This paper addresses the effects of stress ratio on the temperature-dependent high-cycle fatigue (HCF) properties of alloy steels 2CrMo and 9CrCo, which suffer from substantial vibrational loading at small stress am...This paper addresses the effects of stress ratio on the temperature-dependent high-cycle fatigue (HCF) properties of alloy steels 2CrMo and 9CrCo, which suffer from substantial vibrational loading at small stress amplitude, high stress ratio, and high frequency in the high-temperature environments in which they fimcfion as blade and rotor spindle materials in advanced gas or steam turbine engines. Fatigue tests were performed on alloy steels 2CrMo and 9CrCo subjected to constant-amplitude loading at four stress ratios and at four and three temperatures, respectively, to determine their temperature-dependent HCF properties. The interaction mechanisms between high temperature and stress ratio were deduced and compared with each other on the basis of the results of fractographic analysis. A phenomenological model was developed to evaluate the effects of stress ratio on the temperature-dependent HCF properties of alloy steels 2CrMo and 9CrCo. Good correlation was achieved between the predictions and actual experiments, demonstrating the practical and effective use of the proposed method.展开更多
Based on the investigation of the tensile properties of spray formed ultra-high strength Al10.8Zn2.9Mg1.9Cu alloys, the high-cycle fatigue properties under different theoretical stress concentration factors were inves...Based on the investigation of the tensile properties of spray formed ultra-high strength Al10.8Zn2.9Mg1.9Cu alloys, the high-cycle fatigue properties under different theoretical stress concentration factors were investigated, the fatigue fracture surfaces and microstructures were observed, and the fatigue mechanism was discussed. The results indicate that the ultimate tensile strength of spray formed Al10.8Zn2.9Mg1.9Cu alloys can reach up to 730?740 MPa, and the elongation is about 8%?10% under the condition of two-stage aging treatment. For the stress ratio is 0.1, the maximum stress for 107 cycles is over 400 MPa and 120 MPa, when the theoretical stress concentration factor is 1 and 3, respectively.展开更多
The increase in payload capacity of trucks has heightened the demand for cost-effective yet high performance brake discs.In this work,the thermal fatigue and wear of compacted graphite iron brake discs were investigat...The increase in payload capacity of trucks has heightened the demand for cost-effective yet high performance brake discs.In this work,the thermal fatigue and wear of compacted graphite iron brake discs were investigated,aiming to provide an experimental foundation for achieving a balance between their thermal and mechanical properties.Compacted graphite iron brake discs with different tensile strengths,macrohardnesses,specific heat capacities and thermal diffusion coefficients were produced by changing the proportion and strength of ferrite.The peak temperature,pressure load and friction coefficient of compacted graphite iron brake discs were analyzed through inertia friction tests.The morphology of thermal cracks and 3D profiles of the worn surfaces were also discussed.It is found that the thermal fatigue of compacted graphite iron discs is determined by their thermal properties.A compacted graphite iron with the highest specific heat capacity and thermal diffusion coefficient exhibits optimal thermal fatigue resistance.Oxidization of the matrix at low temperatures significantly weakens the function of alloy strengthening in hindering the propagation of thermal cracks.Despite the reduced hardness,increasing the ferrite proportion can mitigate wear loss resulting from low disc temperatures and the absence of abrasive wear.展开更多
In order to study the anti-fatigue performance of RCA modified asphalt (RMA),the performance of RMA and 90#matrix asphalt with different modifier content were measured by asphalt penetration,ductility,softening point,...In order to study the anti-fatigue performance of RCA modified asphalt (RMA),the performance of RMA and 90#matrix asphalt with different modifier content were measured by asphalt penetration,ductility,softening point,Brookfield viscosity,rheological index,infrared spectrum and dielectric constant test.This paper discusses the changes of asphalt basic indexes,fatigue properties and asphalt components based on dielectric properties under different modifier contents,and analyzes the grey correlation degree between components and asphalt pavement performance indexes.The results show that the optimum content of RCA modifier is 16.7%of the asphalt quality according to the penetration,ductility,softening point,Brockfield viscosity,viscosity temperature curve and fatigue life.In the phase angle-strain curve,there is disorder in the latter part of the curve.According to the strain (ε_(d)) corresponding to the disorder point,a new fatigue failure criterion is proposed and proved.Based on the new asphalt fatigue failure criterion,the fatigue prediction model of asphalt mixture is improved,and the fatigue life predicted by the improved fatigue model is compared with the fatigue life obtained by four-point bending fatigue test.The results show that the proposed new asphalt fatigue failure criterion is reasonable,and the fatigue life predicted by the improved asphalt mixture fatigue prediction model is accurate.The research method of classifying asphalt components based on dielectric properties is simple and effective,and the components have a high correlation with the road performance of base asphalt and modified asphalt.展开更多
