers at the atomic scale.Irrespective of the crystallographic termination of MgO,Ca and N co-segregate at the MgO/Mg interface and occupy Mg and O sites,respectively,forming an interfacial structure of a few atomic layers.The interfacial structure is slightly expanded,less ordered and defective compared to the MgO matrix due to compositional deviations,whereby the MgO substrate is altered as a poorer template to nucleate Mg solid.Upon solidification in a TP-1 mould,the impotent MgO particles account for the grain refining mechanism,where they are suggested to participate into nucleation and grain initiation processes in an explosive manner.This work not only reveals the atomic engineering of a substrate through interfacial segregation but also demonstrates the effectiveness of a strategy whereby native MgO particles can be harnessed for grain refinement in Mg-Ca alloys.

Effect of addition temperature on dispersion behavior and grain refinement efficiency of MgO introduced into Mg alloy

The effect of addition temperature of MgO particles(MgOp)on their dispersion behavior and the efficiency of grain refinement in AZ31 Mg alloy was investigated.In addition,the grain refinement mechanism was systematically studied by microstructure characterization,thermodynamic calculation,and analysis of solidification curves.The results show that the grain size of AZ31 Mg alloy initially decreases and then increases as the MgOp addition temperature is increased from 720 to 810℃,exhibiting a minimum value of 136μm at 780℃.The improved grain refinement efficiency with increasing MgOp addition temperature can be attributed to the reduced Mg melt viscosity and enhanced wettability between MgOp and Mg melt.Furthermore,a corresponding physical model describing the solidification behavior and grain refinement mechanism was proposed.

Grain refinement in AZ31 magnesium alloy rod fabricated by extrusion-shearing severe plastic deformation process

A new severe plastic deformation （SPD） method that is extrusion-shearing （ES）, which includes initial forward extrusion and shearing process subsequently, was developed to fabricate the fine grained AZ31 Mg alloys. The components of ES die were manufactured and installed to gleeble1500D thermo-mechanical simulator. Microstructure observations were carried out in different positions of ES formed rods. The results show that homogeneous microstructures with mean grain size of 2 μm are obtained at lower temperature as the accumulated true strain is 2.44. Occurring of continuous dynamic recrystallization （DRX） is the main reason for grain refinement during ES process. The experimental results show that the ES process effectively refines the grains of AZ31 magnesium. The production results of ES extrusion with industrial extruder under different extrusion conditions show that the ES extrusion can be applied in large-scale industry.

Structure uniformity and limits of grain refinement of high purity aluminum during multi-directional forging process at room temperature

The effect of forging passes on the refinement of high purity aluminum during multi-forging was investigated. The attention was focused on the structure uniformity due to deformation uniformity and the grain refinement limitation with very high strains. The results show that the fine grain zone in the center of sample expands gradually with the increase of forging passes. When the forging passes reach 6, an X-shape fine grain zone is initially formed. With a further increase of the passes, this X-shape zone tends to spread the whole sample. Limitation in the structural refinement is observed with increasing strains during multi-forging process at the room temperature. The grains size in the center is refined to a certain size （110 μm as forging passes reach 12, and there is no further grain refinement in the center with increasing the forging passes to 24. However, the size of the coarse grains near the surface is continuously decreased with increasing the forging passes to 24.

Grain refinement of as-cast superalloy IN718 under action of low voltage pulsed magnetic field

The grain refinement of superalloy IN718 under the action of low voltage pulsed magnetic field was investigated. The experimental results show that fine equiaxed grains are acquired under the action of low voltage pulsed magnetic field. The refinement effect of the pulsed magnetic field is affected by the melt cooling rate and superheating. The decrease of cooling rate and superheating enhance the refinement effect of the low voltage pulsed magnetic field. The magnetic force and the melt flow during solidification are modeled and simulated to reveal the grain refinement mechanism. It is considered that the melt convection caused by the pulsed magnetic field, as well as cooling rate and superheating contributes to the refinement of solidified grains.

Numerical simulation of acoustic pressure field for ultrasonic grain refinement of AZ80 magnesium alloy

Ultrasound with different intensities was applied to treating AZ80 alloy melt to improve its solidification structure.The average grain size of the alloy could be decreased from 303 to 148 μm after the ultrasound with intensity of 30.48 W/cm2 was applied.To gain insight into the mechanism of ultrasonic treatment which affected the microstructure of the alloy,numerical simulations were carried out and the effects of different ultrasonic pressures on the behaviors of cavitation bubble in the melt were studied.The ultrasonic field propagation in the melt was also characterized.The results show that samples from different positions are subjected to different acoustic pressures and the effect of grain refinement by ultrasonic treatment for these samples is different.With the increase of ultrasonic intensity,the acoustic pressure is increased and the grain size is decreased generally.

