Experiments were conducted to study the general room temperature corrosion characteristics of heat-treated and non-heat-treated Al-Li alloys with different Li compositions. Corrosion rate was measured using both the p...Experiments were conducted to study the general room temperature corrosion characteristics of heat-treated and non-heat-treated Al-Li alloys with different Li compositions. Corrosion rate was measured using both the polarisation method and the weight-loss method. It was observed that the samples with higher Li content had lower corrosion resistance than those with lower Li content. Moreover, for all the specimens tested, it was fOund that heat treatment at 180℃ for 2 h (for the purpose of precipitation hardening) severely reduced the corrosion resistance,whereas heat treatment at 180℃ for 6 h significantly increased the corrosion resistance.展开更多
文摘Experiments were conducted to study the general room temperature corrosion characteristics of heat-treated and non-heat-treated Al-Li alloys with different Li compositions. Corrosion rate was measured using both the polarisation method and the weight-loss method. It was observed that the samples with higher Li content had lower corrosion resistance than those with lower Li content. Moreover, for all the specimens tested, it was fOund that heat treatment at 180℃ for 2 h (for the purpose of precipitation hardening) severely reduced the corrosion resistance,whereas heat treatment at 180℃ for 6 h significantly increased the corrosion resistance.