The production of low-temperature reheated grain-oriented silicon steel is mainly based on the acquired inhibitor method.Due to the additional nitriding process,a high nitrogen content exists in the oxide layer,which ...The production of low-temperature reheated grain-oriented silicon steel is mainly based on the acquired inhibitor method.Due to the additional nitriding process,a high nitrogen content exists in the oxide layer,which changes the structure of the oxide layer.In this study,the structure of the surface oxide layer after nitriding was analyzed by scanning electron microscopy(SEM),electron back-scattered diffraction(EBSD),glow discharge spectrometry(GDS),and X-ray diffraction(XRD).The size and orientation of ferritic grains in the oxide layer were characterized,and the distribution characteristics of the key elements along the thickness direction were determined.The results show that the oxide layer of the steel sample mainly comprised particles of Fe2SiO4 and spherical and lamellar SiO2,and Fe4N and fcc-Fe phases were also detected.Moreover,the size and orientation of ferritic grains in the oxide layer were different from those of coarse matrix ferritic grains beneath the oxide layer;however,some ferritic grains exhibited same orientations as those in the neighboring matrix.Higher nitrogen content was detected in the oxide layer than that in the matrix beneath the oxide layer.The form of nitrogen enrichment in the oxide layer was analyzed,and the growth mechanism of ferritic grains during the oxide layer formation is proposed.展开更多
Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, ...Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, inductive devices, etc. Most recently, the factors effecting the texture and magnetic properties, e.g. impurities, rolling process and annealing process, have been greatly studied. The benefits of this study are that low core loss silicon steels with stable high-performance can be obtained through an economic production process. This review is intended to summarize the recent developments in the texture, properties, manufacture and application of oriented silicon steel sheets.展开更多
Baosteel＇ s Cr-free ultrathick J coat for non-oriented silicon steel sheets has excellent insulation performance and has been successfully applied to middle and large scale electric power trains and wind electric pow...Baosteel＇ s Cr-free ultrathick J coat for non-oriented silicon steel sheets has excellent insulation performance and has been successfully applied to middle and large scale electric power trains and wind electric power devices, which have stricter requirements than typical for coat insulation. In this paper, the characteristics and application of this type of coating for non-oriented silicon steel sheets were described in detail.展开更多
A Monte Carlo Potts model was developed to simulate the recrystallization process of a cold-rolled ultra-thin grain-oriented silicon steel.The orientation and image quality data from electron backscatter diffraction m...A Monte Carlo Potts model was developed to simulate the recrystallization process of a cold-rolled ultra-thin grain-oriented silicon steel.The orientation and image quality data from electron backscatter diffraction measurements were used as input information for simulation.Three types of nucleation mechanisms,namely,random nucleation,high-stored-energy site nucleation(HSEN),and high-angle boundary nucleation(HABN),were considered for simulation.In particular,the nucleation and growth behaviors of Goss-oriented({011}<100>)grains were investigated.Results showed that Goss grains had a nucleation advantage in HSEN and HABN.The amount of Goss grains was the highest according to HABN,and it matched the experimental measurement.However,Goss grains lacked a size advantage across all mechanisms during the recrystallization process.展开更多
Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy...Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and ratio were analyzed based on the experimentaldata.At 1.0 T,hysteresis loss of tested steelwith scribing spacing of 8 mm descends by 8.2% compared to samples without scribing,which is similar to the totalloss variation,and abnormalloss descends by 16.8%.At 1.0 T,hysteresis loss ratio of the steelwith scribing spacing of 16 mm ascends from 55.7% to 57.9%,and eddy current loss increases from 17.4% to 24.1%,while abnormalloss descends from 26.9% to 23.7%.The experimentalresults show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormalloss.展开更多
A siliconizing process to manufacture 6.5% Si steel sheet has been developed. Electric components, such as transformers and reactors are made easily from 6.5% Si steel sheet. However, improved workability is desirable...A siliconizing process to manufacture 6.5% Si steel sheet has been developed. Electric components, such as transformers and reactors are made easily from 6.5% Si steel sheet. However, improved workability is desirable to increase the applications. Therefore the improvement of workability of 6.5% Si steel sheet was investigated, and the results were obtained as follows: (a) workability of 6.5% Si steel sheet is deteriorated by grain boundary oxidization, (b) grain boundary oxidization can be restrained by the addition of C. Workability and magnetic properties of 6.5% Si steel sheet with C addition are discussed. Furthermore, it was found that the workability of high Si steel sheet was improved remarkably by varying the Si content gradient along the thickness without deterioration of high frequency magnetic properties. This newly developed magnetic gradient high Si steel sheet is also discussed.展开更多
Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were resea...Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.展开更多
High-speed motor has the characteristics of high frequency, high temperature, and more stress, resulting in the field distribution inside the motor being complicated. To better study the electromagnetic characteristic...High-speed motor has the characteristics of high frequency, high temperature, and more stress, resulting in the field distribution inside the motor being complicated. To better study the electromagnetic characteristics of silicon steel sheet for high-speed motor. In this article, a study on the calculation model of silicon sheet electromagnetic characteristics considers the effects of electromagnetic, stress, and temperature factors. The study is divided into two parts, one is to propose the calculation model of silicon steel sheet’s permeability;the other is to improve the calculation model of silicon steel sheet’s loss. Then, the magnetic field, stress field, and temperature field of a surface mount high speed permanent magnet motor(SMHSPMSM) are analyzed by finite element method(FEM), and the results under the consideration of magnetic, stress, and temperature factors are brought into the calculation model for calculation. Finally, the accuracy of the calculation model for electromagnetic characteristics of silicon steel sheet is verified by comparing the calculated results with the finite element results.展开更多
CW-CO2 laser nitriding technique was applied to improve the properties （such as aging property and the core loss） of grain oriented silicon steel. The samples were nitrided with regular space. Laser power density an...CW-CO2 laser nitriding technique was applied to improve the properties （such as aging property and the core loss） of grain oriented silicon steel. The samples were nitrided with regular space. Laser power density and scanning speed were chosen as 7.8×10^5W·cm^-2 and 100mm·min^-1. By some laser irradiation, Fe4N and Fe3N were formed in the nitrided zone. The nitrided samples were annealed at the temperatures ranged from 100 to 90℃. The core loss of some interested samples was tested. The results show that the core loss of the nitrided samples with different thickness of 0.23 and 0.30mm decreased by 14.9% and 9.4% respectively, and the aging property were improved up to 800℃. The mechanism of laser nitriding to improve the properties of grain oriented silicon steel is discussed.展开更多
By rolling and nitriding processes, 0.23- to 0.3-mm-thick grain-oriented 6.5 wt% silicon steel sheets were produced. The core losses of grain-oriented 6.5 wt% silicon steel at frequencies ranging from 400 Hz to 20 kHz...By rolling and nitriding processes, 0.23- to 0.3-mm-thick grain-oriented 6.5 wt% silicon steel sheets were produced. The core losses of grain-oriented 6.5 wt% silicon steel at frequencies ranging from 400 Hz to 20 kHz were lower than that of the grain-oriented 3 wt% silicon steel with the same thickness by 16.6-35.8%. The secondary recrystallization behavior was investigated by scanning electron microscopy, energy-dispersive spectroscopy, and electron backscattered diffraction. The results show that the secondary recrystallization in high-silicon steel sheets develops more completely as the nitrogen content increases after nitriding, secondary recrystallized grain sizes become larger, and the sharpness of Goss texture increases. Because more { 110} （116） grains in the subsurface and the central layer of the sheets have a lot of 20°-45° high-energy boundaries in addition to Goss grains, {110} （116） can be the main component through selective growth during secondary recrystallization when the inhibitor quantity is not enough and inhibitor intensity is weaker. The increases in nitrogen content can increase the inhibitor intensity and hinder abnormal growth of a mount of {110} （116） grains and therefore enhance the sharpness of Goss texture.展开更多
The product quality of graiworiented silicon steel may be affected by each process because of its complicat- ed production technology. Morphologies, compositions and structures of forsterite film formed in different c...The product quality of graiworiented silicon steel may be affected by each process because of its complicat- ed production technology. Morphologies, compositions and structures of forsterite film formed in different conditions on the samples subjected to high temperature annealing were measured by using a scanning electron microscope, an energy disperse spectroscope, an X ray diffractometer and Fourier transform infrared technique respectively. The morphologies and influential factors of forsterite film were investigated. The results showed that the major compo- nent of forsterite film composed of light-gray spherical particles was Mg2 SiO4, and the minor was MgAl2O4. If the amount of MgO coated on the surface of the steel was less, bare holes or even large-scale bare grains for forsterite film appeared. The higher temperature of water bath during decarburization annealing led to gaps of strips in forster ite film. Moreover, MgO coating method had great influence on forsterite film. Roller coating method was beneficial to increase compactness and smoothness of forsterite film, but was disadvantageous to its thickness.展开更多
