Current progress of research on heat -resistant Mg alloys: A review

With the increasing attention received by lightweight metals,numerous essential fields have increased requirements for mag-nesium(Mg)alloys with good room-temperature and high-temperature mechanical properties.However,the high-temperature mechanic-al properties of commonly used commercial Mg alloys,such as AZ91D,deteriorate considerably with increasing temperatures.Over the past several decades,extensive efforts have been devoted to developing heat-resistant Mg alloys.These approaches either inhibit the gen-eration of thermally unstable phases or promote the formation of thermally stable precipitates/phases in matrices through solid solution or precipitation strengthening.In this review,numerous studies are systematically introduced and discussed.Different alloy systems,includ-ing those based on Mg–Al,Mg–Zn,and Mg–rare earth,are carefully classified and compared to reveal their mechanical properties and strengthening mechanisms.The emphasis,limitations,and future prospects of these heat-resistant Mg alloys are also pointed out and dis-cussed to develop heat-resistant Mg alloys and broaden their potential application areas in the future.

Effect of Mn addition on microstructure and mechanical properties of GX40CrNiSi25-12 austenitic heat resistant steel

Three types of steels were designed on the basis of GX40CrNiSi25-12 austenitic heat resistant steel by adding different Mn contents(2wt.%,6wt.%,and 12wt.%).Thermodynamic calculation,microstructure characterization and mechanical property tests were conducted to investigate the effect of Mn addition on the microstructure and mechanical properties of the austenitic heat resistant steel.Results show that the matrix structure in all the three types of steels at room temperature is completely austenite.Carbides NbC and M_(23)C_(6)precipitate at grain boundaries of austenite matrix.With the increase of Mn content,the number of carbides increases and their distribution becomes more uniform.With the Mn content increases from 1.99%to 12.06%,the ultimate tensile strength,yield strength and elongation increase by 14.6%,8.0%and 46.3%,respectively.The improvement of the mechanical properties of austenitic steels can be explained by utilizing classic theories of alloy strengthening,including solid solution strengthening,precipitation strengthening,and grain refinement.The increase in alloy strength can be attributed to solid solution strengthening and precipitation strengthening caused by the addition of Mn.The improvement of the plasticity of austenitic steels can be explained from two aspects:grain refinement and homogenization of precipitated phases.

Wire arc additive manufacturing of a heat-resistant Al-Cu-Ag-Sc alloy:microstructures and high-temperature mechanical properties

With a high energy efficiency,low geometric limitation,and low cracking susceptivity to cracks,wire arc additive manufacturing(WAAM)has become an ideal substitute for casting in the manufacturing of load-bearing high strength aluminum components in aerospace industry.Recently,in scientific researches,the room temperature mechanical performance of additive manufactured high strength aluminum alloys has been continuously broken through,and proves these alloys can achieve comparable or even higher properties than the forged counterpart.Since the aluminum components for aerospace usage experience high-low temperature cycling due to the absence of atmosphere protection,the high temperature performances of additive manufactured high strength aluminum alloys are also important.However,few research focuses on that.A special 2319Ag Sc with 0.4 wt.%Ag and 0.2 wt.%Sc addition designed for high temperature application is deposited successfully via cold metal transfer(CMT)based on WAAM.The microstructures and high temperature tensile properties are investigated.The results show that the as-deposited 2319Ag Sc alloy presents an alternate distribution of columnar grains and equiaxed grains with no significant textures.Main second phases are Al_(2)Cu and Al3Sc,while co-growth of Al_(2)Cu and bulk Al_(3)Sc is found on the grain boundary.During manufacturing,nanoscale Al_(2)Cu can precipitate out from the matrix.Ag and Mg form nano-scaleΩphase on the Al_(2)Cu precipitates.At 260℃,average yield strengths in the horizontal direction and vertical direction are 87 MPa±2 MPa,87 MPa±4 MPa,while average ultimate tensile strengths are 140 MPa±7 MPa,141 MPa±11 MPa,and average elongations are 11.0%±2.5%,13.5%±3.0%.Anisotropy in different directions is weak.

Effect of intermetallic compounds on heat resistance of hot roll bonded titanium alloy-stainless steel transition joint

The effect of intermetallic compounds on the heat resistance of transition joint was investigated. The experiment of post-weld heat treatment for the hot roll bonded titanium alloy-stainless steel joint using nickels interlayer was carried out, and the interface microstructure evolution due to heat treatment was presented. There was not found significant interdiffusion at stainless steel/nickel interface, when the specimens were heat treated in the temperature range of 600-800 °C for 10 and 30 min, while micro-cracks occurred at the stainless steel/nickel interface heat treated at 700 °C for 30 min. The thickness of intermetallic layers at nickel/titanium alloy interface increased at 600 °C, and micro-cracks occurred at 700 and 800 °C. The micro-cracks occurred between intermetallic layers or between intermetallic layer and nickel interlayer as well. The tensile strength of the transition joint decreased with the increase of heat treatment temperature or holding time.

