This paper reports the chemical synthesis of tungsten carbide/cobalt (WC/Co) nanocomposite powders via a unique chemical processing technique, involving the using of all water soluble solution of W-, Co- and C-precurs...This paper reports the chemical synthesis of tungsten carbide/cobalt (WC/Co) nanocomposite powders via a unique chemical processing technique, involving the using of all water soluble solution of W-, Co- and C-precursors. In the actual synthesis, large quantities of commercial-scale WC-Co nanocomposite powders are made by an unique combination of converting a molecularly mixed W-, Co-, and C-containing solutions into a complex inorganic polymeric powder precursor, conversion of the inorganic polymeric precursor powder into a W-Co-C-O containing powder intermediates using a belt furnace with temperature at about 500°C - 600°C in an inert atmosphere, followed by carburization in a rotary furnace at temperature less than 1000°C in nitrogen. Liquid phase sintering technique is used to consolidate the WC/Co nanocomposite powder into sintered bulk parts. The sintered parts have excellent hardness in excess of 93 HRA, with WC grains in the order of 200 - 300 nm, while Co phase is uniformly distributed on the grain boundaries of the WC nanoparticles. We also report the presence of cobalt Co precipitates inside tungsten carbide WC nanograins in the composites of the consolidated bulk parts. EDS is used to identify the presence of these precipitates and micro-micro-diffraction technique is employed to determine the nature of these precipitates.展开更多
文摘This paper reports the chemical synthesis of tungsten carbide/cobalt (WC/Co) nanocomposite powders via a unique chemical processing technique, involving the using of all water soluble solution of W-, Co- and C-precursors. In the actual synthesis, large quantities of commercial-scale WC-Co nanocomposite powders are made by an unique combination of converting a molecularly mixed W-, Co-, and C-containing solutions into a complex inorganic polymeric powder precursor, conversion of the inorganic polymeric precursor powder into a W-Co-C-O containing powder intermediates using a belt furnace with temperature at about 500°C - 600°C in an inert atmosphere, followed by carburization in a rotary furnace at temperature less than 1000°C in nitrogen. Liquid phase sintering technique is used to consolidate the WC/Co nanocomposite powder into sintered bulk parts. The sintered parts have excellent hardness in excess of 93 HRA, with WC grains in the order of 200 - 300 nm, while Co phase is uniformly distributed on the grain boundaries of the WC nanoparticles. We also report the presence of cobalt Co precipitates inside tungsten carbide WC nanograins in the composites of the consolidated bulk parts. EDS is used to identify the presence of these precipitates and micro-micro-diffraction technique is employed to determine the nature of these precipitates.