基金financially supported by the Fundamental Research Funds for the Central Universities (No. FRF-IC-18-006)
文摘The production of low-temperature reheated grain-oriented silicon steel is mainly based on the acquired inhibitor method.Due to the additional nitriding process,a high nitrogen content exists in the oxide layer,which changes the structure of the oxide layer.In this study,the structure of the surface oxide layer after nitriding was analyzed by scanning electron microscopy(SEM),electron back-scattered diffraction(EBSD),glow discharge spectrometry(GDS),and X-ray diffraction(XRD).The size and orientation of ferritic grains in the oxide layer were characterized,and the distribution characteristics of the key elements along the thickness direction were determined.The results show that the oxide layer of the steel sample mainly comprised particles of Fe2SiO4 and spherical and lamellar SiO2,and Fe4N and fcc-Fe phases were also detected.Moreover,the size and orientation of ferritic grains in the oxide layer were different from those of coarse matrix ferritic grains beneath the oxide layer;however,some ferritic grains exhibited same orientations as those in the neighboring matrix.Higher nitrogen content was detected in the oxide layer than that in the matrix beneath the oxide layer.The form of nitrogen enrichment in the oxide layer was analyzed,and the growth mechanism of ferritic grains during the oxide layer formation is proposed.
文摘Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, inductive devices, etc. Most recently, the factors effecting the texture and magnetic properties, e.g. impurities, rolling process and annealing process, have been greatly studied. The benefits of this study are that low core loss silicon steels with stable high-performance can be obtained through an economic production process. This review is intended to summarize the recent developments in the texture, properties, manufacture and application of oriented silicon steel sheets.
文摘Baosteel＇ s Cr-free ultrathick J coat for non-oriented silicon steel sheets has excellent insulation performance and has been successfully applied to middle and large scale electric power trains and wind electric power devices, which have stricter requirements than typical for coat insulation. In this paper, the characteristics and application of this type of coating for non-oriented silicon steel sheets were described in detail.
基金The authors acknowledge the financial support from the National Key Research and Development Program of China(No.2017YFB0903901).
文摘A Monte Carlo Potts model was developed to simulate the recrystallization process of a cold-rolled ultra-thin grain-oriented silicon steel.The orientation and image quality data from electron backscatter diffraction measurements were used as input information for simulation.Three types of nucleation mechanisms,namely,random nucleation,high-stored-energy site nucleation(HSEN),and high-angle boundary nucleation(HABN),were considered for simulation.In particular,the nucleation and growth behaviors of Goss-oriented({011}<100>)grains were investigated.Results showed that Goss grains had a nucleation advantage in HSEN and HABN.The amount of Goss grains was the highest according to HABN,and it matched the experimental measurement.However,Goss grains lacked a size advantage across all mechanisms during the recrystallization process.
基金Funded by the National Natural Science Foundation of China(Nos.51174057 and 51404159)the National High Technology Research and Development Program(No.2012AA03A503)Research Fund for the Doctoral Program of Higher Education of China(No.20130042110040)
文摘Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and ratio were analyzed based on the experimentaldata.At 1.0 T,hysteresis loss of tested steelwith scribing spacing of 8 mm descends by 8.2% compared to samples without scribing,which is similar to the totalloss variation,and abnormalloss descends by 16.8%.At 1.0 T,hysteresis loss ratio of the steelwith scribing spacing of 16 mm ascends from 55.7% to 57.9%,and eddy current loss increases from 17.4% to 24.1%,while abnormalloss descends from 26.9% to 23.7%.The experimentalresults show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormalloss.
文摘A siliconizing process to manufacture 6.5% Si steel sheet has been developed. Electric components, such as transformers and reactors are made easily from 6.5% Si steel sheet. However, improved workability is desirable to increase the applications. Therefore the improvement of workability of 6.5% Si steel sheet was investigated, and the results were obtained as follows: (a) workability of 6.5% Si steel sheet is deteriorated by grain boundary oxidization, (b) grain boundary oxidization can be restrained by the addition of C. Workability and magnetic properties of 6.5% Si steel sheet with C addition are discussed. Furthermore, it was found that the workability of high Si steel sheet was improved remarkably by varying the Si content gradient along the thickness without deterioration of high frequency magnetic properties. This newly developed magnetic gradient high Si steel sheet is also discussed.