Effect of Interface Form on Creep Failure and Life of Dissimilar Metal Welds Involving Nickel-Based Weld Metal and Ferritic Base Metal

For dissimilar metal welds(DMWs)involving nickel-based weld metal(WM)and ferritic heat resistant steel base metal(BM)in power plants,there must be an interface between WM and BM,and this interface suffers mechanical and microstructure mismatches and is often the rupture location of premature failure.In this study,a new form of WM/BM interface form,namely double Y-type interface was designed for the DMWs.Creep behaviors and life of DMWs containing double Y-type interface and conventional I-type interface were compared by finite element analysis and creep tests,and creep failure mechanisms were investigated by stress-strain analysis and microstructure characterization.By applying double Y-type interface instead of conventional I-type interface,failure location of DMW could be shifted from the WM/ferritic heat-affected zone(HAZ)interface into the ferritic HAZ or even the ferritic BM,and the failure mode change improved the creep life of DMW.The interface premature failure of I-type interface DMW was related to the coupling effect of microstructure degradation,stress and strain concentrations,and oxide notch on the WM/HAZ interface.The creep failure of double Y-type interface DMW was the result of Type IV fracture due to the creep voids and micro-cracks on fine-grain boundaries in HAZ,which was a result of the matrix softening of HAZ and lack of precipitate pinning at fine-grain boundaries.The double Y-type interface form separated the stress and strain concentrations in DMW from the WM/HAZ interface,preventing the trigger effect of oxide notch on interface failure and inhibiting the interfacial microstructure cracking.It is a novel scheme to prolong creep life and enhance reliability of DMW,by means of optimizing the interface form,decoupling the damage factors from WM/HAZ interface,and then changing the failure mechanism and shifting the failure location.

Construction of coal pitch-based HA-K grafted poly condensates and their excellent anti-temperature and viscosity-reducing properties

Humic acids(HAs)are widely used as filtrate and viscosity reducers in drilling fluids.However,their practical utility is limited due to poor stability in salt resistance and high-temperature resistance.Hightemperature coal pitch(CP)is a by-product from coal pyrolysis above 650℃.The substance's molecular structure is characterized by a dense arrangement of aromatic hydrocarbon and alkyl substituents.This unique structure gives it unique chemical properties and excellent drilling performance,surpassing traditional humic acids in drilling operations.Potassium humate is prepared from CP(CP-HA-K)by thermal catalysis.A new type of high-quality humic acid temperature-resistant viscosity-reducer(Graft CP-HA-K polymer)is synthesized with CP-HA-K,hydrolyzed polyacrylonitrile sodium salt(Na-HPAN),urea,formaldehyde,phenol and acrylamide(AAM)as raw materials.The experimental results demonstrate that the most favorable conditions for the catalytic preparation of CP-HA-K are 1 wt%catalyst dosage,30 wt%KOH dosage,a reaction temperature of 250℃,and a reaction time of 2 h,resulting in a maximum yield of CP-HA-K of 39.58%.The temperature resistance of the Graft CP-HA-K polymer is measured to be 177.39℃,which is 55.39℃ higher than that of commercial HA-K.This is due to the abundant presence of amide,hydroxyl,and amine functional groups in the Graft CP-HA-K polymer,which increase the length of the carbon chains,enhance the electrostatic repulsion on the surface of solid particles.After being aged to 120℃ for a specified duration,the Graft CP-HA-K polymer demonstrates significantly higher viscosity reduction(42.12%)compared to commercial HA-K(C-HA-K).Furthermore,the Graft CP-HA-K polymer can tolerate a high salt concentration of 8000 mg.L-1,measured after the addition of optimum amount of 3 wt%Graft CP-HA-K polymer.The action mechanism of Graft CP-HA-K polymer on high-temperature drilling fluid is that the Graft CP-HA-K polymer can increase the repulsive force between solid particles and disrupt bentonite's reticulation structure.Overall,this research provides novelty insights into the synthesis of artificial humic acid materials and the development of temperature-resistant viscosity reducers,offering a new avenue for the utilization of CP resources.