The addition of nanoscale additions to magnesium(Mg)based alloys can boost mechanical characteristics without noticeably decreasing ductility.Since Mg is the lightest structural material,the Mg-based nanocomposites(NC...The addition of nanoscale additions to magnesium(Mg)based alloys can boost mechanical characteristics without noticeably decreasing ductility.Since Mg is the lightest structural material,the Mg-based nanocomposites(NCs)with improved mechanical properties are appealing materials for lightweight structural applications.In contrast to conventional Mg-based composites,the incorporation of nano-sized reinforcing particles noticeably boosts the strength of Mg-based nanocomposites without significantly reducing the formability.The present article reviews Mg-based metal matrix nanocomposites(MMNCs)with metallic and ceramic additions,fabricated via both solid-based(sintering and powder metallurgy)and liquid-based(disintegrated melt deposition)technologies.It also reviews strengthening models and mechanisms that have been proposed to explain the improved mechanical characteristics of Mg-based alloys and nanocomposites.Further,synergistic strengthening mecha-nisms in Mg matrix nanocomposites and the dominant equations for quantitatively predicting mechanical properties are provided.Furthermore,this study offers an overview of the creep and fatigue behavior of Mg-based alloys and nanocomposites using both traditional(uniaxial)and depth-sensing indentation techniques.The potential applications of magnesium-based alloys and nanocomposites are also surveyed.展开更多
Mg-Al-Zn-Ca-Y alloys with excellent ignition and corrosion resistances—termed SEN alloys(where the letters"S,""E,"and"N"stand for stainless,environmentally friendly,and non-flammable,res...Mg-Al-Zn-Ca-Y alloys with excellent ignition and corrosion resistances—termed SEN alloys(where the letters"S,""E,"and"N"stand for stainless,environmentally friendly,and non-flammable,respectively)—have been developed recently.In this study,the microstructure,tensile properties,and high-cycle fatigue properties of an extruded Mg-9.0Al-0.8Zn-0.1Mn-0.3Ca-0.2Y(SEN9)alloy are investigated and compared with those of a commercial Mg-9.0Al-0.8Zn-0.1Mn(AZ91)alloy extruded under the same conditions.Both the extruded SEN9 alloy and the extruded AZ91 alloy have a fully recrystallized structure comprising equiaxed grains,but the former has a smaller average grain size owing to the promoted dynamic recrystallization during extrusion.The extruded AZ91 alloy contains coarse Mg_(17)Al_(12) discontinuous precipitate(DP)bands parallel to the extrusion direction,which are formed during its cool down after extrusion.In contrast,the extruded SEN9 alloy contains relatively fine undissolved Al_(2)Ca,Al_(8)Mn_(4)Y,and Al_(2)Y second-phase particles,which are formed during the solidification stage of the casting process.The tensile strength of the extruded SEN9 alloy,which has finer grains and more abundant particles,is slightly higher than that of the extruded AZ91 alloy.However,the difference in their strengths is relatively small because the stronger solid-solution hardening and precipitation hardening effects in the extruded AZ91alloy offset the stronger grain-boundary hardening and dispersion hardening effects in the extruded SEN9alloy to some extent.The tensile elongation of the extruded AZ91 alloy is significantly lower than that of the extruded SEN9 alloy because the large cracks formed in the DP bands in the former cause its premature fracture.Although the extruded SEN9 alloy has higher tensile properties than the extruded AZ91alloy,the high-cycle fatigue life and fatigue strength of the former are shorter and lower,respectively,than those of the latter.The DP bands in the extruded AZ91 alloy do not act as fatigue crack initiation sites,and therefore,fatigue cracks initiate on the specimen surface at all stress amplitude levels.In contrast,in most of the fatigue-fractured specimens of the extruded SEN9 alloy,fatigue cracks initiate on the undissolved Al_(2)Ca and Al_(2)Y particles present on the surface or subsurface of the specimens because of the high local stress concentration on the particles during cyclic loading.This particle-initiated fatigue fracture eventually decreases the high-cycle fatigue resistance of the extruded SEN9 alloy.展开更多
The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and f...The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa ( 1% Ce) and 105.5 MPa (2 % Ce), respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.展开更多
High-temperature mechanical properties of high-boron austenitic steels(HBASs) were studied at 850 °C using a dynamic thermal-mechanical simulation testing machine. In addition, the thermal fatigue properties of t...High-temperature mechanical properties of high-boron austenitic steels(HBASs) were studied at 850 °C using a dynamic thermal-mechanical simulation testing machine. In addition, the thermal fatigue properties of the alloys were investigated using the self-restraint Uddeholm thermal fatigue test, during which the alloy specimens were cycled between room temperature and 800°C. Stereomicroscopy and scanning electron microscopy were used to study the surface cracks and cross-sectional microstructure of the alloy specimens after the thermal fatigue tests. The effects of carbon content on the mechanical properties at room temperature and high-temperature as well as thermal fatigue properties of the HBASs were also studied. The experimental results show that increasing carbon content induces changes in the microstructure and mechanical properties of the HBASs. The boride phase within the HBAS matrix exhibits a round and smooth morphology, and they are distributed in a discrete manner. The hardness of the alloys increases from 239(0.19 wt.% C) to 302(0.29 wt.% C) and 312 HV(0.37 wt.% C); the tensile yield strength at 850 °C increases from 165.1 to 190.3 and 197.1 MPa; and the compressive yield strength increases from 166.1 to 167.9 and 184.4 MPa. The results of the thermal fatigue tests(performed for 300 cycles from room temperature to 800 °C) indicate that the degree of thermal fatigue of the HBAS with 0.29 wt.% C(rating of 2–3) is superior to those of the alloys with 0.19 wt.%(rating of 4–5) and 0.37 wt.%(rating of 3–4) carbon. The main cause of this difference is the ready precipitation of M23(C,B)6-type borocarbides in the alloys with high carbon content during thermal fatigue testing. The precipitation and aggregation of borocarbide particles at the grain boundaries result in the deterioration of the thermal fatigue properties of the alloys.展开更多
The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the hi...The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime up to 107 cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AtSI 4340 steel in which the inclusion size is smaller than 5.5 μm, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 μm, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 pro. In the case of internal inclusion-induced fractures at cycles beyond about 1×10^6 for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure Nf in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with Nf, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1×10^6. Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.展开更多
