Heat-treated wood has good dimensional stability,corrosion resistance and visual quality,but it is prone to mold,which limits its application.Based on the pH value of heat-treated wood,this study examines the factors ...Heat-treated wood has good dimensional stability,corrosion resistance and visual quality,but it is prone to mold,which limits its application.Based on the pH value of heat-treated wood,this study examines the factors affecting the pathogenesis causing heat-treated wood mold.Normally,the pH value of the heat-treated wood is between 4.38 and 5.10,which is suitable for the growth of mold.However,the pH of the heat-treated copper-containing material is between 6.63 and 7.12,which deviates the treated wood from the comfortable growth conditions for the mold,thereby reducing the occurrence of mold.展开更多
Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composite...Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composites were investigated at different temperatures (773-1173K), and the microstructures of carbon/carbon composites were studied by SEM and X-ray diffraction. The experimental results showed that the inter-laminar distance of (002) plane (d002) deceased while the microcrystalline stack height (Lc) increased. The oxidation rate of felt base carbon/carbon composites was invari-able at certain temperatures. The oxidation mechanism of carbon/carbon composites changed remarkably at the oxidation temperature 973K. At the initial oxidation stage of carbon/carbon composites, carbon matrix was oxidized much more rapidly than carbon felt.展开更多
Seeds of Dodonaea viscosa （L.） Jacq, a representative species in dry and hot valleys in Southwest China, were chosen as experimental materials. In this experiment, the D. viscosa seeds were treated at 40, 60, 80 and...Seeds of Dodonaea viscosa （L.） Jacq, a representative species in dry and hot valleys in Southwest China, were chosen as experimental materials. In this experiment, the D. viscosa seeds were treated at 40, 60, 80 and 100℃ respectively before germination to study impacts of high temperature treatment on their generation rate and to further discuss the roles of fire during the process of vegetation formation in dry and hot valley areas of China. The results show that when the temperature was higher than 40 ℃, the germination rate of D. viscosa seeds was significantly higher than that of the control group, and the heat shock effect was apparent. The germination rate was the highest when the seeds were treated at 80 ℃ for 10 min, reaching 63.00%±2.55%. There was still a significant heat shock effect on the D. viscosa seeds which were stored for one year. In comparison with the conventional method of soaking seeds in hot water, the germination rate of D. viscose seeds which were treated at high temperature before germination increased significantly.展开更多
Dry sliding wear tests of a Cr-Mo-V cast hot-forging die steel was carried out within a load range of 50--300 N at 400℃ by a pin-on-disc high temperature wear machine. The effect of heat treatment process on wear res...Dry sliding wear tests of a Cr-Mo-V cast hot-forging die steel was carried out within a load range of 50--300 N at 400℃ by a pin-on-disc high temperature wear machine. The effect of heat treatment process on wear resistance was systematically studied in order to select heat treatment processes of the steel with high wear resistance. The morphology, structure and composition were analyzed using scanning electron microscopy （SEM）, X-ray diffraction （XRD） and energy dispersive spectroscopy （EDS） ; wear mechanism was also discussed. Tribo-oxide layer was found to form on worn surfaces to reduce wear under low loads, but appear inside the matrix to increase wear under high loads. The tribo-oxides were mainly consisted of Fe3O4 and Fe2O3, FeO only appeared under a high load. Oxidative mild wear, transition of mild-severe wear in oxidative wear and extrusive wear took turns to operate with increasing the load. The wear resistance strongly depended on the selection of heat treatment processes or microstructures. It was found that bainite presented a better wear resistance than martensite plus bainite duplex structure, martensite structure was of the poorest wear resistance. The wear resistance increased with increasing austenizing temperature in the range of 920 to 1 120 ℃, then decreased at up to 1 220 ℃. As for tempering temperature and microstructure, the wear resistance increased in following order： 700℃ （tempered sorbite）, 200 ℃ （tempered martensite）, 440 to 650 ℃ （tempered troostite）. An appropriate combination of hardness, toughness, microstructural thermal stability was re- quired for a good wear resistance in high-temperature wear. The optimized heat treatment process was suggested for the cast hot-forging steel to be austenized at 1020 to 1 120 ℃, quenched in oil, then tempered at 440 to 650℃ for 2 h.展开更多
