Influence of hot rolling conditions on the mechanical properties of hot rolled TRIP steel was investigated. Thermomechanical control processing （TMCP） was conducted by using a laboratory hot rolling mill, in which t...Influence of hot rolling conditions on the mechanical properties of hot rolled TRIP steel was investigated. Thermomechanical control processing （TMCP） was conducted by using a laboratory hot rolling mill, in which three different kinds of finish rolling temperatures were applied. The results show that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained by controlled rolling processes. The finer ferrite grain size is produced through the deformation induced transformation during deformation rather than after deformation, which affects the mechanical properties of hot rolled TRIP steel. Mechanical properties increase with decreasing finish rolling temperature due to the stabilization of retained austenite. Ultimate tensile strength （UTS）, total elongation （TEL） and the product of ultimate tensile strength and total elongation （UTS×TEL） reaches optimal values （791 MPa, 36% and 28 476 MPa%, respectively） when the specimen was hot rolled for 50% reduction at finish rolling temperature of 700 ℃.展开更多
A three-step cooling pattern on the runout table（ROT）was conducted for the hot rolled TRIP steel.Microstructural evolution during thermomechanical controlled processing（TMCP）was investigated.Processing condition o...A three-step cooling pattern on the runout table（ROT）was conducted for the hot rolled TRIP steel.Microstructural evolution during thermomechanical controlled processing（TMCP）was investigated.Processing condition of controlled cooling on a ROT in the laboratory rolling mill was discussed.The results indicated that the microstructure containing polygonal ferrite,granular bainite and a significant amount of the stable retained austenite can be obtained through three-step cooling on the ROT after hot rolling.TMCP led to ferrite grain refinement.Controlled cooling after hot rolling resulted in the stability of the remaining austenite and a satisfactory TRIP effect.Excellent mechanical properties were obtained through TMCP for the hot rolled TRIP steel.展开更多
The effect of thermomechanical control processing（TMCP）on microstructure and mechanical properties of Fe-0.2C-1.44Si-1.32Mn hot rolled TRIP steel was investigated through experiments.Strain-induced transformation an...The effect of thermomechanical control processing（TMCP）on microstructure and mechanical properties of Fe-0.2C-1.44Si-1.32Mn hot rolled TRIP steel was investigated through experiments.Strain-induced transformation and transformation-induced plasticity behavior of retained austenite were analyzed.The results show that with multipass deformation,reduction per pass of more than critical deformation in austenite recrystallization region and total reduction of more than 58% in non-recrystallization region and high temperature section of two-phase region,austenite can be refined before γ→α transformation.It is beneficial to obtain refined ferrite grain in final microstructure.To obtain fine and uniform microstructure and excellent strength-ductility balance,a three-stage cooling process（laminar cooling-air cooling-ultra-fast cooling）after hot rolling was conducted.The ultimate tensile strength and elongation of the investigated steel can reach 663 MPa and 41%,respectively.展开更多
基金the National Natural Science Foundation of China(No.50334010)the Program of Education Branch of Liaoning Province of China(No.2006B075)
文摘Influence of hot rolling conditions on the mechanical properties of hot rolled TRIP steel was investigated. Thermomechanical control processing （TMCP） was conducted by using a laboratory hot rolling mill, in which three different kinds of finish rolling temperatures were applied. The results show that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained by controlled rolling processes. The finer ferrite grain size is produced through the deformation induced transformation during deformation rather than after deformation, which affects the mechanical properties of hot rolled TRIP steel. Mechanical properties increase with decreasing finish rolling temperature due to the stabilization of retained austenite. Ultimate tensile strength （UTS）, total elongation （TEL） and the product of ultimate tensile strength and total elongation （UTS×TEL） reaches optimal values （791 MPa, 36% and 28 476 MPa%, respectively） when the specimen was hot rolled for 50% reduction at finish rolling temperature of 700 ℃.
基金Item Sponsored by National Natural Science Foundation of China(50334010)
文摘A three-step cooling pattern on the runout table（ROT）was conducted for the hot rolled TRIP steel.Microstructural evolution during thermomechanical controlled processing（TMCP）was investigated.Processing condition of controlled cooling on a ROT in the laboratory rolling mill was discussed.The results indicated that the microstructure containing polygonal ferrite,granular bainite and a significant amount of the stable retained austenite can be obtained through three-step cooling on the ROT after hot rolling.TMCP led to ferrite grain refinement.Controlled cooling after hot rolling resulted in the stability of the remaining austenite and a satisfactory TRIP effect.Excellent mechanical properties were obtained through TMCP for the hot rolled TRIP steel.
基金Item Sponsored by National Fundamental Project of Science and Technology of China(ZZ0113A0101)
文摘The effect of thermomechanical control processing（TMCP）on microstructure and mechanical properties of Fe-0.2C-1.44Si-1.32Mn hot rolled TRIP steel was investigated through experiments.Strain-induced transformation and transformation-induced plasticity behavior of retained austenite were analyzed.The results show that with multipass deformation,reduction per pass of more than critical deformation in austenite recrystallization region and total reduction of more than 58% in non-recrystallization region and high temperature section of two-phase region,austenite can be refined before γ→α transformation.It is beneficial to obtain refined ferrite grain in final microstructure.To obtain fine and uniform microstructure and excellent strength-ductility balance,a three-stage cooling process（laminar cooling-air cooling-ultra-fast cooling）after hot rolling was conducted.The ultimate tensile strength and elongation of the investigated steel can reach 663 MPa and 41%,respectively.