Low cycle fatigue behavior of extruded AZ80 magnesium alloy was investigated under uniaxial tension-compression at different strain amplitudes and strain rates.The results show that the extruded AZ80 magnesium alloy e...Low cycle fatigue behavior of extruded AZ80 magnesium alloy was investigated under uniaxial tension-compression at different strain amplitudes and strain rates.The results show that the extruded AZ80 magnesium alloy exhibits cyclic hardening at strain amplitudes ranging from 0.4%to 1.0%,the asymmetry of hysteresis loops becomes increasingly obvious when the strain amplitude increases.Higher strain rates correspond to higher stress amplitudes,high mean stresses and short fatigue life.{10–12}extension twins play a role in the cyclic deformation under higher strain amplitudes(0.8%,1.0%).The relationship between total strain energy density and fatigue life can be described by the modified Morrow model.The effect of strain rate on the fatigue life can also be predicted by the model.展开更多
Studies were made of the symmetric tensile-compressive low cycle fatigue behaviour and the influence of dynamic strain aging(DSA)pre-treatment of 18-8 austenitic stainless steel. Within the testing amplitude range of ...Studies were made of the symmetric tensile-compressive low cycle fatigue behaviour and the influence of dynamic strain aging(DSA)pre-treatment of 18-8 austenitic stainless steel. Within the testing amplitude range of strain.±0.5 % to±1.5 %,the three processes of cyclic hardening,cyclic saturation and cyclic softening were observed.In the same amplitude of strain,the peak stress of the samples pre-treated by DSA is higher than that of solid-solu- tion and cold working pre-treatment,but no remarkable differences of the fatigue lives of them were found.TEM observation shows that the uniform and stable dislocation networks with high density form after DSA pre-treatment,which increases the cyclic peak stress.The cyclic softening results from the low dislocation density and elongated cell structure with low energy.展开更多
The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the hi...The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime up to 107 cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AtSI 4340 steel in which the inclusion size is smaller than 5.5 μm, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 μm, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 pro. In the case of internal inclusion-induced fractures at cycles beyond about 1×10^6 for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure Nf in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with Nf, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1×10^6. Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.展开更多
Carbon-manganese steel is often applied in components of pipes in nuclear plant. Ultrasonic fatigue tests following low cycle fatigue (LCF) cycles damaged are used to study the strength of very high cycle fatigure ...Carbon-manganese steel is often applied in components of pipes in nuclear plant. Ultrasonic fatigue tests following low cycle fatigue (LCF) cycles damaged are used to study the strength of very high cycle fatigure (VHCF). The comparison of test results of simple VHCF and cumulative fatigue (LCF plus VHCF) shows that LCF load influences the following VHCF strength. Continuum damage mechanics model is extended to VHCF region.展开更多
The low cycle fatigue (LCF) behavior of two high strength steels, withnominal chemical compositions (mass fraction, %) of 0.40C-1.5Cr-3Ni-0.4Mo-0.2V (PCrNi3MoV) and0.25C-3Cr-3Mo-0.8Ni-0.1Nb (25Cr3Mo3NiNb), was investi...The low cycle fatigue (LCF) behavior of two high strength steels, withnominal chemical compositions (mass fraction, %) of 0.40C-1.5Cr-3Ni-0.4Mo-0.2V (PCrNi3MoV) and0.25C-3Cr-3Mo-0.8Ni-0.1Nb (25Cr3Mo3NiNb), was investigated by using the smooth bar specimenssubjected to strained-controlled push-pull loading. It is found that both steels show cyclicsoftening, but 25Cr3Mo3NiNb steel has a lower tendency to cyclic softening. 25Cr3Mo3NiNb steel hashigher fatigue ductility, and its transition fatigue life is almost three times that of PCrNi3MoV.25Cr3Mo3NiNb steel also shows higher LCF life either at a given total strain amplitude above 0.5% orat any given plastic strain amplitude, despite its lower monotonic tensile strength than that ofPCrNi3MoV. It also means that 25Cr3Mo3NiNb steel can endure higher total strain amplitude andplastic strain amplitude at a given number of reversals to failure within 10~4. 25Cr3Mo3NiNb steelis expected to be a good gun steel with high LCF properties because only several thousand firingsare required for gun barrel in most cases.展开更多
