In this paper the heat withstanding mechanism of heat-resisting aluminum alloy conductor is discussed, the types and performance of the conductor and its application on transmission lines are analyzed and introduced, ...In this paper the heat withstanding mechanism of heat-resisting aluminum alloy conductor is discussed, the types and performance of the conductor and its application on transmission lines are analyzed and introduced, and suggestions on accelerating exploitation and application of the conductor are put forward.展开更多
A heat resistant aluminum alloy pipe blank with dimensions of d 700/300 mm×1 200 mm was prepared by the multi layer spray deposition technology. Optical microscopy, X ray diffractometry and transmission electron ...A heat resistant aluminum alloy pipe blank with dimensions of d 700/300 mm×1 200 mm was prepared by the multi layer spray deposition technology. Optical microscopy, X ray diffractometry and transmission electron microscopy were used to analyze its morphologies and microstructures. The results show that the microstructures of the pipe blank are homogeneous and the precipitates are uniformly distributed d 25～70 nm spherical or sphere like Al 12 (Fe,V) 3Si particles, its mechanical properties at room temperature and 350 ℃ after densification by extrusion are σ b=412 MPa, δ =7.6% and σ b=187 MPa, δ =7.6%, respectively. The analyses indicate that the proper match of the motion rates of atomizer and substrate can produce deposited blanks with uniform thickness and relatively high cooling rate.展开更多
The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical ...The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...展开更多
2195 aluminum-lithium alloy was widely applied in the aviation and aerospace industry, but it is highly susceptible to pitting and intergranular corrosion undergoing sever corrosive circumstance and moisture atmospher...2195 aluminum-lithium alloy was widely applied in the aviation and aerospace industry, but it is highly susceptible to pitting and intergranular corrosion undergoing sever corrosive circumstance and moisture atmosphere. To solve this problem and consequently to prolong its service life, a multi-step-heating-rate(MSRC) process was carried out. Investigations were carried out to find the effect of the MSRC process on the alloys corrosion resistance. It is found that the MSRC process is more favorable for the uniform phase precipitation by comparing the corrosion resistance of samples treated by traditional heat treatments. The potential difference between phases can be reduced and intergranular corrosion is able to be prohibited efficiently. Besides, the rare earth infiltration is beneficial to improving the corrosion resistance. As heating time increases, the corrosion resistance declines gradually, samples treated by artificial aging and solid solution also exhibit a better corrosion resistance.展开更多
In this paper, the composition, two-dimensional and three-dimensional microstructure of heat-resistant wrought aluminum alloy with strong oxidation resistance, heat resistance and easy processing are analyzed by using...In this paper, the composition, two-dimensional and three-dimensional microstructure of heat-resistant wrought aluminum alloy with strong oxidation resistance, heat resistance and easy processing are analyzed by using direct reading spectrometer, metallographic microscope and scanning electron microscope. The main alloy elements of heat-resistant forging aluminum alloy include Cu, Mg, Si, Ni and Fe. The α solid solution of each element in aluminum consists of S phase (Al<sub>2</sub>CuMg), Mg<sub>2</sub>Si phase, bright gray Al<sub>2</sub>CuNi phase and dark brown Al<sub>9</sub>FeNi phase. The distribution of each phase in the aluminum alloy is determined by the three-dimensional energy spectrum analysis of the microstructure, and the distribution of each phase in the crystal position is analyzed. The mechanism of heat resistance, easy processing type and wear resistance is obtained, which provides the theoretical basis for the development and use of heat-resistant forged aluminum alloy.展开更多
Al-8.5Fe-1.3V-1.7Si alloy was prepared by spray deposition and hot extrusion. The high temperature plastic deformation behavior of the spray deposited Al-8.5Fe-1.3V-1.7Si alloy was investigated in the strain rate rang...Al-8.5Fe-1.3V-1.7Si alloy was prepared by spray deposition and hot extrusion. The high temperature plastic deformation behavior of the spray deposited Al-8.5Fe-1.3V-1.7Si alloy was investigated in the strain rate range of 2.77×10-4-2.77×10-2 s-1 and temperature range of 350-550 ℃ by Gleebe-1500 thermomechanical simulator. The mechanism of the high temperature plastic deformation of the alloys was studied by TEM associated with the analysis of Rosler-Artz physical constitutive relationship based on the model of dislocation detaching from dispersion particles. The results show that Al-Fe-V-Si alloy has low strain hardening coefficient, and even exhibits work softening. Stress exponent n and activation energy Q were calculated based on Zener-Hollomon relation and Rosler-Artz physical model respectively. The Rosler-Artz physical model can give a good prediction for the abnormal behavior of high temperature deformation of spray deposited Al-Fe-V-Si alloy, that is, n larger than 8 and Q higher than 142 kJ/mol. However, because of the highly refined microstructure, the high temperature deformation behavior of spray deposited Al-Fe-V-Si alloy deviates more or less from the law predicted by using Rosler-Artz physical model.展开更多
文摘In this paper the heat withstanding mechanism of heat-resisting aluminum alloy conductor is discussed, the types and performance of the conductor and its application on transmission lines are analyzed and introduced, and suggestions on accelerating exploitation and application of the conductor are put forward.
