Carbon nanotubes （CNTs） are excellent scaffolds for advanced electrode materials, resulting from their intrinsic sp2 carbon hybridization, interconnected electron pathway, large aspect ratio, hierarchical porous str...Carbon nanotubes （CNTs） are excellent scaffolds for advanced electrode materials, resulting from their intrinsic sp2 carbon hybridization, interconnected electron pathway, large aspect ratio, hierarchical porous structures, and low cost at a large-scale production. How to make full utilization of the mass produced CNTs as building blocks for nanocomposite electrodes is not well understood yet. Herein, a composite cathode containing commercial agglomerated multi-walled CNTs and S for Li-S battery was fabricated by a facile melt-diffusion strategy. The hierarchical CNT@S coaxial nanocables exhibited a discharging capacity of 1020 and 740 mAh .g-1 at 0.5 and 2.0 C, respectively. A rapid capacity decay of 0.7% per cycle at the initial 10 cycles and a slow decay rate of 0.14% per cycle for the later 140 cycles were detected. Such hierarchical agglomerated CNT@ S cathodes show advantages in easy fabrication, environmentally benign, low cost, excellent scalability, and good Li ion storage performance, which are extraordinary composites for high performance Li-S battery.展开更多
基金supported by National Basic Research Program of China (973 Program, 2011CB932602)Research Fund for the Doctoral Program of Higher Education of China (20120002120047)China Postdoctoral Science Foundation (2012M520293)
文摘Carbon nanotubes （CNTs） are excellent scaffolds for advanced electrode materials, resulting from their intrinsic sp2 carbon hybridization, interconnected electron pathway, large aspect ratio, hierarchical porous structures, and low cost at a large-scale production. How to make full utilization of the mass produced CNTs as building blocks for nanocomposite electrodes is not well understood yet. Herein, a composite cathode containing commercial agglomerated multi-walled CNTs and S for Li-S battery was fabricated by a facile melt-diffusion strategy. The hierarchical CNT@S coaxial nanocables exhibited a discharging capacity of 1020 and 740 mAh .g-1 at 0.5 and 2.0 C, respectively. A rapid capacity decay of 0.7% per cycle at the initial 10 cycles and a slow decay rate of 0.14% per cycle for the later 140 cycles were detected. Such hierarchical agglomerated CNT@ S cathodes show advantages in easy fabrication, environmentally benign, low cost, excellent scalability, and good Li ion storage performance, which are extraordinary composites for high performance Li-S battery.