The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy,and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature ...The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy,and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature to 300℃.It turned out that the optimum T6 heat-treatments for the tested alloy are 525℃×12 h+225℃×14 h and 525℃×12 h+250℃×12 h which integrated age-hardening and tensile properties into account,respectively.The strength of the T6-treated alloy indicates obvious anomalous temperature dependence from room temperature to 300℃,namely both ultimate tensile strength and yield strength of the tested alloy firstly increase with tensile temperature,and then decrease as temperature increases further.Elongation increased with temperature monotonously.The tensile fracture mode of the tested alloy changes from transgranular fracture to intergranular fracture with the increasing of test temperature.展开更多
The article considers one of the possible approaches to the solution of an urgent issue of metal consumption reduction, increase of operating life and maximum operating temperature as well as reduction of irrecoverabl...The article considers one of the possible approaches to the solution of an urgent issue of metal consumption reduction, increase of operating life and maximum operating temperature as well as reduction of irrecoverable losses of platinum products and alloys when operating under high temperature conditions, particularly for glassblowing and single crystal growing crucibles. A two-layered composite material based on platinum-group metals and corundum plasma ceramics is thoroughly investigated. A successful experience of crucibles exploitation, designed for production of high temperature optical glasses from the composite and results of the research on composite material specimens are described.展开更多
Nano hafnium carbide（HfC） powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling trea...Nano hafnium carbide（HfC） powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling treatment on the phase and morphology of pyrolysis products（HfO_2-C） and final HfC product were investigated and the influences of heat treatment temperature and holding time on the structure and properties of the synthesized hafnium carbide powders were also studied. The experimental results showed that the HfO_2-C powders with good uniformity and small particle size were prepared by controlling the milling time. Pure HfC powders with an average particle size of 500 nm were obtained at 1 700 ℃ with a holding time of 3 min, and the oxygen content was about 0.69 wt%, lower than that of the hafnium carbide powders prepared by SPS（0.97%）.展开更多
基金Provincial Science and Technology Research Project of Guangdong(2014A040401043)
文摘Heat-treated wood has good dimensional stability,corrosion resistance and visual quality,but it is prone to mold,which limits its application.Based on the pH value of heat-treated wood,this study examines the factors affecting the pathogenesis causing heat-treated wood mold.Normally,the pH value of the heat-treated wood is between 4.38 and 5.10,which is suitable for the growth of mold.However,the pH of the heat-treated copper-containing material is between 6.63 and 7.12,which deviates the treated wood from the comfortable growth conditions for the mold,thereby reducing the occurrence of mold.
文摘Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composites were investigated at different temperatures (773-1173K), and the microstructures of carbon/carbon composites were studied by SEM and X-ray diffraction. The experimental results showed that the inter-laminar distance of (002) plane (d002) deceased while the microcrystalline stack height (Lc) increased. The oxidation rate of felt base carbon/carbon composites was invari-able at certain temperatures. The oxidation mechanism of carbon/carbon composites changed remarkably at the oxidation temperature 973K. At the initial oxidation stage of carbon/carbon composites, carbon matrix was oxidized much more rapidly than carbon felt.
基金Supported by the National Water Pollution Control and Treatment Science and Technology Major Project(2012ZX07101-003-04-04)~~
文摘Seeds of Dodonaea viscosa （L.） Jacq, a representative species in dry and hot valleys in Southwest China, were chosen as experimental materials. In this experiment, the D. viscosa seeds were treated at 40, 60, 80 and 100℃ respectively before germination to study impacts of high temperature treatment on their generation rate and to further discuss the roles of fire during the process of vegetation formation in dry and hot valley areas of China. The results show that when the temperature was higher than 40 ℃, the germination rate of D. viscosa seeds was significantly higher than that of the control group, and the heat shock effect was apparent. The germination rate was the highest when the seeds were treated at 80 ℃ for 10 min, reaching 63.00%±2.55%. There was still a significant heat shock effect on the D. viscosa seeds which were stored for one year. In comparison with the conventional method of soaking seeds in hot water, the germination rate of D. viscose seeds which were treated at high temperature before germination increased significantly.