In this study,the tensile and high-cycle fatigue properties of as-cast,solid solution treated and as-extruded Mg-8Li-3Al-2Zn-0.5Y alloy are investigated.The results show that the yield strength and ultimate tensile st...In this study,the tensile and high-cycle fatigue properties of as-cast,solid solution treated and as-extruded Mg-8Li-3Al-2Zn-0.5Y alloy are investigated.The results show that the yield strength and ultimate tensile strength of as-cast alloy is 198.1 MPa and 222.5 MPa,which are improved to 274.7 MPa and 321.7 MPa,282.4 MPa and 319.3 MPa after solid solution and extrusion treatment,respectively.The high-cycle fatigue strength(at 10^(7)cycles,R=-1)of as-cast studied alloy is 65 MPa,which is improved to 90 MPa and 105 MPa after solid solution and extrusion treatment,respectively.The improvement of fatigue property of the solid solution treated alloy is mainly due to the lattice distortion caused by solid solution hindering the crack propagation.However,the improvement of fatigue property of the as-extruded alloy is mainly due to that the refined grains,stacked dislocations and dispersed secondary particles impede the crack propagation.展开更多
The fatigue properties of asphalts were investigated after various laboratory simulation ageing tests and outdoor natural exposure ultraviolet radiation ageing,by dynamic shear rheometer(DSR) time sweep fatigue test i...The fatigue properties of asphalts were investigated after various laboratory simulation ageing tests and outdoor natural exposure ultraviolet radiation ageing,by dynamic shear rheometer(DSR) time sweep fatigue test in constant strain model and a new type of specimen which was introduced to avoid the problem of adhesion failure between rotor and asphalt binder.The results show that outdoor natural exposure ageing(NEA) causes the decrease of retained fatigue life distinctly,and photodegradation caused by outdoor NEA of 1 250 μm thin films asphalt for three months,is found to be severer than pressure ageing vessel(PAV) with respects to retained fatigue life.The effect of photodegradation increases as the time of outdoor NEA increases.DSR time sweep fatigue test in constant strain indicates that the aged styrene-butadiene-styrene(SBS) modified asphalt still displays better fatigue properties than the corresponding base asphalt after ageing.展开更多
The microstructure,strength,toughness and fatigue properties of an ultra-high strength steel 40CrMnSiMoVA have been investigated.The so-called meta-bainite,composed of thin re- tained austenite films within or between...The microstructure,strength,toughness and fatigue properties of an ultra-high strength steel 40CrMnSiMoVA have been investigated.The so-called meta-bainite,composed of thin re- tained austenite films within or between the bainitic ferrite lathes was found in the steel after isothermally quenched at 300℃ for 1h.In comparison with the martensite structure obtained by isothermally quenching in martensite range,the meta-bainite has more excellent strength and plasticity,lower notch sensitivity,stronger strain harden ability,higher fatigue strength, longer strain or impact fatigue life,slower crack propagation rate and more remarkable overload effect on increasing fatigue life.展开更多
In this paper, a two dimensional Voronoi cell element, formulated with creep, thermal and plastic strain, is applied for the numerical simulation of thermo-mechanical fatigue behavior for particulate reinforced compos...In this paper, a two dimensional Voronoi cell element, formulated with creep, thermal and plastic strain, is applied for the numerical simulation of thermo-mechanical fatigue behavior for particulate reinforced composites. The relation between mechanical fatigue phases and thermal fatigue phases influences the thermo-mechanical fatigue behavior and cyclic creep damage. The topological features of micro-structure in particulate reinforced composites, such as the orientation, depth-width ratio, distribution and volume fraction of inclusions, have a great influence on thermo-mechanical behavior. Some related conclusions are obtained by examples of numerical simulation.展开更多
The fatigue properties of friction stir welded (FSW) butt joint and base metal of MB8 magnesium alloy were investigated. The comparative fatigue tests were carried out using EHF-EM2OOK2-070-IA fatigue testing machin...The fatigue properties of friction stir welded (FSW) butt joint and base metal of MB8 magnesium alloy were investigated. The comparative fatigue tests were carried out using EHF-EM2OOK2-070-IA fatigue testing machine for both FSW butt joint and base metal specimens. The fatigue fractures were observed and analyzed using a scanning electron microscope of JSM-6063LA type. The experimental results show that the fatigue performance of the FSW butt joint of MB8 magnesium alloy is sharply decreased. The conditional fatigue limit (2 x 106) of base metal and welded butt joint is about 77.44 MPa and 49. 91 MPa, respectively. The conditional fatigue limit (2 x 106 ) of the welded butt joint is 64.45% of that of base metal. The main reasons are that the welding can lead to stress concentration in the flash area, tensile welding residual stress in the welded joint( The residual stress value was 30. 5 MPa), as well as the grain size is not uniform in the heat-affected zone. The cleavage steps or quasi-cleavage patterns present on the fatigue fracture surface, the fracture type of the FSW butt joint belongs to a brittle fracture.展开更多
Fracture evolution process (initiation, propagation and coalescence) of cracked rock was observed and the force- displacement curves of cracked rock were measured under uniaxial cyclic loading. The tested specimens ma...Fracture evolution process (initiation, propagation and coalescence) of cracked rock was observed and the force- displacement curves of cracked rock were measured under uniaxial cyclic loading. The tested specimens made of sandstone-like modeling material contained three pre-existing intermittent cracks with different geometrical distributions. The experimental results indicate that the fatigue deformation limit corresponding to the maximal cyclic load is equal to that of post-peak locus of static complete force?displacement curve; the fatigue deformation process can be divided into three stages: initial deformation, constant deformation rate and accelerative deformation; the time of fracture initiation, propagation and coalescence corresponds to the change of irreversible deformation.展开更多
