The final fractural forms and variation status of hard inclusion samples under biaxial compression have been primarily studied in this paper. The lateral fractural forms of samples are mainly compressive shear fractu...The final fractural forms and variation status of hard inclusion samples under biaxial compression have been primarily studied in this paper. The lateral fractural forms of samples are mainly compressive shear fracture, two kinds appear on surface: one is strike slip fault with reversed thrust, and another is thrust. Some hard inclusions rupture and some do not while hard contact serves between hard inclusions and sample; main fracture bypasses hard inclusion while soft contact serves. Finally, process of stress concentration, yield, softening until failure for hard inclusions have been analysed under a certain condition.展开更多
Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) amorphous alloys were obtained by single-roller melt-spinning technique and the effect of Y addition on the glass forming ability(GFA), crystallization and micro-hardness of Mg-Ni ...Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) amorphous alloys were obtained by single-roller melt-spinning technique and the effect of Y addition on the glass forming ability(GFA), crystallization and micro-hardness of Mg-Ni alloys were studied. The results show that the GFA of Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) is improved successfully with the Y addition. The highest GFA appeares at x=6, while the reduced glass transition temperature (Trg) is 0.5225 and the supercooled liquid region(ΔTx) is 42.06 K; the position of the main diffraction halo is different for the alloys, and the maximum of the main diffraction halo of alloys with x=0, 1, 3 corresponds to the main peaks of a metastable fcc-Mg6Ni or fcc-Mg6Ni + Ni-Y intermetallic phases, and for the alloys with x=6, 10, it corresponds to Mg-Y and Ni-Y intermetallic phases; the micro-hardness of the alloys is improved with Y additions, and the highest micro-hardness is obtained at x=6 at.%, which is 960 MPa.展开更多
文摘The final fractural forms and variation status of hard inclusion samples under biaxial compression have been primarily studied in this paper. The lateral fractural forms of samples are mainly compressive shear fracture, two kinds appear on surface: one is strike slip fault with reversed thrust, and another is thrust. Some hard inclusions rupture and some do not while hard contact serves between hard inclusions and sample; main fracture bypasses hard inclusion while soft contact serves. Finally, process of stress concentration, yield, softening until failure for hard inclusions have been analysed under a certain condition.
基金supported by the Award Fund for Outstanding Young Scientist in Shandong Province, China (No. BS2011CL004)
文摘Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) amorphous alloys were obtained by single-roller melt-spinning technique and the effect of Y addition on the glass forming ability(GFA), crystallization and micro-hardness of Mg-Ni alloys were studied. The results show that the GFA of Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) is improved successfully with the Y addition. The highest GFA appeares at x=6, while the reduced glass transition temperature (Trg) is 0.5225 and the supercooled liquid region(ΔTx) is 42.06 K; the position of the main diffraction halo is different for the alloys, and the maximum of the main diffraction halo of alloys with x=0, 1, 3 corresponds to the main peaks of a metastable fcc-Mg6Ni or fcc-Mg6Ni + Ni-Y intermetallic phases, and for the alloys with x=6, 10, it corresponds to Mg-Y and Ni-Y intermetallic phases; the micro-hardness of the alloys is improved with Y additions, and the highest micro-hardness is obtained at x=6 at.%, which is 960 MPa.