Poly(vinyl alcohol) (PVA) fiber mats containing 20 and 80 wt% H3PW12O40 were prepared by using electrospinning technique. The fiber mats were characterized by IR, XRD spectra and scanning electron microscope (SEM). ...Poly(vinyl alcohol) (PVA) fiber mats containing 20 and 80 wt% H3PW12O40 were prepared by using electrospinning technique. The fiber mats were characterized by IR, XRD spectra and scanning electron microscope (SEM). The diameter of the fiber mats is ca. 400 nm.展开更多
In order to study the effect of PVA fiber on the dynamic and static mechanical properties of low-temperature freeze-thaw concrete under the saturated surface dry state,different contents of PVA fiber were added to pre...In order to study the effect of PVA fiber on the dynamic and static mechanical properties of low-temperature freeze-thaw concrete under the saturated surface dry state,different contents of PVA fiber were added to prepare concrete in this experiment.The concrete was subjected to compression,flexural and SHPB impact tests combined with scanning electron microscopy for microstructure analysis,after different times of freeze-thaw cycles in the temperature range of 20-70℃.The experimental results show that the compressive strength of the PVA fiber reinforced concrete first increases and then decreases after freeze and thaw cycles,and the compressive strength is positively correlated with the fiber content.The flexural strength gradually decreases with freeze-thaw cycles.The flexural strength of the concrete with 1.2 kg/m^(3) of PVA fiber presents the lowest strength loss after 45 freeze and thaw cycles,which is about 14%.The dynamic failure strength gradually decreases with the increase of freeze-thaw times,and the reduction amplitude decreases with the increase of PVA fiber content.The best impact resistance is achieved when the PVA fiber dosage is 1.2 kg/m^(3).展开更多
Some noticeable effects of process conditions, such as coagulation bath, solvent extraction, drying shrinkage and ultra-drawing, on the structure and properties of gel-spun PVA fibers are studied and discussed. High s...Some noticeable effects of process conditions, such as coagulation bath, solvent extraction, drying shrinkage and ultra-drawing, on the structure and properties of gel-spun PVA fibers are studied and discussed. High strength and high modulus PVA fibers with tensile strength of 11.3 cN / dtex and initial modulus of 430 cN / dtex have been obtained.展开更多
Nowadays hydrogels have been attracting the massive interest in oil-water separation due to their robust hydrophilicity and fantastic underwater oiliness features.However,the weak toughness and tensile strength shortc...Nowadays hydrogels have been attracting the massive interest in oil-water separation due to their robust hydrophilicity and fantastic underwater oiliness features.However,the weak toughness and tensile strength shortcomings of hydrogels have thus inhibited their actual applicability.For this reason,we successfully fabricated the electrospun nanofiber membrane-reinforced PVA composite hydrogels.The PVA-PAN composite hydrogel has exhibited the excellent tensile strength and friction performance,separately enhancing 174.2%of the tensile strength,and reducing 20.7%of the friction coefficient and 58.7%of wear volume relative to the neat PVA hydrogel.Furthermore,the pull-out experiments indicated that the PAN nanofiber membrane exerted a stronger interface bonding effect with PVA hydrogel.The oil-water separation evaluation test showed that the separation efficiency reached up to 97.6%for treating the SA-100 lubricating oil/water system.展开更多
文摘Poly(vinyl alcohol) (PVA) fiber mats containing 20 and 80 wt% H3PW12O40 were prepared by using electrospinning technique. The fiber mats were characterized by IR, XRD spectra and scanning electron microscope (SEM). The diameter of the fiber mats is ca. 400 nm.
基金Funded by the National Natural Science Foundation of China (No.51972214)the Innovation Team of Higher Education Institutions in Liaoning Province (No.LT2019012)。
文摘In order to study the effect of PVA fiber on the dynamic and static mechanical properties of low-temperature freeze-thaw concrete under the saturated surface dry state,different contents of PVA fiber were added to prepare concrete in this experiment.The concrete was subjected to compression,flexural and SHPB impact tests combined with scanning electron microscopy for microstructure analysis,after different times of freeze-thaw cycles in the temperature range of 20-70℃.The experimental results show that the compressive strength of the PVA fiber reinforced concrete first increases and then decreases after freeze and thaw cycles,and the compressive strength is positively correlated with the fiber content.The flexural strength gradually decreases with freeze-thaw cycles.The flexural strength of the concrete with 1.2 kg/m^(3) of PVA fiber presents the lowest strength loss after 45 freeze and thaw cycles,which is about 14%.The dynamic failure strength gradually decreases with the increase of freeze-thaw times,and the reduction amplitude decreases with the increase of PVA fiber content.The best impact resistance is achieved when the PVA fiber dosage is 1.2 kg/m^(3).
文摘Some noticeable effects of process conditions, such as coagulation bath, solvent extraction, drying shrinkage and ultra-drawing, on the structure and properties of gel-spun PVA fibers are studied and discussed. High strength and high modulus PVA fibers with tensile strength of 11.3 cN / dtex and initial modulus of 430 cN / dtex have been obtained.
基金funded by the Jiangsu Yangzhou University Graduate Practice Innovation Program (XSJCX19-064)the Jiangsu Provincial Colleges and Universities First-Class Project Program (PPZY2015B112)
文摘Nowadays hydrogels have been attracting the massive interest in oil-water separation due to their robust hydrophilicity and fantastic underwater oiliness features.However,the weak toughness and tensile strength shortcomings of hydrogels have thus inhibited their actual applicability.For this reason,we successfully fabricated the electrospun nanofiber membrane-reinforced PVA composite hydrogels.The PVA-PAN composite hydrogel has exhibited the excellent tensile strength and friction performance,separately enhancing 174.2%of the tensile strength,and reducing 20.7%of the friction coefficient and 58.7%of wear volume relative to the neat PVA hydrogel.Furthermore,the pull-out experiments indicated that the PAN nanofiber membrane exerted a stronger interface bonding effect with PVA hydrogel.The oil-water separation evaluation test showed that the separation efficiency reached up to 97.6%for treating the SA-100 lubricating oil/water system.