Grain refinement of Al-5%Cu aluminum alloy under mechanical vibration using meltable vibrating probe

A mechanical vibration technique to refine solidified microstructure was reported. Vibration energy was directly introduced into a molten alloy by a vibrating horn, and the vibrating horn was melted during vibration. Effects of vibration acceleration and mass ratio on the microstructure of Al-5% Cu alloy were investigated. Results show that the present mechanical vibration could provide localized cooling by extracting heat from the interior of molten alloy, and the cooling rate is strongly dependent on vibration acceleration. It is difficult to refine the solidified microstructure when the treated alloy keeps full liquid state within the entire vibrating duration. Significantly refined microstructure was obtained by applying mechanical vibration during the initial stage of solidification. Moreover, mechanisms of grain refinement were discussed.

Grain refining mechanism of Al-3B master alloy on hypoeutectic Al-Si alloys

Al-3B master alloy is a kind of efficient grain refiner for hypoeutectic Al-Si alloys. Experiments were carried out to evaluate the effect of undissolved AlB2 particles in Al-3B master alloy on the grain refinement of Al-7Si. It is found that the number and the settlement of AlB2 particles in the melt all have effect on the grain refining efficiency. On the basis of experiments and theoretical analysis, a new grain refinement mechanism was proposed to explain the grain refinement action of Al-3B on hypoeutectic Al-Si alloys. The formation of ＇Al-AlB2＇ shell structure is the direct reason for grain refinement and the undissolved AlB2 particles is the indirect nucleating base for subsequent α（Al） phase.

Grain refinement of pure aluminum by direct current pulsed magnetic field and inoculation

The combined effects of direct current pulsed magnetic field （DC-PMF） and inoculation on pure aluminum were investigated, the grain refinement behavior of DC-PMF and inoculation was discussed. The experimental results indicate that the solidification micro structure of pure aluminum can be greatly refined under DC-PMF. Refinement of pure aluminum is attributed to electromagnetic undercooling and forced convection caused by DC-PMF. With single DC-PMF, the grain size in the equiaxed zone is uneven. However, under DC-PMF, by adding 0.05% （mass fraction） Al5Ti-B, the grain size of the sample is smaller, and the size distribution is more uniform than that of single DC-PMF. Furthermore, under the combination of DC-PMF and inoculation, with the increase of output current, the grain size is further reduced. When the output current increases to 100 A, the average grain size can decrease to 113 μn.

Effects of Al-Ti-B-RE grain refiner on microstructure and mechanical properties of Al-7.0Si-0.55Mg alloy

To investigate the effects of Al-Ti-B-RE grain refiner on microstructure and mechanical properties of Al-7.0Si-0.55Mg （A357） alloy, some novel Al-7.0Si-0.55Mg alloys added with different amount of Al-STi-1B-RE grain refiner with different RE composition were prepared by vacuum-melting. The microstructure and fracture behavior of the AI-7.0Si-0.55Mg alloys with the grain refiners were observed by X-ray diffraction （XRD）, optical microscopy （OM）, scanning electron microscopy （SEM）, and the mechanical properties of the alloys were tested in mechanical testing machine at room temperature. The observation of AI-Ti-B-RE morphology and internal structure of the particles reveals that it exhibits a TiAl3/Ti2Al20RE core-shell structure via heterogeneous TiB2 nuclei. The tensile strength of Al-7.0Si-0.55Mg alloys with Al-5Ti-1B-3.0RE grain refiner reaches the peak value at the same addition （0.2%） of grain refiner.

Effect of electrodes and thermal insulators on grain refinement by electric current pulse

The application of electric current pulse（ECP） to a solidification process refers to the immersion of electrodes into the liquid metal and the employment of thermal insulators on the upper surface of metal.In order to ascertain the effects of these two factors on the structure refinement by the ECP technique,three groups of experiments were performed with different types of electrodes or various thermal insulators.By the comparison between solidification structures under different conditions,it is followed that the electrode and the thermal insulator have an obvious influence on the grain refinement under an applied ECP,and further analysis demonstrates that the thermal conditions of the liquid surface play a vital role in the modification of solidification structure.Also,the results support the viewpoint that most of the equiaxed grains originate from the liquid surface subjected to an ECP.

Effect of Al_2Ca intermetallic compound addition on grain refinement of AZ31 magnesium alloy

The Al2Ca intermetallic compound was prepared by melting process in a vacuum induction furnace. And the A12Ca compound was added in as-cast AZ31 alloys for grain refinement. The effect of its additional levels on grain refinement of as-cast AZ31 alloy was investigated and the mechanism of the grain refinement was discussed. The results reveal that the addition of 1.1% Al2Ca （mass fraction） decreases the average grain size of as-cast AZ31 alloy from 354 to 198 μm. And the thermal stability of the grains refined by Al2Ca is superior. The grain refining mechanism is attributed to the combined effects of solute and heterogeneous nucleation from the Al2Ca.

