The refining and modification effect of Ti (from GRAI), B, Sr and RE (cerium-riched mixtures of rare earth) on the mechanical properties of A356 aluminum alloys under T5 and T6 treatment condition were studied by OM, ...The refining and modification effect of Ti (from GRAI), B, Sr and RE (cerium-riched mixtures of rare earth) on the mechanical properties of A356 aluminum alloys under T5 and T6 treatment condition were studied by OM, SEM, EDAX, etc. It is found that the addition of RE to A356 alloys containing Ti and/or B and Sr makes strength and elongation increase in T6 treatment, but make elongation decrease in T5 treatment, at the same time, the long axis ofα(Al) grain structure decreases and the mean diameters of silicon particles increase with RE additions increasing. Grain refining with 0.01%Ti plus 0.03% B makes the dendriteα(Al) grain structure transform into equiaxed structure, resulting in obvious increase of elongation percentage. The mean diameters of silicon particles in T5 treatment are smaller than that in T6 treatment. Roundness of silicon particles in T5 treatment is higher than that in T6 treatment. A356 alloys modified and refined with Ti, B and Sr obtain the best mechanical properties in T5 treatment, however, the alloys with Ti, B, RE and Sr additions obtain the best mechanical properties in T6 treatment.展开更多
The influence of Ti, B, RE (cerium-rich mixtures of rare earth) and Sr, applied in modification and refining processes, on A356 aluminum alloys has been studied with the aids of OM, etc. The results show that the grai...The influence of Ti, B, RE (cerium-rich mixtures of rare earth) and Sr, applied in modification and refining processes, on A356 aluminum alloys has been studied with the aids of OM, etc. The results show that the grain refining efficiency of Grain-Refining Aluminium Ingot (GRAI) and Al-Ti master alloys is similar. But the Tiaddition from GRAI has lower costs than that with Al-Ti master alloys. So A356 aluminum alloys produced with GRAI are feasible in economy. Grain refining with GRAI with 0.01%Ti plus additional 0.03% B offers significant advantages over that from GRAI with 0.1% Ti only in A356 aluminum alloys, which made the dendrite α(Al) grain structure transform into equiaxed α(Al) grain structure, plus a partially modified eutectic silicon structure. RE addition to A356 aluminum alloys with Sr modifier is enable to achieve small DAS, reduced pores, well-refined fibrous silicon, small and dispersive eutectic colonies.展开更多
文摘The refining and modification effect of Ti (from GRAI), B, Sr and RE (cerium-riched mixtures of rare earth) on the mechanical properties of A356 aluminum alloys under T5 and T6 treatment condition were studied by OM, SEM, EDAX, etc. It is found that the addition of RE to A356 alloys containing Ti and/or B and Sr makes strength and elongation increase in T6 treatment, but make elongation decrease in T5 treatment, at the same time, the long axis ofα(Al) grain structure decreases and the mean diameters of silicon particles increase with RE additions increasing. Grain refining with 0.01%Ti plus 0.03% B makes the dendriteα(Al) grain structure transform into equiaxed structure, resulting in obvious increase of elongation percentage. The mean diameters of silicon particles in T5 treatment are smaller than that in T6 treatment. Roundness of silicon particles in T5 treatment is higher than that in T6 treatment. A356 alloys modified and refined with Ti, B and Sr obtain the best mechanical properties in T5 treatment, however, the alloys with Ti, B, RE and Sr additions obtain the best mechanical properties in T6 treatment.
文摘The influence of Ti, B, RE (cerium-rich mixtures of rare earth) and Sr, applied in modification and refining processes, on A356 aluminum alloys has been studied with the aids of OM, etc. The results show that the grain refining efficiency of Grain-Refining Aluminium Ingot (GRAI) and Al-Ti master alloys is similar. But the Tiaddition from GRAI has lower costs than that with Al-Ti master alloys. So A356 aluminum alloys produced with GRAI are feasible in economy. Grain refining with GRAI with 0.01%Ti plus additional 0.03% B offers significant advantages over that from GRAI with 0.1% Ti only in A356 aluminum alloys, which made the dendrite α(Al) grain structure transform into equiaxed α(Al) grain structure, plus a partially modified eutectic silicon structure. RE addition to A356 aluminum alloys with Sr modifier is enable to achieve small DAS, reduced pores, well-refined fibrous silicon, small and dispersive eutectic colonies.