Effects of Sn and Sb on the structure and magnetic properties of high induction oriented silicon steel have been investigated.The heats with Sn or Sb possess rather fine primary and secondary gram sizes.Sn or Sb promo...Effects of Sn and Sb on the structure and magnetic properties of high induction oriented silicon steel have been investigated.The heats with Sn or Sb possess rather fine primary and secondary gram sizes.Sn or Sb promotes the finer AlN particles,increases the amount of pre- cipitated AlN after normalizing and strengthens the ability of inhibition.After decarburizing annealing,the texture components of{110}〈115〉and〈110〉〈001〉tend to increase and form more secondary grain nuclei.展开更多
The magnetic properties and textures of grain oriented silicon steel with different thickness rolled by cross shear rolling （CSR） of different mismatched speed ratio （MSR） and annealed in magnetic field under hyd...The magnetic properties and textures of grain oriented silicon steel with different thickness rolled by cross shear rolling （CSR） of different mismatched speed ratio （MSR） and annealed in magnetic field under hydrogen were presented.Effects of the factors such as thickness and mismatched speed ratio on the magnetic properties and recrystallization texture were analyzed and the recrystallization principles in magnetic field annealing were discussed. The study would provide a new route for mass production of high quality ultra-thin grain oriented silicon steel strip.展开更多
Based on the industrial production of non-oriented silicon steel,calcium treatment by CaSi wire feeding during the RH refining process was studied. The thermodynamics of CaS inclusion formation was analyzed, and the m...Based on the industrial production of non-oriented silicon steel,calcium treatment by CaSi wire feeding during the RH refining process was studied. The thermodynamics of CaS inclusion formation was analyzed, and the morphology and the size distribution were observed. Furthermore, the change in inclusion characteristics after calcium treatment and the effect of calcium treatment on magnetic properties were discussed. The results show that the formation of MnS and A1N inclusions were restrained, and the aggregating, floating and removing of microinclusions after calcium treatment were effectively promoted. The cleanliness of liquid steel was obviously increased. The main type of inclusions was single phase of CaO, with some complex inclusions composed of CaO, SiO2 and MgO. No CaS inclusion was observed after an appropriate calcium treatment. The size of all inclusions was distributed in the range of 2 - 20 μm, and the number was about 1.8 × 10^5/mm3. In addition, as an increasing amount of calcium was added,the core loss gradually decreased to a stable level, and the magnetic induction decreased quickly after a slow increase. The optimal calcium treatment mode depends on the chemical composition of steel.展开更多
The development, production and application of top high-grade non-grain-oriented （NGO） silicon steels at Baosteel were introduced in this paper. Top high grades refer to the highest grades in the intemational silico...The development, production and application of top high-grade non-grain-oriented （NGO） silicon steels at Baosteel were introduced in this paper. Top high grades refer to the highest grades in the intemational silicon steel product standard and above. B35A230 and B50A250 were developed at Baosteel in 2009 and have been used in inverter compressors for air-conditioners, small transformers and big hydropower generators in the Three Gorges project. Small- batch production of B35A210 and B50A230, which exceed the highest grades listed in the intemational silicon steel product standard,began in 2010. That was a breakthrough in the silicon steel making history in China. Presently,Baosteel＇ s high- grade NGO products have passed the strict qualifications of the three major electric power equipment manufacturers in China and the leading international power equipment suppliers like ALSTOM, GE, SIEMENS, VESTAS, etc. These products are characterized by low iron loss, low anisotropy, good punchability and a high lamination factor. They have been used in the 770 MW hydropower generator at Xiluodu Power Station in the three gorges area, 1 000 MW thermal power generators and 2.5 MW wind power generators.展开更多
The Hi-B silicon steels were cold rolled by cross shear rolling (CSR) with different mismatch speed ratio(MSR)s and conventional rolling(CR) respectively, followed by primary recrystallization annealing. The effects o...The Hi-B silicon steels were cold rolled by cross shear rolling (CSR) with different mismatch speed ratio(MSR)s and conventional rolling(CR) respectively, followed by primary recrystallization annealing. The effects of MSR and annealing temperature on magnetic properties of ultra-thin grain oriented silicon steel were analyzed. Experimental results show that, with the increase of MSR, the magnetic properties can be remarkably improved. The higher the annealing temperature is, the higher the magnetic induction and the lower the iron loss in ultra-thin silicon steel is.展开更多
文摘Effects of Sn and Sb on the structure and magnetic properties of high induction oriented silicon steel have been investigated.The heats with Sn or Sb possess rather fine primary and secondary gram sizes.Sn or Sb promotes the finer AlN particles,increases the amount of pre- cipitated AlN after normalizing and strengthens the ability of inhibition.After decarburizing annealing,the texture components of{110}〈115〉and〈110〉〈001〉tend to increase and form more secondary grain nuclei.