Precipitation behavior and martensite lath coarsening during tempering of T/P92 ferritic heat-resistant steel

Tempering is an important process for T/P92 ferritic heat-resistant steel from the viewpoint of microstructure control, as it facili- tates the formation of final tempered martensite under serving conditions. In this study, we have gained deeper insights on the mechanism underlying the microstructural evolution during tempering treatment, including the precipitation of carbides and the coarsening of martensite laths, as systematically analyzed by optical microscopy, transmission electron microscopy, and high-resolution transmission electron mi- croscopy. The chemical composition of the precipitates was analyzed using energy dispersive X-ray spectroscopy. Results indicate the for- mation of M3C （cementite） precipitates under normalized conditions. However, they tend to dissolve within a short time of tempering, owing to their low thermal stability. This phenomenon was substantiated by X-ray diffraction analysis. Besides, we could observe the precipitation of fine carbonitrides （MX） along the dislocations. The mechanism of carbon diffusion controlled growth of M23C6 can be expressed by the Zener＇s equation. The movement of Y-junctions was determined to be the fundamental mechanism underlying the martensite lath coarsening process. Vickers hardness was estimated to determine their mechanical properties. Based on the comprehensive analysis of both the micro- structural evolution and hardness variation, the process of tempering can be separated into three steps.

Improvements of heat resistance and adhesive property of condensed poly-nuclear aromatic resin via epoxy resin modification

A bisphenol epoxy resin was used as modifier to increase the heat resistance of condensed poly-nuclear aromatic （COPNA） resin. The basic properties of COPNA resin and modified resin were characterized by Fourier transform infrared spectroscopy （FT-IR）, nuclear magnetic resonance spectroscopy （1H-NMR）, vapor pressure osmometry （VPO） and elemental analysis （EA）. Average structural parameters of resins were calculated by the improved Brown-Ladner method, and heat resistance of resins was tested by thermogravimetric analysis （TGA）. The chemical structure, mechanical properties and heat resistivity of the resin/graphite composites prepared with different resins were compared. The results show that the adhesive property and heat resistance of COPNA resin can be remarkably improved by addition of 5 wt.% epoxy resin. The reason is that the reactions between epoxy groups of epoxy resin and hydroxyl groups of COPNA resin improve the heat resistance and adhesive property of COPNA resin. Electric motor brushes with good mechanical properties and low electrical resistivity were successfully prepared by using the modified resin as binder.

Effects of composite scale on high temperature oxidation resistance of Fe-Cr-Ni heat resistant alloy

Fe-Cr-Ni heat resistant alloys with aluminum and silicon addition, alone and in combination, were melted using an intermediate frequency induction furnace with a non-oxidation method. By the oxidation weight gain method, the oxidation resistances of the test alloys were determined at 1,200 ℃ for 500 hours. According to the oxidation weight gains, the oxidation kinetic curves were plotted and the functions were regressed by the least squares method. The results show that the oxidation kinetic curves follow the power function of y = ax^b （a〉0, 0〈b〈1）. The effects of scale compositions on oxidation resistance were studied further by analyses using X-ray diffraction （XRD） and scanning electron microscope （SEM）. It is found that the composite scale compounds of Cr203, a-Al2O3, SiO2 and FeCr2O4, with compact structure and tiny grains, shows complete oxidation resistance at 1,200℃. When the composite scale lacks a-Al2O3 or SiO2, it becomes weak in oxidation resistance with a loose structure. By the criterion of standard Gibbs formation free energy, the model of the nucleation and growth of the composite scale is established. The forming of the composite scale is the result of the competition of being oxidized and reduced between aluminum, silicon and the matrix metal elements of iron, chromium and nickel. The protection of the composite scale is analyzed essentially by electrical conductivity and strength properties.

Coarsening behavior of MX carbonitrides in type 347H heat-resistant austenitic steel during thermal aging

In this work, the growth kinetics of MX （M - metal, X - C/N） nanoprecipitates in type 347H austenitic steel was systematically studied. To investigate the coarsening behavior and the growth mechanism of MX carbonitrides during long-term aging, experiments were performed at 700, 800, 850, and 900℃ for different periods （1, 24, 70, and 100 h）. The precipitation behavior of carbonitrides in specimens subjected to various aging conditions was explored using carbon replicas and transmission electron microscopy （TEM） observations. The corresponding sizes ofMX carbonitrides were measured. The results demonstrates that MX carbonitrides precipitate in type 347H austenitic steel as Nb（C,N）. The coarsening rate constant is time-independent; however, an increase in aging temperature results in an increase in coarsening rate of Nb（C,N）. The coarsening process was analyzed according to the calculated diffusion activation energy of Nb（C,N）. When the aging temperature was 800-900℃, the mean activation energy was 294 kJ·mol -1, and the coarsening behavior was controlled primarily by the diffusion of Nb atoms.

