Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure

The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite （CFB/M） complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10^7 cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10^7, and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of ＂soft structure＂. It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.

High-cycle fatigue behavior of friction stir butt welded 6061 aluminium alloy

Friction stir welding （FSW） of 6061 aluminium alloy butt joint was carried out at each rotation speed of 600, 800, 1000, 1200 r/min for two different travel speeds, 80 and 100 mm/min, at a constant probe depth of 1.85 mm. The calculated energy input based on the FSW parameters studied shows that the ultimate tensile strength （UTS） of the butt joint is obtained within a certain range of energy input of 297 kJ to 354 kJ out of total range of energy input studied from 196 kJ to 405 kJ. The fatigue behaviors of high-strength and low-strength joints performed at different stress ratios, i.e., 0.5, 0.3, 0.1, -0.3, -0.5, indicate that the fatigue behaviors of both the welds are sensitive to the microstructural features, such as stir zone （SZ）, thermo mechanically affected zone （TMAZ） and heat affected zone （HAZ）. The observed fatigue strengths were discussed in terms of the microstructure, crack path behavior and fracture surface.

Effect of nano-sized Al2O3 reinforcing particles on uniaxial and high cycle fatigue behaviors of hot-forged AZ31B magnesium alloy

The effect of hot-forging process was investigated on microstructural and mechanical properties of AZ31 B alloy and AZ31 B/1.5 vol.%Al2 O3 nanocomposite under static and cycling loading. The as-cast alloy and composite were firstly subjected to a homogenization heat treatment at 450 ℃ and then an open-die forging at 450 ℃. The results indicated that the presence of reinforcing particles led to grain refinement and improvement of dynamic recrystallization. The forging process was more effective to eliminate the porosity in the cast alloy workpiece. Microhardness of the forged composite was increased by up to 80% and 16%, in comparison with those of the cast and forged alloy samples, respectively. Ultimate tensile strength and maximum tensile strain of the composite were improved by up to 45% and 23%, compared with those of the forged alloy in similar regions. These enhancements were respectively 50% and 37% in the compression test. The composite exhibited a fatigue life improvement in the region with low applied strain;however, a degradation was observed in the high applied strain region. Unlike AZ31 B samples, tensile, compressive and high cycle fatigue behaviors of the composite showed less sensitivity to the applied strain, which can be attributed to the amount of porosity in the samples before and after the hot-forging.

A two-parameter model to predict fatigue life of high-strength steels in a very high cycle fatigue regime

In this paper, ultrasonic （20 kHz） fatigue tests were performed on specimens of a high-strength steel in very high cycle fatigue （VHCF） regime. Experimental results showed that for most tested specimens failed in a VHCF regime, a fatigue crack originated from the interior of specimen with a fish-eye pattern, which contained a fine granular area （FGA） centered by an inclusion as the crack origin. Then, a two-parameter model is proposed to predict the fatigue life of high-strength steels with fish-eye mode failure in a VHCF regime, which takes into account the inclusion size and the FGA size. The model was verified by the data of present experiments and those in the literature. Furthermore, an analytic formula was obtained for estimating the equivalent crack growth rate within the FGA. The results also indicated that the stress intensity factor range at the front of the FGA varies within a small range, which is irrespective of stress amplitude and fatigue life.

High cycle fatigue behavior of the second generation single crystal superalloy DD6

The second generation single crystal superalloy DD6 with 0.10%Hf and 0.34%Hf （in mass fraction） was subjected to high-cycle fatigue （HCF） loading at temperatures of 700 ℃ in ambient atmosphere. SEM was used to determine the initiation site and the failure mechanism. Evolution of the microstructure was investigated by TEM observation. The results show that fatigue limit of DD6 alloy with 0.34%Hf is a little smaller than that of the alloy with 0.10%Hf. The fatigue cracks initiated on the surface or near the surface of the specimens. The crack would propagate along { 111 } octahedral slip planes, rather than perpendicular to the loading axis of specimen. Typical fatigue striation formed in steady propagation of fatigue crack. The fracture mechanisms of the high cycle fatigue of DD6 alloys with 0.10%Hf and 0.34%Hf are quasi-cleavage fracture. Different types of dislocation structures were developed during high cycle fatigue deformation.

Current understanding of ultra-high cycle fatigue

The fatigue life of numerous aerospace,locomotive,automotive and biomedical structures may go beyond 10~8 cycles.Determination of long life fatigue behavior becomes extremely important for better understanding and design of the components and structures.Initially,before the invention of ultrasonic fatigue testing,most of the engineering materials were supposed to exhibit fatigue life up to 10~7 cycles or less.This paper reviews current understanding of some fundamental aspects on the development of accelerated fatigue testing method and its application in ultra-high cycle fatigue,crack initiation and growth mechanisms of internal fracture,S-N diagram,fatigue limit and life prediction, etc.

High Cycle Fatigue Properties of Die-Cast Magnesium Alloy AZ91D with Addition of Different Concentrations of Cerium

The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa （ 1% Ce） and 105.5 MPa （2 % Ce）, respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.

