The dissolution of carbon steel in 5% HCl in the temperature range of 30~90℃ was inhibited by two organic compounds having the general formula: ClR NH2(CH2)n NH2 RCl where R is a benzyl group. The behaviour of these ...The dissolution of carbon steel in 5% HCl in the temperature range of 30~90℃ was inhibited by two organic compounds having the general formula: ClR NH2(CH2)n NH2 RCl where R is a benzyl group. The behaviour of these inhibitors in acidic medium were investigated using weight loss method, open circuit potential and linear polarization technique. These inhibitors provided satisfactory corrosion inhibition for carbon steel in hydrochloric acid solutions even at higher temperature and acid concentration (10%). The electrochemical results showed that the polarization resistance (Rp) values increased with increasing inhibitor concentration, also the corrosion current decreased and a higher inhibition efficiency was obtained. The protective properties of these two organic inhibitors were attributed to the chemisorption mechanism展开更多
Spent fuel reprocessing plays a pivotal role in achieving efficient recycling of nuclear fuel.Among thedifferent forms of failure encountered in spent fuel reprocessing,tribocorrosion stands out as a critical concern....Spent fuel reprocessing plays a pivotal role in achieving efficient recycling of nuclear fuel.Among thedifferent forms of failure encountered in spent fuel reprocessing,tribocorrosion stands out as a critical concern.Herein,the tribocorrosion behavior,as well as the corrosion behavior,of 304L stainless steel(SS)in high-temperatureconcentrated nitric acid was investigated.The results indicated that 304L SS formed a thin(1.54 nm)and stable passivefilm on the surface,imparting high resistance to nitric acid corrosion.Meanwhile,it was found that the synergistic effectbetween corrosion and wear accounted for a high total tribocorrosion weight loss of over 85%,implying the dominantrole of the synergistic effect in the tribocorrosion process.Furthermore,the wear of 304L SS in deionized water revealedboth abrasive and adhesive wear characterizations,whereas the tribocorrosion in nitric acid only exhibited abrasive wearfeature.Eventually,the tribocorrosion and corrosion models of 304L SS in hot concentrated nitric acid were proposedbased on the comprehensive experimental findings.展开更多
文摘The dissolution of carbon steel in 5% HCl in the temperature range of 30~90℃ was inhibited by two organic compounds having the general formula: ClR NH2(CH2)n NH2 RCl where R is a benzyl group. The behaviour of these inhibitors in acidic medium were investigated using weight loss method, open circuit potential and linear polarization technique. These inhibitors provided satisfactory corrosion inhibition for carbon steel in hydrochloric acid solutions even at higher temperature and acid concentration (10%). The electrochemical results showed that the polarization resistance (Rp) values increased with increasing inhibitor concentration, also the corrosion current decreased and a higher inhibition efficiency was obtained. The protective properties of these two organic inhibitors were attributed to the chemisorption mechanism
基金Projects(52101105,52373321)supported by the National Natural Science Foundation of ChinaProject(2023-PY03)supported by the IMR Innovation Fund,ChinaProject(CNNC-LCKY-202274)supported by the LingChuang Research Project of China National Nuclear Corporation。
文摘Spent fuel reprocessing plays a pivotal role in achieving efficient recycling of nuclear fuel.Among thedifferent forms of failure encountered in spent fuel reprocessing,tribocorrosion stands out as a critical concern.Herein,the tribocorrosion behavior,as well as the corrosion behavior,of 304L stainless steel(SS)in high-temperatureconcentrated nitric acid was investigated.The results indicated that 304L SS formed a thin(1.54 nm)and stable passivefilm on the surface,imparting high resistance to nitric acid corrosion.Meanwhile,it was found that the synergistic effectbetween corrosion and wear accounted for a high total tribocorrosion weight loss of over 85%,implying the dominantrole of the synergistic effect in the tribocorrosion process.Furthermore,the wear of 304L SS in deionized water revealedboth abrasive and adhesive wear characterizations,whereas the tribocorrosion in nitric acid only exhibited abrasive wearfeature.Eventually,the tribocorrosion and corrosion models of 304L SS in hot concentrated nitric acid were proposedbased on the comprehensive experimental findings.