Properties and mechanism were investigated on flexural fatigue of concrete containing polypropylene fibers and ground granulated blast furnace slag(GGBFS).Four polypropylene fibers’volume fractions and five slag pr...Properties and mechanism were investigated on flexural fatigue of concrete containing polypropylene fibers and ground granulated blast furnace slag(GGBFS).Four polypropylene fibers’volume fractions and five slag proportions were considered.An experiment was conducted to obtain the fatigue lives at three stress levels in 20 Hz frequency and at a constant stress level of 0.59 in four frequency respectively.Mechanism and evaluation were investigated based on the experimental data.Fatigue life span models were established.The results show that the addition of polypropylene fibers improves the flexural fatigue cumulative strength and fatigue life span.It is proposed that the slag particles and hydrated products improve Interfacial Transition Zone(ITZ)structure and benefit flexural fatigue performance.A composite reinforce effect is found with the incorporation of slag and polypropylene fibers.The optimum mixture contents 55%slag with 0.6%polypropylene fiber for the cumulative fatigue stress.Fatigue properties are decreased as the stress level increasing,the higher frequency reduces the fatigue strength more than lower frequency at a constant stress level.展开更多
The transport properties and fatigue effect of Ag/Bi0.9La0.lFeO3/La0.7Sr0.3MnO3 heterostructures are described. By examining the I-V curves, an anomalous fatigue effect was found and its influences on resistive states...The transport properties and fatigue effect of Ag/Bi0.9La0.lFeO3/La0.7Sr0.3MnO3 heterostructures are described. By examining the I-V curves, an anomalous fatigue effect was found and its influences on resistive states were studied. I-V curves combined with C-f spectra were used to directly analyze the transport properties and fatigue effect. Compared to the first I-V cycle state, this structure shows more than one order increase of resistance after 100 cycles of "I-V curve training". The redistribution of oxygen vacancies in the depletion layer of Ag/Bi0.9La0.lFeO3 is believed to be responsible for the different resistance mechanisms and tenfold magnitude drop in resistance. The resistive switching is understood to be caused by electric field-induced carrier trapping and detrapping, which changes the depletion layer thickness at the Ag/Bi0.9La0.lFeO3 interface.展开更多
The fatigue properties of 400 MPa grade supersteel, plain low carbon steel SS400 and microalloyed steel Q340TM were investigated through tensile-compression fatigue experiment with R =- 1. The results indicate that th...The fatigue properties of 400 MPa grade supersteel, plain low carbon steel SS400 and microalloyed steel Q340TM were investigated through tensile-compression fatigue experiment with R =- 1. The results indicate that the fatigue limit of the 400 MPa supersteel is higher than that of SS400 steel and close to that of the 340TM steel. According to the analysis of fatigue fracture, the fatigue striations of supersteel SS400 is thinner than that of SS400 steel and 340TM steel, and grain refinement can increase the fatigue limit.展开更多
High-cycle rotating bending fatigue behavior of SRR99 nickel-base single crystal alloy at 700 and 900℃ was investigated. The fatigue strengths for 107 cycles are 350 and 335MPa at 700 and 900℃, respectively. T...High-cycle rotating bending fatigue behavior of SRR99 nickel-base single crystal alloy at 700 and 900℃ was investigated. The fatigue strengths for 107 cycles are 350 and 335MPa at 700 and 900℃, respectively. The total fatigue life becomes shorter when the temperature increases regardless of the loading stress and frequency. With the number of cycles decreasing, the difference in fatigue strength at the two temperatures becomes smaller. Typical fatigue rupture process including crack initiation site, crack propagation region and final rupture region exhibits at 700℃. The fracture surface is basically characterized by cleavage rupture at 900℃.展开更多
The influence of fabrication on the tensile and fatigue behavior of copper films manufactured by 3 kinds of fabrication methods was investigated. The tensile and high cycle fatigue tests were performed using the test ...The influence of fabrication on the tensile and fatigue behavior of copper films manufactured by 3 kinds of fabrication methods was investigated. The tensile and high cycle fatigue tests were performed using the test machine developed by authors. Young's moduli (72, 71 and 69 GPa, respectively) are lower than the literature values (108-145 GPa), while the yield strengths were as high as 358, 350 and 346 MPa, respectively and the ultimate strengths as 462, 456 and 446 MPa, respectively. There is not much difference in the tensile properties of the 3 kinds of films. There is little difference in the fatigue properties of the 3 kinds of films but one of them has shorter fatigue life than others in high cycle region and longer fatigue life than others in low cycle region.展开更多
基金supported by the National Natural Science Foundation of China(Nos.51375033 and 51405006)
文摘This paper addresses the effects of stress ratio on the temperature-dependent high-cycle fatigue (HCF) properties of alloy steels 2CrMo and 9CrCo, which suffer from substantial vibrational loading at small stress amplitude, high stress ratio, and high frequency in the high-temperature environments in which they fimcfion as blade and rotor spindle materials in advanced gas or steam turbine engines. Fatigue tests were performed on alloy steels 2CrMo and 9CrCo subjected to constant-amplitude loading at four stress ratios and at four and three temperatures, respectively, to determine their temperature-dependent HCF properties. The interaction mechanisms between high temperature and stress ratio were deduced and compared with each other on the basis of the results of fractographic analysis. A phenomenological model was developed to evaluate the effects of stress ratio on the temperature-dependent HCF properties of alloy steels 2CrMo and 9CrCo. Good correlation was achieved between the predictions and actual experiments, demonstrating the practical and effective use of the proposed method.