The ultra-fine grained(UFG)pure titanium was prepared by equal channel angular pressing(ECAP)and rotary swaging(RS).The strain controlled low cycle fatigue(LCF)test was carried out at room temperature.The fatigue life...The ultra-fine grained(UFG)pure titanium was prepared by equal channel angular pressing(ECAP)and rotary swaging(RS).The strain controlled low cycle fatigue(LCF)test was carried out at room temperature.The fatigue life prediction model and mean stress relaxation model under asymmetrical stress load were discussed.The results show that the strain ratio has a significant effect on the low cycle fatigue performance of the UFG pure titanium,and the traditional Manson-coffin model can not accurately predict the fatigue life under asymmetric stress load.Therefore,the SWT mean stress correction model and three-parameter power curve model are proposed,and the test results are verified.The final research shows that the threeparameter power surface model has better representation.By studying the mean stress relaxation phenomenon under the condition of R≠-1,it is revealed that the stress ratio and the strain amplitude are the factors that significantly afiect the mean stress relaxation rate,and the mean stress relaxation model with the two variables is calculated to describe the mean stress relaxation phenomenon of the UFG pure titanium under different strain ratios.The fracture morphology of the samples was observed by SEM,and it was concluded that the final fracture zone of the fatigue fracture of the UFG pure titanium was a mixture of ductile fracture and quasi cleavage fracture.The toughness of the material increases with the increase of strain ratio at the same strain amplitude.展开更多
The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and f...The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa ( 1% Ce) and 105.5 MPa (2 % Ce), respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.展开更多
The cyclic stress-strain responses (CSSR), Neuber's rule (NR) and cyclic strain-life relation (CSLR) are treated as probabilistic curves in local stress and strain method of low cycle fatigue analysis. The randomn...The cyclic stress-strain responses (CSSR), Neuber's rule (NR) and cyclic strain-life relation (CSLR) are treated as probabilistic curves in local stress and strain method of low cycle fatigue analysis. The randomness of loading and the theory of fatigue damage accumulation (TOFDA) are considered. The probabilistic analysis of local stress, local strain and fatigue life are constructed based on the first-order Taylor's series expansions. Through this method proposed fatigue reliability analysis can be accomplished.展开更多
Cold Metal Transfer-Based Wire Arc Directed Energy Deposition(CMT-WA-DED)presents a promising avenue for the rapid fabrication of components crucial to automotive,shipbuilding,and aerospace industries.However,the susc...Cold Metal Transfer-Based Wire Arc Directed Energy Deposition(CMT-WA-DED)presents a promising avenue for the rapid fabrication of components crucial to automotive,shipbuilding,and aerospace industries.However,the susceptibility to fatigue of CMT-WA-DED-produced AZ31 Mg alloy components has impeded their widespread adoption for critical load-bearing applications.In this study,a comprehensive investigation into the fatigue behaviour of WA-DED-fabricated AZ31 Mg alloy has been carried out and compared to commercially available wrought AZ31 alloy.Our findings indicate that the as-deposited parts exhibit a lower fatigue life than wrought Mg alloy,primarily due to poor surface finish,tensile residual stress,porosity,and coarse grain microstructure inherent in the WA-DED process.Low Plasticity Burnishing(LPB)treatment is applied to mitigate these issues,which induce significant plastic deformation on the surface.This treatment resulted in a remarkable improvement of fatigue life by 42%,accompanied by a reduction in surface roughness,grain refinement and enhancement of compressive residual stress levels.Furthermore,during cyclic deformation,WA-DED specimens exhibited higher plasticity and dislocation density compared to both wrought and WA-DED+LPB specimens.A higher fraction of Low Angle Grain Boundaries(LAGBs)in WA-DED specimens contributed to multiple crack initiation sites and convoluted crack paths,ultimately leading to premature failure.In contrast,wrought and WA-DED+LPB specimens displayed a higher percentage of High Angle Grain Boundaries(HAGBs),which hindered dislocation movement and resulted in fewer crack initiation sites and less complex crack paths,thereby extending fatigue life.These findings underscore the effectiveness of LPB as a post-processing technique to enhance the fatigue performance of WA-DED-fabricated AZ31 Mg alloy components.Our study highlights the importance of LPB surface treatment on AZ31 Mg components produced by CMT-WA-DED to remove surface defects,enabling their widespread use in load-bearing applications.展开更多
