The microstructure, mechanical properties and wear resistance of high chromium cast steel containing boron after different heat treatments were studied by means of the optical microscopy （OM）, the scanning electron ...The microstructure, mechanical properties and wear resistance of high chromium cast steel containing boron after different heat treatments were studied by means of the optical microscopy （OM）, the scanning electron microscopy （SEM）, X-ray diffraction （XRD）, hardness, impact toughness, tensile and pin-on-disc abrasion tests. The results show that as cast microstructures of boron-free high chromium steel consist of martensite and a few （Cr, Fe）_7C_3 carbide, and the macro-hardness of boron-free high chromium steel is 55-57 HRC. After 0.5 mass% B was added into high chromium cast steel, as-cast structure transforms into eutectic （Fe, Cr）2B, （Cr, Fe）7 （C, B）a and martensite, and the macro-hardness reaches 58-60 HRC. High temperature quenching leads to the disconnection and isolated distribution of boride, and there are many （Cr,Fe）_23 （C,B）_6 precipitated phases in the quenching structure. Quenching from 1050 ℃, high chromium steel obtained the highest hardness, and the hardness of high chromium cast steel containing boron is higher than that of boron-free high chromium steel. The change of quenching temperature has no obvious effect on impact toughness of high chromium steel, and the increase of quenching temperature leads to tensile strength having an increasing tendency. At the same quenching temperature, the wear resistance of high chromium cast steel containing boron is more excellent than that of boron-free high chromium steel. High chromium cast steel guide containing boron has good performance while using in steel bar mill.展开更多
In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing ...In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.展开更多
The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-c...The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-chromium cast steel are obviously improved after hot deformation,and the best mechanical properties of the cast steel can be obtained under hot deformation ratio of 40 %-50 %,which leads to the morphology change of eutectic carbide and the precipitation of granular carbides.展开更多
Wear properties of two different crushers used for grinding raw materials of cement industry are compared using pin-on-disk wear test.The wear test was carried out with different loads on a pin.Abrasive wear behavior ...Wear properties of two different crushers used for grinding raw materials of cement industry are compared using pin-on-disk wear test.The wear test was carried out with different loads on a pin.Abrasive wear behavior of two alloys was evaluated by comparing mass loss,wear resistance,microhardness and friction coefficient.The microstructure of the specimens was detected using optical microscope.The results showed that abrasive wear of high chromium cast iron is lower than that of Hadfield steel.Due to the presence of M7C3 carbides on the high chromium cast iron matrix,impact crushers exhibited higher friction coefficient展开更多
基金Item Sponsored by National Natural Science Foundation of China(51274016)Natural Science Foundation of Beijing of China(2142009)Plan Item of Beijing Education Committee of China(KM201310005003)
文摘The microstructure, mechanical properties and wear resistance of high chromium cast steel containing boron after different heat treatments were studied by means of the optical microscopy （OM）, the scanning electron microscopy （SEM）, X-ray diffraction （XRD）, hardness, impact toughness, tensile and pin-on-disc abrasion tests. The results show that as cast microstructures of boron-free high chromium steel consist of martensite and a few （Cr, Fe）_7C_3 carbide, and the macro-hardness of boron-free high chromium steel is 55-57 HRC. After 0.5 mass% B was added into high chromium cast steel, as-cast structure transforms into eutectic （Fe, Cr）2B, （Cr, Fe）7 （C, B）a and martensite, and the macro-hardness reaches 58-60 HRC. High temperature quenching leads to the disconnection and isolated distribution of boride, and there are many （Cr,Fe）_23 （C,B）_6 precipitated phases in the quenching structure. Quenching from 1050 ℃, high chromium steel obtained the highest hardness, and the hardness of high chromium cast steel containing boron is higher than that of boron-free high chromium steel. The change of quenching temperature has no obvious effect on impact toughness of high chromium steel, and the increase of quenching temperature leads to tensile strength having an increasing tendency. At the same quenching temperature, the wear resistance of high chromium cast steel containing boron is more excellent than that of boron-free high chromium steel. High chromium cast steel guide containing boron has good performance while using in steel bar mill.
基金Item Sponsored by Guiding Programme of Science and Technology Research of Hebei of China(94122123)
文摘In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.
基金Item Sponsored by Guiding Program of Science and Technology Research of Hebei Province of China(94122123)
文摘The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-chromium cast steel are obviously improved after hot deformation,and the best mechanical properties of the cast steel can be obtained under hot deformation ratio of 40 %-50 %,which leads to the morphology change of eutectic carbide and the precipitation of granular carbides.
文摘Wear properties of two different crushers used for grinding raw materials of cement industry are compared using pin-on-disk wear test.The wear test was carried out with different loads on a pin.Abrasive wear behavior of two alloys was evaluated by comparing mass loss,wear resistance,microhardness and friction coefficient.The microstructure of the specimens was detected using optical microscope.The results showed that abrasive wear of high chromium cast iron is lower than that of Hadfield steel.Due to the presence of M7C3 carbides on the high chromium cast iron matrix,impact crushers exhibited higher friction coefficient