基金Project(2001AA332030) supported by the National High-Tech Research and Development Program of China
文摘Based on the investigation of the tensile properties of spray formed ultra-high strength Al10.8Zn2.9Mg1.9Cu alloys, the high-cycle fatigue properties under different theoretical stress concentration factors were investigated, the fatigue fracture surfaces and microstructures were observed, and the fatigue mechanism was discussed. The results indicate that the ultimate tensile strength of spray formed Al10.8Zn2.9Mg1.9Cu alloys can reach up to 730?740 MPa, and the elongation is about 8%?10% under the condition of two-stage aging treatment. For the stress ratio is 0.1, the maximum stress for 107 cycles is over 400 MPa and 120 MPa, when the theoretical stress concentration factor is 1 and 3, respectively.
基金supported by the Science and Technology Innovation Development Project of Yantai(No.2023ZDX016)。
文摘The increase in payload capacity of trucks has heightened the demand for cost-effective yet high performance brake discs.In this work,the thermal fatigue and wear of compacted graphite iron brake discs were investigated,aiming to provide an experimental foundation for achieving a balance between their thermal and mechanical properties.Compacted graphite iron brake discs with different tensile strengths,macrohardnesses,specific heat capacities and thermal diffusion coefficients were produced by changing the proportion and strength of ferrite.The peak temperature,pressure load and friction coefficient of compacted graphite iron brake discs were analyzed through inertia friction tests.The morphology of thermal cracks and 3D profiles of the worn surfaces were also discussed.It is found that the thermal fatigue of compacted graphite iron discs is determined by their thermal properties.A compacted graphite iron with the highest specific heat capacity and thermal diffusion coefficient exhibits optimal thermal fatigue resistance.Oxidization of the matrix at low temperatures significantly weakens the function of alloy strengthening in hindering the propagation of thermal cracks.Despite the reduced hardness,increasing the ferrite proportion can mitigate wear loss resulting from low disc temperatures and the absence of abrasive wear.
基金Funded by Natural Science Foundation of Inner Mongolia,China (No. 2019MS05033)。
文摘In order to study the anti-fatigue performance of RCA modified asphalt (RMA),the performance of RMA and 90#matrix asphalt with different modifier content were measured by asphalt penetration,ductility,softening point,Brookfield viscosity,rheological index,infrared spectrum and dielectric constant test.This paper discusses the changes of asphalt basic indexes,fatigue properties and asphalt components based on dielectric properties under different modifier contents,and analyzes the grey correlation degree between components and asphalt pavement performance indexes.The results show that the optimum content of RCA modifier is 16.7%of the asphalt quality according to the penetration,ductility,softening point,Brockfield viscosity,viscosity temperature curve and fatigue life.In the phase angle-strain curve,there is disorder in the latter part of the curve.According to the strain (ε_(d)) corresponding to the disorder point,a new fatigue failure criterion is proposed and proved.Based on the new asphalt fatigue failure criterion,the fatigue prediction model of asphalt mixture is improved,and the fatigue life predicted by the improved fatigue model is compared with the fatigue life obtained by four-point bending fatigue test.The results show that the proposed new asphalt fatigue failure criterion is reasonable,and the fatigue life predicted by the improved asphalt mixture fatigue prediction model is accurate.The research method of classifying asphalt components based on dielectric properties is simple and effective,and the components have a high correlation with the road performance of base asphalt and modified asphalt.
基金H.R.Bakhsheshi-Rad and S.Sharif would like to acknowledge UTM Research Management for the financial support through the funding(Q.J130000.2409.08G37).
