In order to prolong the service life of castables for hot blast stove pipes,effects of SiO2 micropowder addition and aggregate kind on properties of castables for hot blast stove pipes,and properties of silica sol bon...In order to prolong the service life of castables for hot blast stove pipes,effects of SiO2 micropowder addition and aggregate kind on properties of castables for hot blast stove pipes,and properties of silica sol bonded castables were researched using homogenized bauxite,andalusite particles,andalusite fines,white fused corundum fines,α-Al2O3 micropowder,pure calcium aluminate cement,SiO2 micropowder,and silica sol as starting materials. The results show that:(1) as SiO2 micropowder addition increases,the shrinkage rate of fired specimens increases; BD increases firstly,reaches the highest at 4 mass%,and then decreases; CMOR and CCS of all specimens increase gradually; so the appropriate SiO2 micropowder addition is 4 mass%;(2) the specimens with bauxite aggregate have better CCS and volume stability,but specimens with andalusite aggregate have better thermal shock resistance;( 3) for castables for hot blast stoves using silica sol as binder,the addition of pure calcium aluminate cement can decrease the linear change rate after treatment at 1 400℃ and can slightly enhance CCS and CMOR,but has very little influence on AP and BD; and the introduction of citric acid worsens the thermal shock resistance of specimens.展开更多
This article shows an innovative method to model and validate the hot air flow through the blast furnacés tuyeres. This study will be the basis for flow measurements implementation and safety interlocks for the p...This article shows an innovative method to model and validate the hot air flow through the blast furnacés tuyeres. This study will be the basis for flow measurements implementation and safety interlocks for the pulverized coal injection. The flow measurements were taken in the blast furnace down leg pipes by installing refractory Venturi tubes. The system for the calculation of differential pressure takes into consideration the dimension of the Venturi, the air density and compressibility. The objective is to specify the flow transmitters required to automate a control system and implement safety interlocks for the coal injection plant.展开更多
文章提出一种能够准确评估高炉风口鼓风均匀性的方法,并以通才公司1860 m 3高炉的热风围管、热风支管、直吹管和风口小套为研究对象,采用CFD仿真研究方法,对高炉风口鼓风均匀性进行计算评估,根据评估结果对高炉风口参数进行针对性调节...文章提出一种能够准确评估高炉风口鼓风均匀性的方法,并以通才公司1860 m 3高炉的热风围管、热风支管、直吹管和风口小套为研究对象,采用CFD仿真研究方法,对高炉风口鼓风均匀性进行计算评估,根据评估结果对高炉风口参数进行针对性调节。结果表明,高炉风口尺寸相同时风口鼓风均匀率为95.69%,调节风口参数后风口鼓风均匀率可提高1.12个百分点,很大程度上改善了高炉风口鼓风均匀性。展开更多
文摘In order to prolong the service life of castables for hot blast stove pipes,effects of SiO2 micropowder addition and aggregate kind on properties of castables for hot blast stove pipes,and properties of silica sol bonded castables were researched using homogenized bauxite,andalusite particles,andalusite fines,white fused corundum fines,α-Al2O3 micropowder,pure calcium aluminate cement,SiO2 micropowder,and silica sol as starting materials. The results show that:(1) as SiO2 micropowder addition increases,the shrinkage rate of fired specimens increases; BD increases firstly,reaches the highest at 4 mass%,and then decreases; CMOR and CCS of all specimens increase gradually; so the appropriate SiO2 micropowder addition is 4 mass%;(2) the specimens with bauxite aggregate have better CCS and volume stability,but specimens with andalusite aggregate have better thermal shock resistance;( 3) for castables for hot blast stoves using silica sol as binder,the addition of pure calcium aluminate cement can decrease the linear change rate after treatment at 1 400℃ and can slightly enhance CCS and CMOR,but has very little influence on AP and BD; and the introduction of citric acid worsens the thermal shock resistance of specimens.
文摘This article shows an innovative method to model and validate the hot air flow through the blast furnacés tuyeres. This study will be the basis for flow measurements implementation and safety interlocks for the pulverized coal injection. The flow measurements were taken in the blast furnace down leg pipes by installing refractory Venturi tubes. The system for the calculation of differential pressure takes into consideration the dimension of the Venturi, the air density and compressibility. The objective is to specify the flow transmitters required to automate a control system and implement safety interlocks for the coal injection plant.
文摘文章提出一种能够准确评估高炉风口鼓风均匀性的方法,并以通才公司1860 m 3高炉的热风围管、热风支管、直吹管和风口小套为研究对象,采用CFD仿真研究方法,对高炉风口鼓风均匀性进行计算评估,根据评估结果对高炉风口参数进行针对性调节。结果表明,高炉风口尺寸相同时风口鼓风均匀率为95.69%,调节风口参数后风口鼓风均匀率可提高1.12个百分点,很大程度上改善了高炉风口鼓风均匀性。