Tensile and high-cycle fatigue properties of spray formed Al10.8Zn2.9Mg1.9Cu alloys after two-stage aging treatment

Based on the investigation of the tensile properties of spray formed ultra-high strength Al10.8Zn2.9Mg1.9Cu alloys, the high-cycle fatigue properties under different theoretical stress concentration factors were investigated, the fatigue fracture surfaces and microstructures were observed, and the fatigue mechanism was discussed. The results indicate that the ultimate tensile strength of spray formed Al10.8Zn2.9Mg1.9Cu alloys can reach up to 730?740 MPa, and the elongation is about 8%?10% under the condition of two-stage aging treatment. For the stress ratio is 0.1, the maximum stress for 107 cycles is over 400 MPa and 120 MPa, when the theoretical stress concentration factor is 1 and 3, respectively.

High-cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime up to 107 cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy （FESEM）. It was found that the size of inclusion has significant effect on the fatigue behavior. For AtSI 4340 steel in which the inclusion size is smaller than 5.5 μm, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 μm, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 pro. In the case of internal inclusion-induced fractures at cycles beyond about 1×10^6 for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet （GBF） was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure Nf in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with Nf, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1×10^6. Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.

Effect of low cycle fatigue pre-damage on very high cycle fatigue

Carbon-manganese steel is often applied in components of pipes in nuclear plant. Ultrasonic fatigue tests following low cycle fatigue （LCF） cycles damaged are used to study the strength of very high cycle fatigure （VHCF）. The comparison of test results of simple VHCF and cumulative fatigue （LCF plus VHCF） shows that LCF load influences the following VHCF strength. Continuum damage mechanics model is extended to VHCF region.

Very high cycle fatigue for GCr15 steel with smooth and hole-defect specimens

Very high cycle fatigue（VHCF） properties of a low temperature tempering bearing steel GCr15 with smooth and hole-defect specimens are studied by employing a rotary bending test machine with frequency of 52.5 Hz.Both smooth and hole-defect specimens break in VHCF regime with some difference in fatigue crack initiation.For smooth specimens,a fine granular area（FGA） is observed near the grain boundary in the fracture surface of the specimens broken after 10~7 cycles. But no FGA is observed in the hole-defect specimens broken in VHCF regime,and the VHCF crack does not initiate from the small hole at the surface as it does at low or high cycle fatigue regime. Internal stress is employed to explain the VHCF behavior of these two types of specimens.At last,an advanced dislocation model based on Tanaka and Mura model is proposed to illustrate the internal stress process and to predict fatigue crack initiation life with FGA observed in the fracture region.

EFFECT OF MICROSTRUCTURE OF ALUMINIDE COATING ON HIGH-CYCLE FATIGUE PERFORMANCE OF COATING-SUPERALLOY SYSTEM

The high-cycle fatigue performance of different microstructures of aluminide coating- superalloy system has been studied at 900℃.The single phase coating of coarse equiaxial grain NiAI(β)has unfavorable eJfect onJatigue life of the coating-superalloy.The fatigue life may shorten if the coating of NiAl(β)was an enrichment of coarse refractory metal grains. While an improvement can be made by dispersing numerous secondary phase particles such as extreme.fine γ′,quasi-σ-phase and others.

High cycle fatigue behavior of the forged Mg-7Gd-5Y-1Nd-0.5Zr alloy

This paper investigated the high cycle fatigue behavior of a forged Mg-7Gd-5Y-1Nd-0.5Zr alloy with different stress concentration factor(Kt),under different stress ratio(R),and along different loading direction.The smooth specimen(Kt=1),under R=0.1 and along longitude direction,shows a high fatigue strength of 162 MPa at 107 cycles.The fatigue behavior of the forged Mg-7Gd-5Y-1Nd-0.5Zr alloy exhibits a high sensitive to the notch.Moreover,change of stress ratio from 0.1 to−1 may also result in a bad fatigue property.The flux inclusions were elongated along longitude direction and/or transverse direction during the forging process of the Mg-7Gd-5Y-1Nd-0.5Zr alloy.The interface between the flux inclusion and the matrix may debond and serve as the crack initiation site during the fatigue loading process,leading to the deterioration of the fatigue property along thickness direction and a high anisotropic fatigue behavior between longitude direction and thickness direction.

Effect of long-period stacking ordered structure on very high cycle fatigue properties of Mg-Gd-Y-Zn-Zr alloys

Magnesium alloys with a long-period stacking ordered(LPSO)structure usually possess excellent static strength,but their fatigue behaviors are poorly understood.This work presents the effect of the LPSO structure on the crack behaviors of Mg alloys in a very high cycle fatigue(VHCF)regime.The LPSO lamellas lead to a facet-like cracking process along the basal planes at the crack initiation site and strongly prohibit the early crack propagation by deflecting the growth direction.The stress intensity factor at the periphery of the faceted area is much higher than the conventional LPSO-free Mg alloys,contributing higher fatigue crack propagation threshold of LPSO-containing Mg alloys.Microstructure observation at the facets reveals a layer of ultrafine grains at the fracture surface due to the cyclic contact of the crack surface,which supports the numerous cyclic pressing model describing the VHCF crack initiation behavior.