文摘The addition of nanoscale additions to magnesium(Mg)based alloys can boost mechanical characteristics without noticeably decreasing ductility.Since Mg is the lightest structural material,the Mg-based nanocomposites(NCs)with improved mechanical properties are appealing materials for lightweight structural applications.In contrast to conventional Mg-based composites,the incorporation of nano-sized reinforcing particles noticeably boosts the strength of Mg-based nanocomposites without significantly reducing the formability.The present article reviews Mg-based metal matrix nanocomposites(MMNCs)with metallic and ceramic additions,fabricated via both solid-based(sintering and powder metallurgy)and liquid-based(disintegrated melt deposition)technologies.It also reviews strengthening models and mechanisms that have been proposed to explain the improved mechanical characteristics of Mg-based alloys and nanocomposites.Further,synergistic strengthening mecha-nisms in Mg matrix nanocomposites and the dominant equations for quantitatively predicting mechanical properties are provided.Furthermore,this study offers an overview of the creep and fatigue behavior of Mg-based alloys and nanocomposites using both traditional(uniaxial)and depth-sensing indentation techniques.The potential applications of magnesium-based alloys and nanocomposites are also surveyed.
基金supported by the National Research Council of Science&Technology(NST)grant(No.CRC-15-06-KIGAM)funded by the Korea government(MSIP)。
文摘Mg-Al-Zn-Ca-Y alloys with excellent ignition and corrosion resistances—termed SEN alloys(where the letters"S,""E,"and"N"stand for stainless,environmentally friendly,and non-flammable,respectively)—have been developed recently.In this study,the microstructure,tensile properties,and high-cycle fatigue properties of an extruded Mg-9.0Al-0.8Zn-0.1Mn-0.3Ca-0.2Y(SEN9)alloy are investigated and compared with those of a commercial Mg-9.0Al-0.8Zn-0.1Mn(AZ91)alloy extruded under the same conditions.Both the extruded SEN9 alloy and the extruded AZ91 alloy have a fully recrystallized structure comprising equiaxed grains,but the former has a smaller average grain size owing to the promoted dynamic recrystallization during extrusion.The extruded AZ91 alloy contains coarse Mg_(17)Al_(12) discontinuous precipitate(DP)bands parallel to the extrusion direction,which are formed during its cool down after extrusion.In contrast,the extruded SEN9 alloy contains relatively fine undissolved Al_(2)Ca,Al_(8)Mn_(4)Y,and Al_(2)Y second-phase particles,which are formed during the solidification stage of the casting process.The tensile strength of the extruded SEN9 alloy,which has finer grains and more abundant particles,is slightly higher than that of the extruded AZ91 alloy.However,the difference in their strengths is relatively small because the stronger solid-solution hardening and precipitation hardening effects in the extruded AZ91alloy offset the stronger grain-boundary hardening and dispersion hardening effects in the extruded SEN9alloy to some extent.The tensile elongation of the extruded AZ91 alloy is significantly lower than that of the extruded SEN9 alloy because the large cracks formed in the DP bands in the former cause its premature fracture.Although the extruded SEN9 alloy has higher tensile properties than the extruded AZ91alloy,the high-cycle fatigue life and fatigue strength of the former are shorter and lower,respectively,than those of the latter.The DP bands in the extruded AZ91 alloy do not act as fatigue crack initiation sites,and therefore,fatigue cracks initiate on the specimen surface at all stress amplitude levels.In contrast,in most of the fatigue-fractured specimens of the extruded SEN9 alloy,fatigue cracks initiate on the undissolved Al_(2)Ca and Al_(2)Y particles present on the surface or subsurface of the specimens because of the high local stress concentration on the particles during cyclic loading.This particle-initiated fatigue fracture eventually decreases the high-cycle fatigue resistance of the extruded SEN9 alloy.
基金Project supported bythe Key Technologies Fifteen R &D Programme (2001BA311A07-2) 985-Automotive Engineering ofJilin University
文摘The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa ( 1% Ce) and 105.5 MPa (2 % Ce), respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.
基金supported by the National Natural Science Foundation of China(No.50974080)
文摘High-temperature mechanical properties of high-boron austenitic steels(HBASs) were studied at 850 °C using a dynamic thermal-mechanical simulation testing machine. In addition, the thermal fatigue properties of the alloys were investigated using the self-restraint Uddeholm thermal fatigue test, during which the alloy specimens were cycled between room temperature and 800°C. Stereomicroscopy and scanning electron microscopy were used to study the surface cracks and cross-sectional microstructure of the alloy specimens after the thermal fatigue tests. The effects of carbon content on the mechanical properties at room temperature and high-temperature as well as thermal fatigue properties of the HBASs were also studied. The experimental results show that increasing carbon content induces changes in the microstructure and mechanical properties of the HBASs. The boride phase within the HBAS matrix exhibits a round and smooth morphology, and they are distributed in a discrete manner. The hardness of the alloys increases from 239(0.19 wt.% C) to 302(0.29 wt.% C) and 312 HV(0.37 wt.% C); the tensile yield strength at 850 °C increases from 165.1 to 190.3 and 197.1 MPa; and the compressive yield strength increases from 166.1 to 167.9 and 184.4 MPa. The results of the thermal fatigue tests(performed for 300 cycles from room temperature to 800 °C) indicate that the degree of thermal fatigue of the HBAS with 0.29 wt.% C(rating of 2–3) is superior to those of the alloys with 0.19 wt.%(rating of 4–5) and 0.37 wt.%(rating of 3–4) carbon. The main cause of this difference is the ready precipitation of M23(C,B)6-type borocarbides in the alloys with high carbon content during thermal fatigue testing. The precipitation and aggregation of borocarbide particles at the grain boundaries result in the deterioration of the thermal fatigue properties of the alloys.