文摘A heat resistant aluminum alloy pipe blank with dimensions of d 700/300 mm×1 200 mm was prepared by the multi layer spray deposition technology. Optical microscopy, X ray diffractometry and transmission electron microscopy were used to analyze its morphologies and microstructures. The results show that the microstructures of the pipe blank are homogeneous and the precipitates are uniformly distributed d 25～70 nm spherical or sphere like Al 12 (Fe,V) 3Si particles, its mechanical properties at room temperature and 350 ℃ after densification by extrusion are σ b=412 MPa, δ =7.6% and σ b=187 MPa, δ =7.6%, respectively. The analyses indicate that the proper match of the motion rates of atomizer and substrate can produce deposited blanks with uniform thickness and relatively high cooling rate.
文摘The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...
基金Project(51471050105HK0101) supported by the National Key Laboratory of Precision Thermal Treatment, Harbin Institute of Technology,China
文摘2195 aluminum-lithium alloy was widely applied in the aviation and aerospace industry, but it is highly susceptible to pitting and intergranular corrosion undergoing sever corrosive circumstance and moisture atmosphere. To solve this problem and consequently to prolong its service life, a multi-step-heating-rate(MSRC) process was carried out. Investigations were carried out to find the effect of the MSRC process on the alloys corrosion resistance. It is found that the MSRC process is more favorable for the uniform phase precipitation by comparing the corrosion resistance of samples treated by traditional heat treatments. The potential difference between phases can be reduced and intergranular corrosion is able to be prohibited efficiently. Besides, the rare earth infiltration is beneficial to improving the corrosion resistance. As heating time increases, the corrosion resistance declines gradually, samples treated by artificial aging and solid solution also exhibit a better corrosion resistance.
文摘In this paper, the composition, two-dimensional and three-dimensional microstructure of heat-resistant wrought aluminum alloy with strong oxidation resistance, heat resistance and easy processing are analyzed by using direct reading spectrometer, metallographic microscope and scanning electron microscope. The main alloy elements of heat-resistant forging aluminum alloy include Cu, Mg, Si, Ni and Fe. The α solid solution of each element in aluminum consists of S phase (Al<sub>2</sub>CuMg), Mg<sub>2</sub>Si phase, bright gray Al<sub>2</sub>CuNi phase and dark brown Al<sub>9</sub>FeNi phase. The distribution of each phase in the aluminum alloy is determined by the three-dimensional energy spectrum analysis of the microstructure, and the distribution of each phase in the crystal position is analyzed. The mechanism of heat resistance, easy processing type and wear resistance is obtained, which provides the theoretical basis for the development and use of heat-resistant forged aluminum alloy.
文摘Al-8.5Fe-1.3V-1.7Si alloy was prepared by spray deposition and hot extrusion. The high temperature plastic deformation behavior of the spray deposited Al-8.5Fe-1.3V-1.7Si alloy was investigated in the strain rate range of 2.77×10-4-2.77×10-2 s-1 and temperature range of 350-550 ℃ by Gleebe-1500 thermomechanical simulator. The mechanism of the high temperature plastic deformation of the alloys was studied by TEM associated with the analysis of Rosler-Artz physical constitutive relationship based on the model of dislocation detaching from dispersion particles. The results show that Al-Fe-V-Si alloy has low strain hardening coefficient, and even exhibits work softening. Stress exponent n and activation energy Q were calculated based on Zener-Hollomon relation and Rosler-Artz physical model respectively. The Rosler-Artz physical model can give a good prediction for the abnormal behavior of high temperature deformation of spray deposited Al-Fe-V-Si alloy, that is, n larger than 8 and Q higher than 142 kJ/mol. However, because of the highly refined microstructure, the high temperature deformation behavior of spray deposited Al-Fe-V-Si alloy deviates more or less from the law predicted by using Rosler-Artz physical model.