Grain refinement of magnesium alloys processed by severe plastic deformation

Grain refinement of AZ31 Mg alloy during cyclic extrusion compression （CEC） at 225-400 ℃ was investigated quantitatively by electron backscattering diffraction （EBSD）. Results show that an ultrafine grained microstructure of AZ31 alloy is obtained only after 3 passes of CEC at 225 ℃. The mean misorientation and the fraction of high angle grain boundaries （HAGBs） increase gradually by lowering extrusion temperature. Only a small fraction of {101^-2} twinning is observed by EBSD in AZ31 Mg alloys after 3 passes of CEC. Schmid factors calculation shows that the most active slip system is pyramidal slip {101^-1}〈1120〉and basal slip {0001}〈1120〉 at 225-350 ℃ and 400 ℃, respectively. Direct evidences at subgrain boundaries support the occurrence of continuous dynamic recrystallization （CDRX） mechanism in grain refinement of AZ31 Mg alloy processed by CEC.

Grain refinement mechanism of Al-5C master alloy in AZ31 magnesium alloy

Al-5C master alloy was prepared by powder in situ synthesis process, and its effects on grain refinement of AZ31 alloy and refining mechanism were investigated. The results indicate that the AI 5C master alloy consists of a（Al） and A14C3 phases, and the size distribution of Al4C3 particles is controlled by sintering time. The AI 5C master alloy can remarkably reduce the grain size of AZ31 alloy, which decreases with the increasing addition amount of AI-SC master alloy when the addition amount is below 2%. The refining mechanism is attributed to the formation of new compounds of Al-C-Mnparticles by Al4C3 and Mn, which might act as nucleating substrates for a-Mg grain.

Grain refining technique of AM60B magnesium alloy by MgCO_3

The effects of grain refining parameters on microstructure of AM60B magnesium alloy with MgCO3 were investigated and then a refining technique was developed.Simultaneously,the corresponding mechanisms were discussed.The results indicate that increasing addition temperature of MgCO3 or pouring temperature is beneficial for obtaining fine grains.There is an optimal addition amount of 1.2%at the addition temperature of 790°C.Prolonging holding time at 790°C will increase grain size.The grain refining technique that 1.2%MgCO3 is added at 790°C followed by holding for 10 min and pouring can decrease the grain size from 348μm of the un-refined alloy to 69μm.The nucleation substrates are actually the Al4C3 particles formed from reactions between the MgCO3 and alloying elements in the melt.Besides the heterogeneous nucleation regime,growth restriction of the Al4C3 particles agglomerated at growing front is the other mechanism.

Effects of grain refining and modification on mechanical properties and microstructures of Al-7.5Si-4Cu cast alloy

Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.

Grain refining effect of Mg by novel particle cluster-containing Al-Ti-C master alloy

A novel A1-Ti-C master alloy containing A14C3 and TiC particle clusters, which exhibits great refining potential for Mg, was prepared. With the addition of 2% A1-Ti-C master alloy, the grains transform to equiaxed crystal with a diameter of （110-a：17） ~tm. The results indicate that A14C3 and TiC particle cluster, rather than a single particle, plays an important role in the refining process. Compared with the simplex smooth nucleating substrate, concave regions on the particle cluster provide easier route for the transformation from liquid Mg atoms to stable nucleus. Nucleus with a small size can also reach the critical nucleation radius when they attach on the concave regions of the substrate. A14C3 and TiC particle clusters thus become more favorable nucleating substrate for a-Mg grains.

Effect of processing route on grain refinement in pure copper processed by equal channel angular extrusion

An experimental study of the microstructures in pure copper billets processed by 8 passes of equal channel angular extrusion （ECAE） via an extended range of processing routes with a 90° die is carried out. Each processing route is defined according to the inter-pass billet rotation angle （χ）, which varies from 0° to 180°. According to the generation of high-angle boundaries and reduction of grain size by electron backscatter diffraction （EBSD） measurements, the grain refinement is found to be most efficient for route with χ=90°and least efficient with χ=180°, among the seven routes studied. This trend is supported by supplementary transmission electron microscopy （TEM） measurements. Comparison of the EBSD and TEM data reveals the importance of considering the non-equiaxity of grain structures in quantitative assessment of microstructural differences in ECAE-processed materials.

Grain Refining Performance of SHS Al-50TiC Master Alloys for Commercially Pure Aluminum

An Al 50wt%TiC composite was directly synthesized by self propagating high temperature synthesis (SHS) technology,and then was used as a grain refining master alloy for commercially pure aluminum.The microstructure and grain refining performance of the synthesized master alloy were emphatically investigated.The SHS master alloy only contained submicron TiC particles except for Al matrix.Moreover,TiC particles were relatively free of agglomeration. Grain refining tests show that adding only 0.1 wt% of the master alloys to the aluminum melt could transform the structure of the solidified samples from coarse columnar grains to fine equiaxed grains (average grain size 120μm),and that this grain refining effectiveness could be maintained for almost 1.5h at 1003K. Therefore,it is concluded that the SHS master alloy is an effective grain refiner for aluminum and its alloys, and that it is highly resistant to the grain refining fading encountered with most grain refiners.