With the development of technology for earthquake resistant,the research of the low yield point(LYP) steel which used for the fabrication of energy dissipation damper were paid more and more attention.The common studi...With the development of technology for earthquake resistant,the research of the low yield point(LYP) steel which used for the fabrication of energy dissipation damper were paid more and more attention.The common studies of the low yield point steel is mainly about the performance with constant amplitude and constant frequency.The low cycle fatigue properties of low yield piont steel were studied by series of test with continuous varying amplitude and varying frequency with the materials testing system by us.The test results showed that low yield point steel of Baosteel have excellent low cycle fatigue properties,which meet the requirement for steel used for the fabrication of energy dissipation damper completely.The low cycle fatigue performance of low yield point steel of Baosteel mainly depended on the amplitude in test.And the effect of varying frequency for the low yield point steel was more less than varying amplitude.展开更多
The influence of hydrogen embrittlement on the fatigue behaviors of AISI 304 stainless steel is investigated. The fatigue endurance limits of the untreated and hydrogen-embrittled materials were almost the same at 400...The influence of hydrogen embrittlement on the fatigue behaviors of AISI 304 stainless steel is investigated. The fatigue endurance limits of the untreated and hydrogen-embrittled materials were almost the same at 400 MPa, and hydrogen embrittlement had little influence even though the sample contained about 8.1 times more hydrogen. Thus, the sensitivity of hydrogen gas in this material is very low. A surface crack initiation, growth, coalescence, and micro ridge model is proposed in this study. Slip line formation?⇒microcrack formation?⇒increases in the crack width, and blunting of the crack tip as it grows?⇒formation of many slip lines because of deformation in the shear direction?⇒growth of the crack in the shear direction, forming micro ridges, coalescence with adjacent cracks ⇒?continuous initiation, growth, coalescence, and ridge formation of surface cracks and specimen breakage.展开更多
The low cycle fatigue (LCF) behavior of a high-strength structural steel was investigated in the strain rate range of 4×10^-6 -0.12 s^-1 (0. 001-3 Hz) under constant total strain (±1%) control. The cyc...The low cycle fatigue (LCF) behavior of a high-strength structural steel was investigated in the strain rate range of 4×10^-6 -0.12 s^-1 (0. 001-3 Hz) under constant total strain (±1%) control. The cyclic stress response at all strain rates exhibited behavior of rapid softening in the early stage of fatigue life and subsequent saturation up to failure. It was found that the stress amplitude, the plastic strain amplitude, the plastic strain energy density and the fatigue life depend mainly on the strain rate. The strain rate of 0. 012 s-1 was found as a transition point where the LCF of the steel showed different behavior from low strain rate to high strain rate. The relationship between the time to failure and strain rate was expressed well by a power law relation. The fracture surfaces of the fatigue sam-ples were characterized by using a scanning electron microscope (SEM) and the fracture mechanisms were discussed in terms of time-dependent deformation of the steel.展开更多
Fatigue induced products generally bear fatigue loads accompanied by impact processes,which reduces their reliable life rapidly. This paper introduces a reliability assessment model based on a local stress–strain app...Fatigue induced products generally bear fatigue loads accompanied by impact processes,which reduces their reliable life rapidly. This paper introduces a reliability assessment model based on a local stress–strain approach considering both low-cycle fatigue and high energy impact loads.Two coupling relationships between fatigue and impact are given with effects of an impact process on fatigue damage and effects of fatigue damage on impact performance. The analysis of the former modifies the fatigue parameters and the Manson–Coffin equation for fatigue life based on material theories. On the other hand, the latter proposes the coupling variables and the difference of fracture toughness caused by accumulative fatigue damage. To form an overall reliability model including both fatigue failure and impact failure, a competing risk model is developed. A case study of an actuator cylinder is given to validate this method.展开更多
基金the National Basic Research Program of China(No.2013CB632205).