文摘The magnetic properties and textures of grain oriented silicon steel with different thickness rolled by cross shear rolling （CSR） of different mismatched speed ratio （MSR） and annealed in magnetic field under hydrogen were presented.Effects of the factors such as thickness and mismatched speed ratio on the magnetic properties and recrystallization texture were analyzed and the recrystallization principles in magnetic field annealing were discussed. The study would provide a new route for mass production of high quality ultra-thin grain oriented silicon steel strip.
文摘Based on the industrial production of non-oriented silicon steel,calcium treatment by CaSi wire feeding during the RH refining process was studied. The thermodynamics of CaS inclusion formation was analyzed, and the morphology and the size distribution were observed. Furthermore, the change in inclusion characteristics after calcium treatment and the effect of calcium treatment on magnetic properties were discussed. The results show that the formation of MnS and A1N inclusions were restrained, and the aggregating, floating and removing of microinclusions after calcium treatment were effectively promoted. The cleanliness of liquid steel was obviously increased. The main type of inclusions was single phase of CaO, with some complex inclusions composed of CaO, SiO2 and MgO. No CaS inclusion was observed after an appropriate calcium treatment. The size of all inclusions was distributed in the range of 2 - 20 μm, and the number was about 1.8 × 10^5/mm3. In addition, as an increasing amount of calcium was added,the core loss gradually decreased to a stable level, and the magnetic induction decreased quickly after a slow increase. The optimal calcium treatment mode depends on the chemical composition of steel.
文摘The development, production and application of top high-grade non-grain-oriented （NGO） silicon steels at Baosteel were introduced in this paper. Top high grades refer to the highest grades in the intemational silicon steel product standard and above. B35A230 and B50A250 were developed at Baosteel in 2009 and have been used in inverter compressors for air-conditioners, small transformers and big hydropower generators in the Three Gorges project. Small- batch production of B35A210 and B50A230, which exceed the highest grades listed in the intemational silicon steel product standard,began in 2010. That was a breakthrough in the silicon steel making history in China. Presently,Baosteel＇ s high- grade NGO products have passed the strict qualifications of the three major electric power equipment manufacturers in China and the leading international power equipment suppliers like ALSTOM, GE, SIEMENS, VESTAS, etc. These products are characterized by low iron loss, low anisotropy, good punchability and a high lamination factor. They have been used in the 770 MW hydropower generator at Xiluodu Power Station in the three gorges area, 1 000 MW thermal power generators and 2.5 MW wind power generators.
文摘The Hi-B silicon steels were cold rolled by cross shear rolling (CSR) with different mismatch speed ratio(MSR)s and conventional rolling(CR) respectively, followed by primary recrystallization annealing. The effects of MSR and annealing temperature on magnetic properties of ultra-thin grain oriented silicon steel were analyzed. Experimental results show that, with the increase of MSR, the magnetic properties can be remarkably improved. The higher the annealing temperature is, the higher the magnetic induction and the lower the iron loss in ultra-thin silicon steel is.