16.6%Co/γ-Al2O3 catalysts prepared by incipient wetness impregnation method were used for Fischer-Tropsch synthesis. The support was pre-treated with different concentration of NH4NO3 aqueous solution. The effect of ...16.6%Co/γ-Al2O3 catalysts prepared by incipient wetness impregnation method were used for Fischer-Tropsch synthesis. The support was pre-treated with different concentration of NH4NO3 aqueous solution. The effect of support pre-treatment on the properties of support and performance of supportedcobalt-based catalysts was investigated. To treat the support with NH4NO3 aqueous solution enlarged the pore of γ-Al2O3, decreased the impurity Na2O content, and weakened the surface acidity of γ-Al2O3. The change in the properties of the support decreased the interaction between cobalt species and support, enhanced the CO hydrogenation rate and the C5+ selectivity. For all catalysts, increasing the reaction temperature increased the CO hydrogenation rate or the CO conversion, slightly decreased the total hydrocarbon selectivity, and favored the formation of methane and light hydrocarbons, while the chain growth probability decreased. For 16.6%Co/γ-Al2O3 catalysts, prepared with the support treated with 100 g/L NH4NO3 aqueous solution, the CO conversion, the CH4 selectivity, and the C5+ selectivity were 83.13%, 6.86% and 82.75% respectively, and the chain growth probability was 0.83 under the condition of 493 K, 1.5 MPa, 500 h-1 and the molar ratio of H2 to CO being 2.0 in feed.展开更多
基金This work was supported by the Doctoral Foundation of China(No.20050251006).
文摘16.6%Co/γ-Al2O3 catalysts prepared by incipient wetness impregnation method were used for Fischer-Tropsch synthesis. The support was pre-treated with different concentration of NH4NO3 aqueous solution. The effect of support pre-treatment on the properties of support and performance of supportedcobalt-based catalysts was investigated. To treat the support with NH4NO3 aqueous solution enlarged the pore of γ-Al2O3, decreased the impurity Na2O content, and weakened the surface acidity of γ-Al2O3. The change in the properties of the support decreased the interaction between cobalt species and support, enhanced the CO hydrogenation rate and the C5+ selectivity. For all catalysts, increasing the reaction temperature increased the CO hydrogenation rate or the CO conversion, slightly decreased the total hydrocarbon selectivity, and favored the formation of methane and light hydrocarbons, while the chain growth probability decreased. For 16.6%Co/γ-Al2O3 catalysts, prepared with the support treated with 100 g/L NH4NO3 aqueous solution, the CO conversion, the CH4 selectivity, and the C5+ selectivity were 83.13%, 6.86% and 82.75% respectively, and the chain growth probability was 0.83 under the condition of 493 K, 1.5 MPa, 500 h-1 and the molar ratio of H2 to CO being 2.0 in feed.