Microstructural Evolution of 2.25Cr-1.6W-V-Nb Heat Resistant Steel during Creep

2.25Cr-1.6W-V-Nb developed in Japan, is a low alloy heat resistant steel with good comprehensive properties. Influence of long term creep at elevated temperature on the structure of 2.25Cr-1.6W-V-Nb steel was studied in this paper, and the micromechanism of creep strength degradation was elucidated, too. Both TEM observation and thermodynamic calculation reveal that during creep the transformation occurs from M7C3 and M23C6 to M6C, which can be cavity nucleation sites. Besides, creep at 600癈 also leads to the decrease of dislocation density, the coarsening and coalescence of M23C6, the nucleation of cavities and development of cracks. The strength decrease of 2.25Cr-1.6W-V-Nb steel after long term creep is related to the decrease of dislocation hardening, precipitation hardening, solution hardening, the nucleation of cavities and development of cracks.

Hot deformation behavior of Super304H austenitic heat resistant steel

The hot compression tests of Super304H austenitic heat resistant steel were carried out at 800-1200℃and 0.005-5 s^-1 using a Gleeble 3500 thermal-mechanical simulator,and its deformation behavior was analyzed.The results show that the flow stress of Super304H steel decreases with the decrease of strain rate and the increase of deformation temperature; the hot deformation activation energy of the steel is 485 kJ/mol.The hot deformation equation and the relationship between the peak stress and the deformation temperature and strain rate is obtained.The softening caused by deformation heating cannot be neglected when both the deformation temperature and strain rate are higher.

IMPROVEMENT OF TYPE IV CRACKING RESISTANCE OF 9Cr HEAT RESISTING STEEL WELDMENT BY BORON ADDITION

Creep lives of high Cr ferritic heat resisting steel weldments decrease due to Type Ⅳ fracture, which occurs as a result of formation and growth of creep voids and cracks on grain boundaries in fine-grained heat affected zone (HAZ). Because boron is considered to suppress the coarsening of grain boundary precipitates and growth of creep voids, we have investigated the effect of boron addition on the creep properties of 9Cr steel weldments. Four kinds of 9Cr3WSCoVNb steels with boron content varying from 4.7×10-5 to 1.8×10-4 and with nitrogen as low as 2.0×10-5 were prepared. The steel plates were welded by gas tungsten arc welding and crept at 923K. It was found that the microstructures of HAZ were quite different from those of conventional high Cr steels such as P91 and P92, namely the fine-grained HAZ did not exist in the present steel weldments. Boron addition also has the effect to suppress coarsening of grain boundary carbides in HAZ during creep. As a result of these phenomena, the welded joints of present steels showed no Type Ⅳ fractures and much better creep lives than those of conventional steels.

Micro-analysis of high-temperature oxidation-resistance of a new kind of heat-resistant grid plate in grate-kiln

To further improve the oxidation-resistance of materials and reduce the cost of grid plates in grate-kiln, a new kind of heat-resistant grid plate was developed. The microstructure of this grid plate with a life more than 18 months was studied by XRD, SEM and EDS techniques. The results show that high hardness, high intensity and good impact property make the new kind of heat-resistant grid plate and its oxide film have a higher resistance to deformation and abrasion at 900-1000℃ Besides, small grain size is beneficial to form a complete protective oxide film. The oxide film composed of SiO2 layer, Cr2O3 layer and Fe2O3 layer is rather thin and bonds closely with the backing. The forming of the chemical stable nickel-rich layer increases the density of Cr2O3 layer.

Characterizing pressure fluctuation into single-loop oscillating heat pipe

The pressure characteristics inside single loop oscillating heat pipe （OHP） having 4.5 mm inner diameter copper tube with the loop height of 440 mm were addressed. Distilled water was used as working fluid inside the OHP with different filling ratios of 40%, 60% and 80% of total inside volume. Experimental results show that the thermal characteristics are significantly inter-related with pressure fluctuations as well as pressure frequency. And the pressure frequency also depends upon the evaporator temperature that is maintained in the range of 60-96 ℃. Piezoresistive absolute pressure sensor （Model-Kistler 4045A5） was used to take data. The investigation shows that the filling ratio of 60% gives the highest inside pressure magnitude at maximum number of pressure frequency at any of set evaporator temperature and the lowest heat flow resistance is achieved at 60% filling ratio.