文摘Low cycle fatigue behavior of extruded AZ80 magnesium alloy was investigated under uniaxial tension-compression at different strain amplitudes and strain rates.The results show that the extruded AZ80 magnesium alloy exhibits cyclic hardening at strain amplitudes ranging from 0.4%to 1.0%,the asymmetry of hysteresis loops becomes increasingly obvious when the strain amplitude increases.Higher strain rates correspond to higher stress amplitudes,high mean stresses and short fatigue life.{10–12}extension twins play a role in the cyclic deformation under higher strain amplitudes(0.8%,1.0%).The relationship between total strain energy density and fatigue life can be described by the modified Morrow model.The effect of strain rate on the fatigue life can also be predicted by the model.
文摘Studies were made of the symmetric tensile-compressive low cycle fatigue behaviour and the influence of dynamic strain aging(DSA)pre-treatment of 18-8 austenitic stainless steel. Within the testing amplitude range of strain.±0.5 % to±1.5 %,the three processes of cyclic hardening,cyclic saturation and cyclic softening were observed.In the same amplitude of strain,the peak stress of the samples pre-treated by DSA is higher than that of solid-solu- tion and cold working pre-treatment,but no remarkable differences of the fatigue lives of them were found.TEM observation shows that the uniform and stable dislocation networks with high density form after DSA pre-treatment,which increases the cyclic peak stress.The cyclic softening results from the low dislocation density and elongated cell structure with low energy.
基金the National Key Basic Research and Development Program of China under grant No.2004CB619104.
文摘The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime up to 107 cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AtSI 4340 steel in which the inclusion size is smaller than 5.5 μm, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 μm, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 pro. In the case of internal inclusion-induced fractures at cycles beyond about 1×10^6 for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure Nf in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with Nf, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1×10^6. Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.
基金supported by AREVA(France)the National Natural Science Foundation of China(51101107)
文摘Carbon-manganese steel is often applied in components of pipes in nuclear plant. Ultrasonic fatigue tests following low cycle fatigue (LCF) cycles damaged are used to study the strength of very high cycle fatigure (VHCF). The comparison of test results of simple VHCF and cumulative fatigue (LCF plus VHCF) shows that LCF load influences the following VHCF strength. Continuum damage mechanics model is extended to VHCF region.
文摘The low cycle fatigue (LCF) behavior of two high strength steels, withnominal chemical compositions (mass fraction, %) of 0.40C-1.5Cr-3Ni-0.4Mo-0.2V (PCrNi3MoV) and0.25C-3Cr-3Mo-0.8Ni-0.1Nb (25Cr3Mo3NiNb), was investigated by using the smooth bar specimenssubjected to strained-controlled push-pull loading. It is found that both steels show cyclicsoftening, but 25Cr3Mo3NiNb steel has a lower tendency to cyclic softening. 25Cr3Mo3NiNb steel hashigher fatigue ductility, and its transition fatigue life is almost three times that of PCrNi3MoV.25Cr3Mo3NiNb steel also shows higher LCF life either at a given total strain amplitude above 0.5% orat any given plastic strain amplitude, despite its lower monotonic tensile strength than that ofPCrNi3MoV. It also means that 25Cr3Mo3NiNb steel can endure higher total strain amplitude andplastic strain amplitude at a given number of reversals to failure within 10~4. 25Cr3Mo3NiNb steelis expected to be a good gun steel with high LCF properties because only several thousand firingsare required for gun barrel in most cases.