基金the National Key Basic Research and Development Program of China under grant No.2004CB619104.
文摘The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime up to 107 cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AtSI 4340 steel in which the inclusion size is smaller than 5.5 μm, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 μm, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 pro. In the case of internal inclusion-induced fractures at cycles beyond about 1×10^6 for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure Nf in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with Nf, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1×10^6. Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.
基金supported by National Natural Science Foundation of China(Nos.51771115,51775334 and 51821001)Joint Fund for Space Science and Technology(Nos.6141B06310106 and 6141B06300401)National Defense Science and Technology Innovation Special Zone Project(No.002-002-01)。
文摘In this study,the tensile and high-cycle fatigue properties of as-cast,solid solution treated and as-extruded Mg-8Li-3Al-2Zn-0.5Y alloy are investigated.The results show that the yield strength and ultimate tensile strength of as-cast alloy is 198.1 MPa and 222.5 MPa,which are improved to 274.7 MPa and 321.7 MPa,282.4 MPa and 319.3 MPa after solid solution and extrusion treatment,respectively.The high-cycle fatigue strength(at 10^(7)cycles,R=-1)of as-cast studied alloy is 65 MPa,which is improved to 90 MPa and 105 MPa after solid solution and extrusion treatment,respectively.The improvement of fatigue property of the solid solution treated alloy is mainly due to the lattice distortion caused by solid solution hindering the crack propagation.However,the improvement of fatigue property of the as-extruded alloy is mainly due to that the refined grains,stacked dislocations and dispersed secondary particles impede the crack propagation.
基金Projects(2006BAB04A05) supported by the Eleventh Five-Year Plan of the National Key Technology Research and Development Program
文摘The fatigue properties of asphalts were investigated after various laboratory simulation ageing tests and outdoor natural exposure ultraviolet radiation ageing,by dynamic shear rheometer(DSR) time sweep fatigue test in constant strain model and a new type of specimen which was introduced to avoid the problem of adhesion failure between rotor and asphalt binder.The results show that outdoor natural exposure ageing(NEA) causes the decrease of retained fatigue life distinctly,and photodegradation caused by outdoor NEA of 1 250 μm thin films asphalt for three months,is found to be severer than pressure ageing vessel(PAV) with respects to retained fatigue life.The effect of photodegradation increases as the time of outdoor NEA increases.DSR time sweep fatigue test in constant strain indicates that the aged styrene-butadiene-styrene(SBS) modified asphalt still displays better fatigue properties than the corresponding base asphalt after ageing.
文摘The microstructure,strength,toughness and fatigue properties of an ultra-high strength steel 40CrMnSiMoVA have been investigated.The so-called meta-bainite,composed of thin re- tained austenite films within or between the bainitic ferrite lathes was found in the steel after isothermally quenched at 300℃ for 1h.In comparison with the martensite structure obtained by isothermally quenching in martensite range,the meta-bainite has more excellent strength and plasticity,lower notch sensitivity,stronger strain harden ability,higher fatigue strength, longer strain or impact fatigue life,slower crack propagation rate and more remarkable overload effect on increasing fatigue life.
基金The project supported by the Special Funds for the National Major Fundamental Research Projects(2004CB619304)the National Natural Science Foundation of China(10276020 and 50371042)the Key Grant Project of Chinese Ministry of Education(0306)
文摘In this paper, a two dimensional Voronoi cell element, formulated with creep, thermal and plastic strain, is applied for the numerical simulation of thermo-mechanical fatigue behavior for particulate reinforced composites. The relation between mechanical fatigue phases and thermal fatigue phases influences the thermo-mechanical fatigue behavior and cyclic creep damage. The topological features of micro-structure in particulate reinforced composites, such as the orientation, depth-width ratio, distribution and volume fraction of inclusions, have a great influence on thermo-mechanical behavior. Some related conclusions are obtained by examples of numerical simulation.
基金supported by the National Natural Science Foundation(No.51265013)the Natural Science Foundation of Jiangxi Province(No.20151BAB206007)
文摘The fatigue properties of friction stir welded (FSW) butt joint and base metal of MB8 magnesium alloy were investigated. The comparative fatigue tests were carried out using EHF-EM2OOK2-070-IA fatigue testing machine for both FSW butt joint and base metal specimens. The fatigue fractures were observed and analyzed using a scanning electron microscope of JSM-6063LA type. The experimental results show that the fatigue performance of the FSW butt joint of MB8 magnesium alloy is sharply decreased. The conditional fatigue limit (2 x 106) of base metal and welded butt joint is about 77.44 MPa and 49. 91 MPa, respectively. The conditional fatigue limit (2 x 106 ) of the welded butt joint is 64.45% of that of base metal. The main reasons are that the welding can lead to stress concentration in the flash area, tensile welding residual stress in the welded joint( The residual stress value was 30. 5 MPa), as well as the grain size is not uniform in the heat-affected zone. The cleavage steps or quasi-cleavage patterns present on the fatigue fracture surface, the fracture type of the FSW butt joint belongs to a brittle fracture.
