Acid loss and plasticization of phosphoric acid(PA)-doped high-temperature polymer electrolyte membranes(HT-PEMs)are critical limitations to their practical application in fuel cells.To overcome these barriers,poly(te...Acid loss and plasticization of phosphoric acid(PA)-doped high-temperature polymer electrolyte membranes(HT-PEMs)are critical limitations to their practical application in fuel cells.To overcome these barriers,poly(terphenyl piperidinium)s constructed from the m-and p-isomers of terphenyl were synthesized to regulate the microstructure of the membrane.Highly rigid p-terphenyl units prompt the formation of moderate PA aggregates,where the ion-pair interaction between piperidinium and biphosphate is reinforced,leading to a reduction in the plasticizing effect.As a result,there are trade-offs between the proton conductivity,mechanical strength,and PA retention of the membranes with varied m/p-isomer ratios.The designed PA-doped PTP-20m membrane exhibits superior ionic conductivity,good mechanical strength,and excellent PA retention over a wide range of temperature(80–160°C)as well as satisfactory resistance to harsh accelerated aging tests.As a result,the membrane presents a desirable combination of performance(1.462 W cm^(-2) under the H_(2)/O_(2)condition,which is 1.5 times higher than that of PBI-based membrane)and durability(300 h at 160°C and 0.2 A cm^(-2))in the fuel cell.The results of this study provide new insights that will guide molecular design from the perspective of microstructure to improve the performance and robustness of HT-PEMs.展开更多
In this study,nitrogen doped electrochemically exfoliated reduced graphene oxide and carbon black supported platinum(Pt/Nr EGO_(2)-CB_(3))has been prepared to enhance the performance and durability of hightemperature ...In this study,nitrogen doped electrochemically exfoliated reduced graphene oxide and carbon black supported platinum(Pt/Nr EGO_(2)-CB_(3))has been prepared to enhance the performance and durability of hightemperature PEMFCs with lower Pt loading.On the one hand,Pt/Nr EGO_(2)-CB_(3)with the strong interaction between the Pt and nitrogen(N)prevent agglomeration of Pt particles and Pt particles is 5.46±1.46 nm,which is smaller than that of 6.78±1.34 nm in Pt/C.Meanwhile,ECSA of Pt/Nr EGO_(2)-CB_(3)decrease 13.65%after AST,which is much lower than that of 97.99%in Pt/C.On the other hand,the Nr EGO flakes in MEAac act as a barrier to mitigate phosphoric acid redistribution,which improves the formation of triple-phase boundaries(TPBs)and gives stable operation of the MEAacwith a lower decay rate of 0.02 mV h^(-1)within100 h.After steady-state operation,the maximum power density of Pt/Nr EGO_(2)-CB_(3)(0.411 W cm^(-2))is three times higher than that of conventional Pt/C(0.134 W cm^(-2))in high-temperature PEMFCs.After AST,the mass transfer resistance of Pt/Nr EGO_(2)-CB_(3)electrode(0.560Ωcm^(2))is lower than that in Pt/C(0.728Ωcm^(2)).展开更多
The formation of the barrier layer of anodic porous alumina film has been investigated in phosphoric acid solution. The results show that with the increase of phosphoric acid concentration,the time needed to form barr...The formation of the barrier layer of anodic porous alumina film has been investigated in phosphoric acid solution. The results show that with the increase of phosphoric acid concentration,the time needed to form barrier layer is shortened,and also the barrier layer becomes thinner. The phenomenon can be interpreted reasonablyby the stress concentration that developed in barrier layer.展开更多
基金supported by The National Key Research and Development Program of China(2021YFB4001204)National Natural Science Foundation of China(22379143)。
文摘Acid loss and plasticization of phosphoric acid(PA)-doped high-temperature polymer electrolyte membranes(HT-PEMs)are critical limitations to their practical application in fuel cells.To overcome these barriers,poly(terphenyl piperidinium)s constructed from the m-and p-isomers of terphenyl were synthesized to regulate the microstructure of the membrane.Highly rigid p-terphenyl units prompt the formation of moderate PA aggregates,where the ion-pair interaction between piperidinium and biphosphate is reinforced,leading to a reduction in the plasticizing effect.As a result,there are trade-offs between the proton conductivity,mechanical strength,and PA retention of the membranes with varied m/p-isomer ratios.The designed PA-doped PTP-20m membrane exhibits superior ionic conductivity,good mechanical strength,and excellent PA retention over a wide range of temperature(80–160°C)as well as satisfactory resistance to harsh accelerated aging tests.As a result,the membrane presents a desirable combination of performance(1.462 W cm^(-2) under the H_(2)/O_(2)condition,which is 1.5 times higher than that of PBI-based membrane)and durability(300 h at 160°C and 0.2 A cm^(-2))in the fuel cell.The results of this study provide new insights that will guide molecular design from the perspective of microstructure to improve the performance and robustness of HT-PEMs.
基金supported by the Engineering and Physical Sciences Research Council(EPSRC)(EP/P009050/1 and EP/S021531/1)Tthe Henry Royce Institute for Advanced Materials,funded through the EPSRC grants(EP/R00661X/1,EP/S019367/1,EP/P025021/1 and EP/P025498/1)。
文摘In this study,nitrogen doped electrochemically exfoliated reduced graphene oxide and carbon black supported platinum(Pt/Nr EGO_(2)-CB_(3))has been prepared to enhance the performance and durability of hightemperature PEMFCs with lower Pt loading.On the one hand,Pt/Nr EGO_(2)-CB_(3)with the strong interaction between the Pt and nitrogen(N)prevent agglomeration of Pt particles and Pt particles is 5.46±1.46 nm,which is smaller than that of 6.78±1.34 nm in Pt/C.Meanwhile,ECSA of Pt/Nr EGO_(2)-CB_(3)decrease 13.65%after AST,which is much lower than that of 97.99%in Pt/C.On the other hand,the Nr EGO flakes in MEAac act as a barrier to mitigate phosphoric acid redistribution,which improves the formation of triple-phase boundaries(TPBs)and gives stable operation of the MEAacwith a lower decay rate of 0.02 mV h^(-1)within100 h.After steady-state operation,the maximum power density of Pt/Nr EGO_(2)-CB_(3)(0.411 W cm^(-2))is three times higher than that of conventional Pt/C(0.134 W cm^(-2))in high-temperature PEMFCs.After AST,the mass transfer resistance of Pt/Nr EGO_(2)-CB_(3)electrode(0.560Ωcm^(2))is lower than that in Pt/C(0.728Ωcm^(2)).
文摘The formation of the barrier layer of anodic porous alumina film has been investigated in phosphoric acid solution. The results show that with the increase of phosphoric acid concentration,the time needed to form barrier layer is shortened,and also the barrier layer becomes thinner. The phenomenon can be interpreted reasonablyby the stress concentration that developed in barrier layer.