Influence of Ageing Heat Treatment on the High Cycle Fatigue of an 8090 Al-Li Alloy

Fatigue lives for the smooth and notched specimens of 8090 Al-Li alloy jn the different ageing conditions have been studied. For the smooth samples of 8090 alloy the artificial ageing results in an increase in fatigue life in comparison with natural ageing. On the contrary, the notched specimens of 8090 alloy in the naturally aged condition show higher fatigue life than in the peak-aged. The exposure to either the peak-aged or naturally aged leads to superior fatigue properties of Al-Li alloy to the traditional high strength aluminum alloys of 7075 and 2024, especially in the latter aged condition. In all ageing conditions, i,e. naturally, under-, peak- and over-aged, the peak-aged 8090 alloy displays the highest fatigue life and the over-aged material has a minimum value at the same stress amplitude. The difference in fatigue life is mainly attributable to the size and distribution of strengthening precipitates as well as the wide of precipitate free zones (PFZ's) along grain boundaries.

Very High Cycle Fatigue Behaviors and Surface Crack Growth Mechanism of Hydrogen-Embrittled AISI 304 Stainless Steels

The influence of hydrogen embrittlement on the fatigue behaviors of AISI 304 stainless steel is investigated. The fatigue endurance limits of the untreated and hydrogen-embrittled materials were almost the same at 400 MPa, and hydrogen embrittlement had little influence even though the sample contained about 8.1 times more hydrogen. Thus, the sensitivity of hydrogen gas in this material is very low. A surface crack initiation, growth, coalescence, and micro ridge model is proposed in this study. Slip line formation?⇒microcrack formation?⇒increases in the crack width, and blunting of the crack tip as it grows?⇒formation of many slip lines because of deformation in the shear direction?⇒growth of the crack in the shear direction, forming micro ridges, coalescence with adjacent cracks ⇒?continuous initiation, growth, coalescence, and ridge formation of surface cracks and specimen breakage.

High-cycle fatigue behavior of nickel-base single crystal superalloy

High-cycle rotating bending fatigue behavior of SRR99 nickel-base single crystal alloy at 700 and 900℃ was investigated. The fatigue strengths for 107 cycles are 350 and 335MPa at 700 and 900℃, respectively. The total fatigue life becomes shorter when the temperature increases regardless of the loading stress and frequency. With the number of cycles decreasing, the difference in fatigue strength at the two temperatures becomes smaller. Typical fatigue rupture process including crack initiation site, crack propagation region and final rupture region exhibits at 700℃. The fracture surface is basically characterized by cleavage rupture at 900℃.

High cycle fatigue properties of die-cast magnesium alloy AZ91 D-1%MM

<正>The high cycle fatigue properties of the die-cast magnesium alloy AZ91D containing 1%mischmetal(mass fraction) at a fatigue ratio of 0.1 were investigated.The difference in the microstructure between the skin and core region of the die-cast magnesium alloy was analyzed by optical microscopy.The mechanical property tests indicate that the values of the tensile strength, elongation and hardness are 185 MPa,1.5%and HBS 70±3 at room temperature,respectively.The p-S-N curve(p=50%) of the die-cast magnesium alloy AZ91D-1%MM is determined and the mean fatigue strength corresponding to 3.8×10~5 cycles is 70 MPa. A linear relation between S and N_p in log scale between 10~3 and 10~6 cycles is written with a equation.The mechanical properties are influenced by the casting defects.The fatigue life of the samples with minor defects is near to the upper limit of the fatigue life data. The fatigue fracture surface of the samples with minor defects possesses the mixed characteristics of quasi-cleavage,lacerated ridge and dimple and it is brittle fracture mode as a whole.

Effect of heat treatment on high-cycle fatigue behavior of Mg-Zn-Y-Zr alloy

High-cycle fatigue (HCF) behavior of as-forged-T5 Mg-Zn-Y-Zr wrought alloy with stress-ratio R=-1 at ambient environment was presented. The relationship between the maximum stress and the number of cycles to failure was constructed. The results show that the fatigue strength at 107 cycles of the as-forged alloy in T5 state is higher than that of the alloy in T4 state. However, in T6 state, the fatigue strength at 107 cycles is higher than those of the alloys in both T5 and T4 states.

Improving fatigue strength of bainite/martensite dual-phase steels in very high cycle fatigue regime by refining microstructures

Very high cycle fatigue behaviors of two bainite/martensite dual-phase steels were investigated.One of the steels was cyclic rapid heat treated and its microstructures were refined. Fatigue strength of the steel is 225 MPa higher than that without refining.Observation of fracture surfaces show that the fatigue cracks initiate at bainites for non-refined steel and at non-metallic inclusions for the refined steel.The size of inclusions is much smaller than that of bainites which results in the improvement of fatigue strength.