In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the ...In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the optimized mold flux were compared in a comprehensive way by using analytical measures, such as a slag film heat-flow simulator, a thermowire molten flux crystallization tester and an X-ray diffractometer in the laboratory. The results reveal that one of the major reasons for the cracks is the poor heat transfer ability of the original mold flux. However, the optimized mold flux with a high basicity features a high crystallizing rate,low crystallization temperature and low heat-flow density. Therefore, the optimized mold flux is more suitable for casting peritectic steel by the heavy slab continuous caster. The test results show that the slabs produced by using the optimized mold flux had no surface longitudinal crack in four test casts, while the surface longitudinal crack ratio of the slabs produced by using the original mold flux was 5%. The optimized mold flux can effectively prevent slab surface longitudinal cracks from occurring.展开更多
In order to research the influence of La2O3 on crystallization behavior of free-fluoride mould flux and the heat transfer of slag film,free-fluoride mould flux with various La2O3 content were investigated by using sel...In order to research the influence of La2O3 on crystallization behavior of free-fluoride mould flux and the heat transfer of slag film,free-fluoride mould flux with various La2O3 content were investigated by using self-made mould simulator,comprehensive thermal analyzer and SEM-EDS.With the increase of La2O3 content from 0% to 20%,the crystallization ratios of mould flux films were improved from 2% to 90% and the thicknesses of films were also enhanced over two times.Moreover,crystallization temperature was greatly raised and its increasing extent reached 100 oC.It could also decrease the melting temperature of casting powder about 50 oC.However,the undissolved La2O3 particles appeared in slag film if the ratio of La2O3 in free-fluoride mould flux was much too high.展开更多
An experimental apparatus for simulating copper mold is used to quantify the heat flux through the slag film and to obtain a solid slag for further determining its crystallization behavior. The result indicates that b...An experimental apparatus for simulating copper mold is used to quantify the heat flux through the slag film and to obtain a solid slag for further determining its crystallization behavior. The result indicates that both the chemical composition of the mold powder and the cooling rate have an important influence on the heat flux through the slag film. With increasing the binary basicity, the heat flux of slag film decreases at first, reaches the minimum at the basicity of 1.4, and then increases, indicating that the maximum binary basicity is about 1.4 for selecting ＂mild cooling＂ mold powder. The heat transfer through the slag film can be specified in terms of the crystalline ratio and the thickness of the slag film. Recrystallization of the solid slag occurs and must be considered as an important factor that may influence the heat transfer through the solid slag layer.展开更多
Numerical simulation has been done for liquid film cooling in liquid rocket combustor.Multiple species of axial Navier-Stokes equations have been solved for liquid-film / hot-gas flow field,and k-εequations have been...Numerical simulation has been done for liquid film cooling in liquid rocket combustor.Multiple species of axial Navier-Stokes equations have been solved for liquid-film / hot-gas flow field,and k-εequations have been used for compressible turbulent flow.The results of the model agree well with the results of software FLUENT.The results show that :(1) Liquid film can decrease the wall heat flux and temperature effectively,and the cold border area formed by the film covers the whole combustor and nozzle wall.(2) The turbulent viscosity is higher than the physical viscosity,and its biggest value is in the border area of the convergent area in nozzle.The effect of turbulent flow on the whole simulation field can not be ignored.(3) The mass fraction of kerosene at the film inlet is 1,but it decreases along the nozzle wall and achieves its lowest value at the outlet.However,the mass fraction of kerosene near the wall is the biggest at any axial location.展开更多
文摘In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the optimized mold flux were compared in a comprehensive way by using analytical measures, such as a slag film heat-flow simulator, a thermowire molten flux crystallization tester and an X-ray diffractometer in the laboratory. The results reveal that one of the major reasons for the cracks is the poor heat transfer ability of the original mold flux. However, the optimized mold flux with a high basicity features a high crystallizing rate,low crystallization temperature and low heat-flow density. Therefore, the optimized mold flux is more suitable for casting peritectic steel by the heavy slab continuous caster. The test results show that the slabs produced by using the optimized mold flux had no surface longitudinal crack in four test casts, while the surface longitudinal crack ratio of the slabs produced by using the original mold flux was 5%. The optimized mold flux can effectively prevent slab surface longitudinal cracks from occurring.
基金Project supported by the Inner Mongolia Science Foundation of China (20080404MS)
文摘In order to research the influence of La2O3 on crystallization behavior of free-fluoride mould flux and the heat transfer of slag film,free-fluoride mould flux with various La2O3 content were investigated by using self-made mould simulator,comprehensive thermal analyzer and SEM-EDS.With the increase of La2O3 content from 0% to 20%,the crystallization ratios of mould flux films were improved from 2% to 90% and the thicknesses of films were also enhanced over two times.Moreover,crystallization temperature was greatly raised and its increasing extent reached 100 oC.It could also decrease the melting temperature of casting powder about 50 oC.However,the undissolved La2O3 particles appeared in slag film if the ratio of La2O3 in free-fluoride mould flux was much too high.
基金Item Sponsored by National Natural Science Foundation of China (50574109)
文摘An experimental apparatus for simulating copper mold is used to quantify the heat flux through the slag film and to obtain a solid slag for further determining its crystallization behavior. The result indicates that both the chemical composition of the mold powder and the cooling rate have an important influence on the heat flux through the slag film. With increasing the binary basicity, the heat flux of slag film decreases at first, reaches the minimum at the basicity of 1.4, and then increases, indicating that the maximum binary basicity is about 1.4 for selecting ＂mild cooling＂ mold powder. The heat transfer through the slag film can be specified in terms of the crystalline ratio and the thickness of the slag film. Recrystallization of the solid slag occurs and must be considered as an important factor that may influence the heat transfer through the solid slag layer.
文摘Numerical simulation has been done for liquid film cooling in liquid rocket combustor.Multiple species of axial Navier-Stokes equations have been solved for liquid-film / hot-gas flow field,and k-εequations have been used for compressible turbulent flow.The results of the model agree well with the results of software FLUENT.The results show that :(1) Liquid film can decrease the wall heat flux and temperature effectively,and the cold border area formed by the film covers the whole combustor and nozzle wall.(2) The turbulent viscosity is higher than the physical viscosity,and its biggest value is in the border area of the convergent area in nozzle.The effect of turbulent flow on the whole simulation field can not be ignored.(3) The mass fraction of kerosene at the film inlet is 1,but it decreases along the nozzle wall and achieves its lowest value at the outlet.However,the mass fraction of kerosene near the wall is the biggest at any axial location.