Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composite...Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composites were investigated at different temperatures (773-1173K), and the microstructures of carbon/carbon composites were studied by SEM and X-ray diffraction. The experimental results showed that the inter-laminar distance of (002) plane (d002) deceased while the microcrystalline stack height (Lc) increased. The oxidation rate of felt base carbon/carbon composites was invari-able at certain temperatures. The oxidation mechanism of carbon/carbon composites changed remarkably at the oxidation temperature 973K. At the initial oxidation stage of carbon/carbon composites, carbon matrix was oxidized much more rapidly than carbon felt.展开更多
Nano hafnium carbide（HfC） powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling trea...Nano hafnium carbide（HfC） powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling treatment on the phase and morphology of pyrolysis products（HfO_2-C） and final HfC product were investigated and the influences of heat treatment temperature and holding time on the structure and properties of the synthesized hafnium carbide powders were also studied. The experimental results showed that the HfO_2-C powders with good uniformity and small particle size were prepared by controlling the milling time. Pure HfC powders with an average particle size of 500 nm were obtained at 1 700 ℃ with a holding time of 3 min, and the oxygen content was about 0.69 wt%, lower than that of the hafnium carbide powders prepared by SPS（0.97%）.展开更多
The deoiled asphalt as the carbon source and the ferrocene as the metal source and the catalyst precursor were chosen to synthesize iron-containing carbon microparticles through co-carbonization at the temperature of ...The deoiled asphalt as the carbon source and the ferrocene as the metal source and the catalyst precursor were chosen to synthesize iron-containing carbon microparticles through co-carbonization at the temperature of about 450℃ for 3 h. The resulting products were treated at 2 000 ℃ for 2 h. All samples were examined by high resolution transmission electron microscopy （HRTEM） and X-ray diffraction （XRD）. The results show that the iron particles in the heat-treated material are completely coated by carbon. In addition to the fully filled carbon microparticles as well as hollow carbon ones, also form carbon fibers with hollow centers. The formation mechanism of the as-prepared products was discussed briefly.展开更多
文摘Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composites were investigated at different temperatures (773-1173K), and the microstructures of carbon/carbon composites were studied by SEM and X-ray diffraction. The experimental results showed that the inter-laminar distance of (002) plane (d002) deceased while the microcrystalline stack height (Lc) increased. The oxidation rate of felt base carbon/carbon composites was invari-able at certain temperatures. The oxidation mechanism of carbon/carbon composites changed remarkably at the oxidation temperature 973K. At the initial oxidation stage of carbon/carbon composites, carbon matrix was oxidized much more rapidly than carbon felt.
基金the National Key R&D Program of China(2017YFB0310400)the National Natural Science Foundation of China(51672197)
文摘Nano hafnium carbide（HfC） powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling treatment on the phase and morphology of pyrolysis products（HfO_2-C） and final HfC product were investigated and the influences of heat treatment temperature and holding time on the structure and properties of the synthesized hafnium carbide powders were also studied. The experimental results showed that the HfO_2-C powders with good uniformity and small particle size were prepared by controlling the milling time. Pure HfC powders with an average particle size of 500 nm were obtained at 1 700 ℃ with a holding time of 3 min, and the oxygen content was about 0.69 wt%, lower than that of the hafnium carbide powders prepared by SPS（0.97%）.
基金National Basic Research Program of China (2004CB217808)National Natural Science Foundation of China (20471041, 90306014)+1 种基金Natural Science Foundation of Shanxi Province (20051018)Shanxi Research Fund for Returned Scholars (200428)
文摘The deoiled asphalt as the carbon source and the ferrocene as the metal source and the catalyst precursor were chosen to synthesize iron-containing carbon microparticles through co-carbonization at the temperature of about 450℃ for 3 h. The resulting products were treated at 2 000 ℃ for 2 h. All samples were examined by high resolution transmission electron microscopy （HRTEM） and X-ray diffraction （XRD）. The results show that the iron particles in the heat-treated material are completely coated by carbon. In addition to the fully filled carbon microparticles as well as hollow carbon ones, also form carbon fibers with hollow centers. The formation mechanism of the as-prepared products was discussed briefly.