基金Item Sponsored by National Nature Science Foundation of China(51071078)
文摘Dry sliding wear tests of a Cr-Mo-V cast hot-forging die steel was carried out within a load range of 50--300 N at 400℃ by a pin-on-disc high temperature wear machine. The effect of heat treatment process on wear resistance was systematically studied in order to select heat treatment processes of the steel with high wear resistance. The morphology, structure and composition were analyzed using scanning electron microscopy （SEM）, X-ray diffraction （XRD） and energy dispersive spectroscopy （EDS） ; wear mechanism was also discussed. Tribo-oxide layer was found to form on worn surfaces to reduce wear under low loads, but appear inside the matrix to increase wear under high loads. The tribo-oxides were mainly consisted of Fe3O4 and Fe2O3, FeO only appeared under a high load. Oxidative mild wear, transition of mild-severe wear in oxidative wear and extrusive wear took turns to operate with increasing the load. The wear resistance strongly depended on the selection of heat treatment processes or microstructures. It was found that bainite presented a better wear resistance than martensite plus bainite duplex structure, martensite structure was of the poorest wear resistance. The wear resistance increased with increasing austenizing temperature in the range of 920 to 1 120 ℃, then decreased at up to 1 220 ℃. As for tempering temperature and microstructure, the wear resistance increased in following order： 700℃ （tempered sorbite）, 200 ℃ （tempered martensite）, 440 to 650 ℃ （tempered troostite）. An appropriate combination of hardness, toughness, microstructural thermal stability was re- quired for a good wear resistance in high-temperature wear. The optimized heat treatment process was suggested for the cast hot-forging steel to be austenized at 1020 to 1 120 ℃, quenched in oil, then tempered at 440 to 650℃ for 2 h.
基金This work is supported by National Natural Science Foundation of China(Nos.51771115 and 51775334)National Science and Technology Major Project(2017ZX04006001)+1 种基金Joint Fund for Space Science and Technology(6141B06300401 and 6141B06310106)Science Innovation Foundation of Shanghai Academy of Spaceflight Technology(No.SAST2016048).
文摘The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy,and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature to 300℃.It turned out that the optimum T6 heat-treatments for the tested alloy are 525℃×12 h+225℃×14 h and 525℃×12 h+250℃×12 h which integrated age-hardening and tensile properties into account,respectively.The strength of the T6-treated alloy indicates obvious anomalous temperature dependence from room temperature to 300℃,namely both ultimate tensile strength and yield strength of the tested alloy firstly increase with tensile temperature,and then decrease as temperature increases further.Elongation increased with temperature monotonously.The tensile fracture mode of the tested alloy changes from transgranular fracture to intergranular fracture with the increasing of test temperature.
文摘The article considers one of the possible approaches to the solution of an urgent issue of metal consumption reduction, increase of operating life and maximum operating temperature as well as reduction of irrecoverable losses of platinum products and alloys when operating under high temperature conditions, particularly for glassblowing and single crystal growing crucibles. A two-layered composite material based on platinum-group metals and corundum plasma ceramics is thoroughly investigated. A successful experience of crucibles exploitation, designed for production of high temperature optical glasses from the composite and results of the research on composite material specimens are described.
基金the National Key R&D Program of China(2017YFB0310400)the National Natural Science Foundation of China(51672197)
文摘Nano hafnium carbide（HfC） powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling treatment on the phase and morphology of pyrolysis products（HfO_2-C） and final HfC product were investigated and the influences of heat treatment temperature and holding time on the structure and properties of the synthesized hafnium carbide powders were also studied. The experimental results showed that the HfO_2-C powders with good uniformity and small particle size were prepared by controlling the milling time. Pure HfC powders with an average particle size of 500 nm were obtained at 1 700 ℃ with a holding time of 3 min, and the oxygen content was about 0.69 wt%, lower than that of the hafnium carbide powders prepared by SPS（0.97%）.