基金Projects(50479023, 50708034) supported by the National Natural Science Foundation of ChinaProject(20070532069) supported by Specialized Research Fund for the Doctoral Program of Higher Education+1 种基金Project (20060400263) supported by China Postdoctoral Science FoundationProject(2007RS4031) supported by Provincial Science and Technology Plan of Hunan
文摘Fracture evolution process (initiation, propagation and coalescence) of cracked rock was observed and the force- displacement curves of cracked rock were measured under uniaxial cyclic loading. The tested specimens made of sandstone-like modeling material contained three pre-existing intermittent cracks with different geometrical distributions. The experimental results indicate that the fatigue deformation limit corresponding to the maximal cyclic load is equal to that of post-peak locus of static complete force?displacement curve; the fatigue deformation process can be divided into three stages: initial deformation, constant deformation rate and accelerative deformation; the time of fracture initiation, propagation and coalescence corresponds to the change of irreversible deformation.
基金Funded by the National Science and Technology Support Plan (No.2006BAD11B03)Shaanxi Provincial Natural Science Foundation(No.SJ08E111)
文摘Properties and mechanism were investigated on flexural fatigue of concrete containing polypropylene fibers and ground granulated blast furnace slag(GGBFS).Four polypropylene fibers’volume fractions and five slag proportions were considered.An experiment was conducted to obtain the fatigue lives at three stress levels in 20 Hz frequency and at a constant stress level of 0.59 in four frequency respectively.Mechanism and evaluation were investigated based on the experimental data.Fatigue life span models were established.The results show that the addition of polypropylene fibers improves the flexural fatigue cumulative strength and fatigue life span.It is proposed that the slag particles and hydrated products improve Interfacial Transition Zone(ITZ)structure and benefit flexural fatigue performance.A composite reinforce effect is found with the incorporation of slag and polypropylene fibers.The optimum mixture contents 55%slag with 0.6%polypropylene fiber for the cumulative fatigue stress.Fatigue properties are decreased as the stress level increasing,the higher frequency reduces the fatigue strength more than lower frequency at a constant stress level.
基金supported by the Knowledge Innovation Project of the Chinese Academy of Sciencesthe Beijing Municipal Natural Science Foundation+2 种基金the National Natural Science Foundation of China(Grant Nos.51102288 and 51372283)the Natural Science Foundation Project of Chongqing,China(Grant No.CSTC2012jjA50017)the Cooperative Project of Academician Workstation of Chongqing University of Science&Technology,China(Grant Nos.CKYS2014Z01 and CKYS2014Y04)
文摘The transport properties and fatigue effect of Ag/Bi0.9La0.lFeO3/La0.7Sr0.3MnO3 heterostructures are described. By examining the I-V curves, an anomalous fatigue effect was found and its influences on resistive states were studied. I-V curves combined with C-f spectra were used to directly analyze the transport properties and fatigue effect. Compared to the first I-V cycle state, this structure shows more than one order increase of resistance after 100 cycles of "I-V curve training". The redistribution of oxygen vacancies in the depletion layer of Ag/Bi0.9La0.lFeO3 is believed to be responsible for the different resistance mechanisms and tenfold magnitude drop in resistance. The resistive switching is understood to be caused by electric field-induced carrier trapping and detrapping, which changes the depletion layer thickness at the Ag/Bi0.9La0.lFeO3 interface.
基金ItemSponsored by High Technology Development Programof China (863) (2001AA332020)
文摘The fatigue properties of 400 MPa grade supersteel, plain low carbon steel SS400 and microalloyed steel Q340TM were investigated through tensile-compression fatigue experiment with R =- 1. The results indicate that the fatigue limit of the 400 MPa supersteel is higher than that of SS400 steel and close to that of the 340TM steel. According to the analysis of fatigue fracture, the fatigue striations of supersteel SS400 is thinner than that of SS400 steel and 340TM steel, and grain refinement can increase the fatigue limit.
文摘High-cycle rotating bending fatigue behavior of SRR99 nickel-base single crystal alloy at 700 and 900℃ was investigated. The fatigue strengths for 107 cycles are 350 and 335MPa at 700 and 900℃, respectively. The total fatigue life becomes shorter when the temperature increases regardless of the loading stress and frequency. With the number of cycles decreasing, the difference in fatigue strength at the two temperatures becomes smaller. Typical fatigue rupture process including crack initiation site, crack propagation region and final rupture region exhibits at 700℃. The fracture surface is basically characterized by cleavage rupture at 900℃.
文摘The influence of fabrication on the tensile and fatigue behavior of copper films manufactured by 3 kinds of fabrication methods was investigated. The tensile and high cycle fatigue tests were performed using the test machine developed by authors. Young's moduli (72, 71 and 69 GPa, respectively) are lower than the literature values (108-145 GPa), while the yield strengths were as high as 358, 350 and 346 MPa, respectively and the ultimate strengths as 462, 456 and 446 MPa, respectively. There is not much difference in the tensile properties of the 3 kinds of films. There is little difference in the fatigue properties of the 3 kinds of films but one of them has shorter fatigue life than others in high cycle region and longer fatigue life than others in low cycle region.