基金Funded by National Natural Science Foundation of China(No.51474170)the Key Laboratory Project of Shaanxi Provincial Department of Education(No.20js075)。
文摘The ultra-fine grained(UFG)pure titanium was prepared by equal channel angular pressing(ECAP)and rotary swaging(RS).The strain controlled low cycle fatigue(LCF)test was carried out at room temperature.The fatigue life prediction model and mean stress relaxation model under asymmetrical stress load were discussed.The results show that the strain ratio has a significant effect on the low cycle fatigue performance of the UFG pure titanium,and the traditional Manson-coffin model can not accurately predict the fatigue life under asymmetric stress load.Therefore,the SWT mean stress correction model and three-parameter power curve model are proposed,and the test results are verified.The final research shows that the threeparameter power surface model has better representation.By studying the mean stress relaxation phenomenon under the condition of R≠-1,it is revealed that the stress ratio and the strain amplitude are the factors that significantly afiect the mean stress relaxation rate,and the mean stress relaxation model with the two variables is calculated to describe the mean stress relaxation phenomenon of the UFG pure titanium under different strain ratios.The fracture morphology of the samples was observed by SEM,and it was concluded that the final fracture zone of the fatigue fracture of the UFG pure titanium was a mixture of ductile fracture and quasi cleavage fracture.The toughness of the material increases with the increase of strain ratio at the same strain amplitude.
基金Project supported bythe Key Technologies Fifteen R &D Programme (2001BA311A07-2) 985-Automotive Engineering ofJilin University
文摘The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa ( 1% Ce) and 105.5 MPa (2 % Ce), respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.
文摘The cyclic stress-strain responses (CSSR), Neuber's rule (NR) and cyclic strain-life relation (CSLR) are treated as probabilistic curves in local stress and strain method of low cycle fatigue analysis. The randomness of loading and the theory of fatigue damage accumulation (TOFDA) are considered. The probabilistic analysis of local stress, local strain and fatigue life are constructed based on the first-order Taylor's series expansions. Through this method proposed fatigue reliability analysis can be accomplished.
基金supported by the Department of Science and Technology Government of India,grant number SP/YO2019/1287(G)supported by Fronius India Solutions&Skill Centre,Bengaluru and CRF NITK Surathkal.
文摘Cold Metal Transfer-Based Wire Arc Directed Energy Deposition(CMT-WA-DED)presents a promising avenue for the rapid fabrication of components crucial to automotive,shipbuilding,and aerospace industries.However,the susceptibility to fatigue of CMT-WA-DED-produced AZ31 Mg alloy components has impeded their widespread adoption for critical load-bearing applications.In this study,a comprehensive investigation into the fatigue behaviour of WA-DED-fabricated AZ31 Mg alloy has been carried out and compared to commercially available wrought AZ31 alloy.Our findings indicate that the as-deposited parts exhibit a lower fatigue life than wrought Mg alloy,primarily due to poor surface finish,tensile residual stress,porosity,and coarse grain microstructure inherent in the WA-DED process.Low Plasticity Burnishing(LPB)treatment is applied to mitigate these issues,which induce significant plastic deformation on the surface.This treatment resulted in a remarkable improvement of fatigue life by 42%,accompanied by a reduction in surface roughness,grain refinement and enhancement of compressive residual stress levels.Furthermore,during cyclic deformation,WA-DED specimens exhibited higher plasticity and dislocation density compared to both wrought and WA-DED+LPB specimens.A higher fraction of Low Angle Grain Boundaries(LAGBs)in WA-DED specimens contributed to multiple crack initiation sites and convoluted crack paths,ultimately leading to premature failure.In contrast,wrought and WA-DED+LPB specimens displayed a higher percentage of High Angle Grain Boundaries(HAGBs),which hindered dislocation movement and resulted in fewer crack initiation sites and less complex crack paths,thereby extending fatigue life.These findings underscore the effectiveness of LPB as a post-processing technique to enhance the fatigue performance of WA-DED-fabricated AZ31 Mg alloy components.Our study highlights the importance of LPB surface treatment on AZ31 Mg components produced by CMT-WA-DED to remove surface defects,enabling their widespread use in load-bearing applications.
