Using TiAl alloy to substitute superalloy is a hot topic in aeroengine industry because of its low density, high elevated temperature strength, and anti-oxidization ability. In this research, Ti-47.5AL-2Cr-2Nb-0.2B al...Using TiAl alloy to substitute superalloy is a hot topic in aeroengine industry because of its low density, high elevated temperature strength, and anti-oxidization ability. In this research, Ti-47.5AL-2Cr-2Nb-0.2B alloy was used as the test material. By applying a combination process of ceramic shell mold and core making, vacuum arc melting and centrifugal pouring, and heat isostatic pressing （HIP） and heat treatment （HT） etc., the TiAl vortex agitator casting for aeroengine was successfully made. This paper introduced key techniques in making the TiAl vortex agitator with investment casting process, provided some experimental results including mechanical properties and machinability, and explained some concerns that could affect applications of TiAl castings.展开更多
The addition of rare earth yttrium(Y) can improve the performances of high temperature titanium alloys,such as the tensile ductility,thermal stability and creep property,etc.However,few studies on the effect of Y on t...The addition of rare earth yttrium(Y) can improve the performances of high temperature titanium alloys,such as the tensile ductility,thermal stability and creep property,etc.However,few studies on the effect of Y on the castability of titanium alloys have been carried out,which is significant to fabrication of thin-walled complex titanium castings by investment casting.In this study,the microstructure and mold filling capacity of a Ti-1100 alloy with different Y additions(0,0.1wt.%,0.3wt.%,0.5wt.% and 1.0wt.%) were investigated systematically through investment casting experiments,and the casting experiments were carried out in a centrifugal titanium casting machine.The microstructures of the alloy were observed via the optical microscopy,scanning electron microscopy and transmission electron microscopy.The mold filling capacity was tested by using of a grid pattern and was evaluated by the number of segments completely filled by the cast alloy.The results indicate that the grain size is decreased and the mold filling capacity is improved significantly with increasing the addition of Y from 0 to 1.0wt.%.The average primary grain size of Ti-1100 alloy is reduced from 250 μm to 50 μm and the mold filling capacity is increased from 61.5% to 100%.Considering the potential harmful effect on tensile properties of titanium alloys due to high concentrations of Y,it is suggested that Y addition should be about 0.3wt.%.展开更多
In the present study, Ti-45Al-(6, 7, 8)Nb(at%) and Ti-45Al-8Nb-0.5(Mn, Si, Y, B) alloys were prepared by arc melting and casting into Zr O2(Y2O3 stabilized) ceramic moulds to study the effect of alloying elements Nb a...In the present study, Ti-45Al-(6, 7, 8)Nb(at%) and Ti-45Al-8Nb-0.5(Mn, Si, Y, B) alloys were prepared by arc melting and casting into Zr O2(Y2O3 stabilized) ceramic moulds to study the effect of alloying elements Nb and Mn, Si, Y, B on the interfacial reaction between casting Ti Al alloys and ceramic moulds by SEM, and the elements' distribution in the interface reaction layer by line scanning. The results showed that with an increase in Nb content, the interfacial reaction weakened and the thickness of the reaction layer decreased gradually. The interface reaction thickness of the alloys with Nb content of 6, 7, 8at% were 60, 34 and 26 μm, respectively. Clearly, the addition of 8at% Nb to Ti-45 Al is the best for the thickness of the reaction layer. The addition of Nb would form a Nb-rich film in the reaction layer, which could reduce the solubility of oxygen in the interface, and suppress further diffusion of oxygen to the matrix. If the same content of Mn, Si, Y, or B alloying elements were added respectively to Ti-45Al-8Nb, the thickness of the interface reaction layer from large to small was as follows: Mn>Si>Y>B. The interface reaction thickness increased after 0.5at% Mn added, had no obvious change after 0.5at% Si addition, and decreased after adding 0.5at% Y or B. The introduced elements, which formed a protective film or/and promoted the formation of a dense aluminum oxide layer, would be of benefit to the resistance of interfacial reaction.展开更多
文摘Using TiAl alloy to substitute superalloy is a hot topic in aeroengine industry because of its low density, high elevated temperature strength, and anti-oxidization ability. In this research, Ti-47.5AL-2Cr-2Nb-0.2B alloy was used as the test material. By applying a combination process of ceramic shell mold and core making, vacuum arc melting and centrifugal pouring, and heat isostatic pressing （HIP） and heat treatment （HT） etc., the TiAl vortex agitator casting for aeroengine was successfully made. This paper introduced key techniques in making the TiAl vortex agitator with investment casting process, provided some experimental results including mechanical properties and machinability, and explained some concerns that could affect applications of TiAl castings.
文摘The addition of rare earth yttrium(Y) can improve the performances of high temperature titanium alloys,such as the tensile ductility,thermal stability and creep property,etc.However,few studies on the effect of Y on the castability of titanium alloys have been carried out,which is significant to fabrication of thin-walled complex titanium castings by investment casting.In this study,the microstructure and mold filling capacity of a Ti-1100 alloy with different Y additions(0,0.1wt.%,0.3wt.%,0.5wt.% and 1.0wt.%) were investigated systematically through investment casting experiments,and the casting experiments were carried out in a centrifugal titanium casting machine.The microstructures of the alloy were observed via the optical microscopy,scanning electron microscopy and transmission electron microscopy.The mold filling capacity was tested by using of a grid pattern and was evaluated by the number of segments completely filled by the cast alloy.The results indicate that the grain size is decreased and the mold filling capacity is improved significantly with increasing the addition of Y from 0 to 1.0wt.%.The average primary grain size of Ti-1100 alloy is reduced from 250 μm to 50 μm and the mold filling capacity is increased from 61.5% to 100%.Considering the potential harmful effect on tensile properties of titanium alloys due to high concentrations of Y,it is suggested that Y addition should be about 0.3wt.%.
基金supported by the National Basic Research Program of China(973 Program,No.2011CB605500)the"Fundamental Research Funds for the Central Universities"(FRF-MP-10-005B)the National Natural Science Foundation of China under Contract No.51171015
文摘In the present study, Ti-45Al-(6, 7, 8)Nb(at%) and Ti-45Al-8Nb-0.5(Mn, Si, Y, B) alloys were prepared by arc melting and casting into Zr O2(Y2O3 stabilized) ceramic moulds to study the effect of alloying elements Nb and Mn, Si, Y, B on the interfacial reaction between casting Ti Al alloys and ceramic moulds by SEM, and the elements' distribution in the interface reaction layer by line scanning. The results showed that with an increase in Nb content, the interfacial reaction weakened and the thickness of the reaction layer decreased gradually. The interface reaction thickness of the alloys with Nb content of 6, 7, 8at% were 60, 34 and 26 μm, respectively. Clearly, the addition of 8at% Nb to Ti-45 Al is the best for the thickness of the reaction layer. The addition of Nb would form a Nb-rich film in the reaction layer, which could reduce the solubility of oxygen in the interface, and suppress further diffusion of oxygen to the matrix. If the same content of Mn, Si, Y, or B alloying elements were added respectively to Ti-45Al-8Nb, the thickness of the interface reaction layer from large to small was as follows: Mn>Si>Y>B. The interface reaction thickness increased after 0.5at% Mn added, had no obvious change after 0.5at% Si addition, and decreased after adding 0.5at% Y or B. The introduced elements, which formed a protective film or/and promoted the formation of a dense aluminum oxide layer, would be of benefit to the resistance of interfacial reaction.