基金National Natural Science Foundation of China!(No. 59671037).
文摘Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.
基金the Key International Cooperation of National Natural Science Foundation of China under Grant 51920105011Liaoning BaiQianWan Talents Programthe Natural Science Foundation of LiaoNing Province under Grant 2021-YQ-09。
文摘High-speed motor has the characteristics of high frequency, high temperature, and more stress, resulting in the field distribution inside the motor being complicated. To better study the electromagnetic characteristics of silicon steel sheet for high-speed motor. In this article, a study on the calculation model of silicon sheet electromagnetic characteristics considers the effects of electromagnetic, stress, and temperature factors. The study is divided into two parts, one is to propose the calculation model of silicon steel sheet’s permeability;the other is to improve the calculation model of silicon steel sheet’s loss. Then, the magnetic field, stress field, and temperature field of a surface mount high speed permanent magnet motor(SMHSPMSM) are analyzed by finite element method(FEM), and the results under the consideration of magnetic, stress, and temperature factors are brought into the calculation model for calculation. Finally, the accuracy of the calculation model for electromagnetic characteristics of silicon steel sheet is verified by comparing the calculated results with the finite element results.
基金supported by the National Natural Science Foundation of China(No.50174020).
文摘CW-CO2 laser nitriding technique was applied to improve the properties （such as aging property and the core loss） of grain oriented silicon steel. The samples were nitrided with regular space. Laser power density and scanning speed were chosen as 7.8×10^5W·cm^-2 and 100mm·min^-1. By some laser irradiation, Fe4N and Fe3N were formed in the nitrided zone. The nitrided samples were annealed at the temperatures ranged from 100 to 90℃. The core loss of some interested samples was tested. The results show that the core loss of the nitrided samples with different thickness of 0.23 and 0.30mm decreased by 14.9% and 9.4% respectively, and the aging property were improved up to 800℃. The mechanism of laser nitriding to improve the properties of grain oriented silicon steel is discussed.
基金Financial support from the National HighTechnology Research and Development Program of China(No.2012AA03A505)
文摘By rolling and nitriding processes, 0.23- to 0.3-mm-thick grain-oriented 6.5 wt% silicon steel sheets were produced. The core losses of grain-oriented 6.5 wt% silicon steel at frequencies ranging from 400 Hz to 20 kHz were lower than that of the grain-oriented 3 wt% silicon steel with the same thickness by 16.6-35.8%. The secondary recrystallization behavior was investigated by scanning electron microscopy, energy-dispersive spectroscopy, and electron backscattered diffraction. The results show that the secondary recrystallization in high-silicon steel sheets develops more completely as the nitrogen content increases after nitriding, secondary recrystallized grain sizes become larger, and the sharpness of Goss texture increases. Because more { 110} （116） grains in the subsurface and the central layer of the sheets have a lot of 20°-45° high-energy boundaries in addition to Goss grains, {110} （116） can be the main component through selective growth during secondary recrystallization when the inhibitor quantity is not enough and inhibitor intensity is weaker. The increases in nitrogen content can increase the inhibitor intensity and hinder abnormal growth of a mount of {110} （116） grains and therefore enhance the sharpness of Goss texture.
文摘The product quality of graiworiented silicon steel may be affected by each process because of its complicat- ed production technology. Morphologies, compositions and structures of forsterite film formed in different conditions on the samples subjected to high temperature annealing were measured by using a scanning electron microscope, an energy disperse spectroscope, an X ray diffractometer and Fourier transform infrared technique respectively. The morphologies and influential factors of forsterite film were investigated. The results showed that the major compo- nent of forsterite film composed of light-gray spherical particles was Mg2 SiO4, and the minor was MgAl2O4. If the amount of MgO coated on the surface of the steel was less, bare holes or even large-scale bare grains for forsterite film appeared. The higher temperature of water bath during decarburization annealing led to gaps of strips in forster ite film. Moreover, MgO coating method had great influence on forsterite film. Roller coating method was beneficial to increase compactness and smoothness of forsterite film, but was disadvantageous to its thickness.