文摘With the development of technology for earthquake resistant,the research of the low yield point(LYP) steel which used for the fabrication of energy dissipation damper were paid more and more attention.The common studies of the low yield point steel is mainly about the performance with constant amplitude and constant frequency.The low cycle fatigue properties of low yield piont steel were studied by series of test with continuous varying amplitude and varying frequency with the materials testing system by us.The test results showed that low yield point steel of Baosteel have excellent low cycle fatigue properties,which meet the requirement for steel used for the fabrication of energy dissipation damper completely.The low cycle fatigue performance of low yield point steel of Baosteel mainly depended on the amplitude in test.And the effect of varying frequency for the low yield point steel was more less than varying amplitude.
文摘The influence of hydrogen embrittlement on the fatigue behaviors of AISI 304 stainless steel is investigated. The fatigue endurance limits of the untreated and hydrogen-embrittled materials were almost the same at 400 MPa, and hydrogen embrittlement had little influence even though the sample contained about 8.1 times more hydrogen. Thus, the sensitivity of hydrogen gas in this material is very low. A surface crack initiation, growth, coalescence, and micro ridge model is proposed in this study. Slip line formation?⇒microcrack formation?⇒increases in the crack width, and blunting of the crack tip as it grows?⇒formation of many slip lines because of deformation in the shear direction?⇒growth of the crack in the shear direction, forming micro ridges, coalescence with adjacent cracks ⇒?continuous initiation, growth, coalescence, and ridge formation of surface cracks and specimen breakage.
基金Item Sponsored by National Natural Science Foundation of China ( 50978174 , 10925211 )
文摘The low cycle fatigue (LCF) behavior of a high-strength structural steel was investigated in the strain rate range of 4×10^-6 -0.12 s^-1 (0. 001-3 Hz) under constant total strain (±1%) control. The cyclic stress response at all strain rates exhibited behavior of rapid softening in the early stage of fatigue life and subsequent saturation up to failure. It was found that the stress amplitude, the plastic strain amplitude, the plastic strain energy density and the fatigue life depend mainly on the strain rate. The strain rate of 0. 012 s-1 was found as a transition point where the LCF of the steel showed different behavior from low strain rate to high strain rate. The relationship between the time to failure and strain rate was expressed well by a power law relation. The fracture surfaces of the fatigue sam-ples were characterized by using a scanning electron microscope (SEM) and the fracture mechanisms were discussed in terms of time-dependent deformation of the steel.
基金supported by the National Natural Science Foundation of China(No.61104132)
文摘Fatigue induced products generally bear fatigue loads accompanied by impact processes,which reduces their reliable life rapidly. This paper introduces a reliability assessment model based on a local stress–strain approach considering both low-cycle fatigue and high energy impact loads.Two coupling relationships between fatigue and impact are given with effects of an impact process on fatigue damage and effects of fatigue damage on impact performance. The analysis of the former modifies the fatigue parameters and the Manson–Coffin equation for fatigue life based on material theories. On the other hand, the latter proposes the coupling variables and the difference of fracture toughness caused by accumulative fatigue damage. To form an overall reliability model including both fatigue failure and impact failure, a competing risk model is developed. A case study of an actuator cylinder is given to validate this method.