A study on the melting and viscosity properties of the chromium-containing high-titanium melting slag(CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3) with TiO2 contents ranging from 38.63 wt% to 42.63 wt% was conducted. The melti...A study on the melting and viscosity properties of the chromium-containing high-titanium melting slag(CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3) with TiO2 contents ranging from 38.63 wt% to 42.63 wt% was conducted. The melting properties were investigated with a meltingpoint apparatus, and viscosity was measured using the rotating cylinder method. The FactSage 7.1 software and X-ray diffraction, in combination with scanning electron microscopy–energy-dispersive spectroscopy(SEM–EDS), were used to characterize the phase equilibrium and microstructure of chromium-containing high-titanium melting slags. The results indicated that an increase in the TiO2 content led to a decrease in the viscosity of the chromium-containing high-titanium melting slag. In addition, the softening temperature, hemispheric temperature, and flowing temperature decreased with increasing TiO2 content. The amount of crystallized anosovite and sphene phases gradually increased with increasing TiO2 content, whereas the amount of perovskite phase decreased. SEM observations revealed that the distribution of the anosovite phase was dominantly influenced by TiO2.展开更多
In order to clarify the slag system of high Cr2O3 vanadium-titanium magnetite smelting in BF （blast furnace）, the melting properties of slag samples prepared by analytically pure reagents were measured. By means of ...In order to clarify the slag system of high Cr2O3 vanadium-titanium magnetite smelting in BF （blast furnace）, the melting properties of slag samples prepared by analytically pure reagents were measured. By means of orthogonal test synthetic weighted score method, the optimal slag for high Cr2O3 vanadium-titanium magnetite was obtained, which contained 10% MgO, 8% TiO2 and 15% Al2O3, with the binary basicity being 1.15. In addition, the effects of basicity, MgO, TiO2 and A12 03 on slag melting properties were investigated by single factor test, and the results showed that, with increasing the basicity or TiO2 content, melting temperature （Tin） increased, whereas initial vis- cosity （r/0） and high temperature viscosity （r/h） decreased. With increasing the MgO content, Tm decreased firstly and then increased. With increasing the Al2 O3 content, Tm increased, and η0 and r/h decreased firstly and then increased.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51904066)the Fundamental Research Funds for the Central Universities,China(No.N182503032)+1 种基金the Postdoctoral Foundation of Northeastern University,China(No.20190201)the Postdoctoral International Exchange Program,China(Dispatch Project,20190075)
文摘A study on the melting and viscosity properties of the chromium-containing high-titanium melting slag(CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3) with TiO2 contents ranging from 38.63 wt% to 42.63 wt% was conducted. The melting properties were investigated with a meltingpoint apparatus, and viscosity was measured using the rotating cylinder method. The FactSage 7.1 software and X-ray diffraction, in combination with scanning electron microscopy–energy-dispersive spectroscopy(SEM–EDS), were used to characterize the phase equilibrium and microstructure of chromium-containing high-titanium melting slags. The results indicated that an increase in the TiO2 content led to a decrease in the viscosity of the chromium-containing high-titanium melting slag. In addition, the softening temperature, hemispheric temperature, and flowing temperature decreased with increasing TiO2 content. The amount of crystallized anosovite and sphene phases gradually increased with increasing TiO2 content, whereas the amount of perovskite phase decreased. SEM observations revealed that the distribution of the anosovite phase was dominantly influenced by TiO2.
基金Item Sponsored by National Natural Science Foundation of China(51090384)National High Technology Research and Development Program(863 Program)of China(2012AA062302,2012AA062304)Fundamental Research Funds for the Central Universities of China(N110202001)
文摘In order to clarify the slag system of high Cr2O3 vanadium-titanium magnetite smelting in BF （blast furnace）, the melting properties of slag samples prepared by analytically pure reagents were measured. By means of orthogonal test synthetic weighted score method, the optimal slag for high Cr2O3 vanadium-titanium magnetite was obtained, which contained 10% MgO, 8% TiO2 and 15% Al2O3, with the binary basicity being 1.15. In addition, the effects of basicity, MgO, TiO2 and A12 03 on slag melting properties were investigated by single factor test, and the results showed that, with increasing the basicity or TiO2 content, melting temperature （Tin） increased, whereas initial vis- cosity （r/0） and high temperature viscosity （r/h） decreased. With increasing the MgO content, Tm decreased firstly and then increased. With increasing the Al2 O3 content, Tm increased, and η0 and r/h decreased firstly and then increased.