EFFECT OF HEAT TREATMENT ON INTERMEDIATE TEMPERATURE STRESS RUPTURE PROPERTIES OF ALLOY K403

The standard heat treatment of cast nickel base superalloy K403 is the solid solution treatment of 1210℃/4h, air cooling. It is very difficult to meet the requirements of Aviation Standard HB5155, in which the stress rupture life at 750℃ and 645MPa is longer than 50h. The results showed that the intermediate temperature stress rupture properties impaired by treatment of 1210℃/4h were due to precipitation of too small γ′ phase(<0.2μm) in grains and absence of the secondary carbides at grain boundaries. Microstructure containing the intergranular M6C carbides with envelope of γ′ and the residual coarse γ′ was obtained by means of 1180℃/4h treatment, therefore the stress rupture life was obviously increased to meet the demand of HB5155. The effect of γ′ size was also discussed from the view point of deformation mechanism in this paper.

Formation Mechanism and Existing Form of Sb in Heat Resistance Mg-Gd-Y-Sb Alloy

The existing form and reaction mechanism of Sb in heat resistane Mg-Gd-Y-Sb rare earth magnesium alloy were investigated by inductive coupled plasma emission spectroscopy(ICP),scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS),and X-ray diffraction(XRD).It is found that Sb tends to form high melting point intermetallics with rare earth elements of Gd and Y.The existing form of Sb is determined to be GdSb and SbY,respectively,which has high melting point(GdSb:2142℃/SbY:1782℃).Meanwhile,the first principle calculation and electronegativity difference calculation were performed to further understand the reaction mechanism.Therefore,the forming heat and binding energy were calculated.The experimental results show that the binding tendency of Sb element to Gd and Y is much stronger than that of it with other elements in this alloy,which results in the formation of high melting point of Gd-Sb and Y-Sb intermetallics,and finally leads to the high temperature resistant further improvement of the Mg-Gd-Y magnesium alloy.

Heat Resistance of TiN Coated HSS Tools

The cutting friction, cutting deformation, producing heat, conducting heat, temperature field of TiN coated HSS tools in the cutting process are discussed profoundly. In order to make clear the heat property of TiN coated tools, from the micromechanism angle, the relationship of the heat property and the crystal structure of TiN compound is analyzed, and the regularity of TiN compound crystal structure changing with temperature rising is sought. The difference of the wear resistance and heat resistance of TiN coated tools deposited by c1 and c2 depositing techniques is proved by tests. The conclusions will offer the theoretical basis for correct design of geometrical parameters of TiN coated tools, rational selection of cutting regimes and optimization of the depositing technique.

Effect of Aluminium and Silicon on High Temperature Oxidation Resistance of Fe-Cr-Ni Heat Resistant Steel

Fe-Cr-Ni heat resistant steels with different contents of Al and Si were cast in intermediate frequency induction furnace with non-oxidation method. With oxidation weight gain method, the oxidation resistance of test alloys was examined at 1 200 ℃ for 500 h. The effects of Al and Si on oxidation resistance were studied through analyses of X-ray diffraction （XRD） and scanning electron microscope （SEM）. It is shown that the composition of oxide scales is a decisive factor for the oxidation resistance of heat resistant steels. The compounded scale composed of Cr203, α-Al2O3, SiO2 and Fe （Ni）Cr2O4, with flat and compact structure, fine and even grains, exhibits complete oxidation resistance at 1 200 ℃. Its oxidation weight gain rate is only 0.081 g/（m^2.h）. By the criterion of standard Gibbs formation free energy, a model of nucleation and growth of the compounded scale was established. The formation of the compounded scale was the result of the competition of being oxidated and reduction among Al, Si, and the matrix metal elements of Fe, Cr and Ni. The protection of the compounded scale was analyzed from the perspectives of electrical conductivity and strength properties.

High-temperature oxidation behavior of heat resistant stainless steel 1.4828

The kinetic curves of the high-temperature oxidation of austenitic heat resistant stainless steel 1. 4828 at 1 050 ℃ were measured using a weighing method. It is shown that the oxidation curves at 1 050 ℃ followed the parabolic line law, and after 250 h of oxidation, the mass gain was about 80 g/m2. The surface morphology and structure of the oxide layers were studied by scanning electron microscopy and X-ray diffraction. A complicated oxide layer obtained at 1 050 ℃ was mainly composed, from inner to outer, of （FeSi） 3 04, Cr2 03, Fe2 03, and spinel oxides FeCr204 and NiMn204.