Investigation and improvement of tiny spot defects on hot-dip galvanized automotive steel sheets

The causes of tiny spot defects on the surface of hot-dip galvanized automotive steel sheets were studied using scanning electron microscopy(SEM)and energy dispersive spectrometer(EDS),and effective control measures were introduced.The results show that rubbing against the top roller after galvanizing is easy due to the local thickness of tiny spot defect location coating;therefore,the surface morphology is different from the normal part.Three kinds of defects,namely zinc slag,small slivers,and pitting,are likely to cause local thickening of the coating after galvanizing,leading to the formation of tiny spots.Therefore,resolving the three types of defects can effectively control the generation of tiny spot defects.Among them,due to the hereditary nature of the small sliver defect,focusing on its control and supervision is necessary.

Recent development of UHSS and its hot-dip galvanizing processes in Baosteel

Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel products.Some milestones achieved by Baosteel automotive steel sheet were briefly reviewed.The current challenges in producing ultra-high strength steel(UHSS),especially hot-dip galvanized UHSS,were summarized.The most current advancements in UHSS and the corresponding hot-dip galvanizing processes were discussed.The galvanizability of Si-Mn-added QP steel and DP steel, Mn-added TWIP steel, and Al-added low-density steel has been improved by different techniques in Baosteel.

Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel

A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and then reheated to 450°C(process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel(DP600) was investigated using optical microscopy, scanning electron microscopy(SEM), transmission electron microscopy(TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength(YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient(n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength(UTS) and elongation(A80) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties(YS = 362 MPa, UTS = 638 MPa, A_(80) = 24.3%, n = 0.17) was obtained via process A.

Hot-Dip Galvanized Sheet Production and Application

Hot-dip galvanized sheet is wildly used in construction,household appliances,ship,vehicle and vessel building and machinery,etc.In last ten years,with the development of automobile industry,the anti-eorrosion requirements for car body are increasingly strict,by which the rapid development in technology has been promoted.The application of hot-dip galvanized sheet,technological progress in production and some Chinese large units were introduced.

Preparation and hot-dip galvanizing application of CeO_2/Zn nanocomposite

CeO2/Zn nanocomposite was fabricated by high-energy ball milling and subsequent hot-press sintering under vacuum. The produced nanocomposite powders and bulks were characterized using X-ray diffraction （XRD）, transmission electron microscopy （TEM） and scanning electron microscopy （SEM） with an energy dispersive X-ray spectrum （EDS）. The as-fabricated nanocomposite bulks were added successfully into the hot-dip galvanizing bath to improve the corrosion resistance of coatings. The results show that after milling for 120min, nano-sized CeO2 particles are distributed homogeneously on the surface of fine Zn particles to form spherical-like nanocomposite powder with narrow grain size distribution. The subsequent sintering does not lead to a dramatic grain growth, and the distribution of CeO2 nanoparticles in the composite bulk is also homogeneous. With the addition of as-prepared bulks, the corrosion resistance of the galvanized coatings is improved obviously. It provides a feasible route for adding CeO2 nanoparticles into the hot-dip galvanized coating.

Evolution of appearance profile of hot-dip galvanized car-body steel sheet during deformation process

In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the painting process is reduced, which directly affects the appearance quality（ long-and short-wave values） of the body paint. Thus, there are correspondingly higher requirements for the white body surface profile prior to painting. The surface profile of the white body is mainly affected by the plate material, the surface profile, and the deformation process. So,the change rule for the surface profile during deformation of the steel plate is a key factor in coating appearance optimization. In this paper, we first analyze the typical deformation of the outer cover of a car body. Then ,we examine the change tendency of the surface profile of steel plates with respect to different deformation rates, specifically for a steel plate comprising a hot-dip galvanized bake-hardened steel sheet. Based on our analysis of the influence of the deformation on the coating appearance,we selected 3% ,5% ,and 8% deformation rates in this research. We found the roughness （Ra） value in the typical deformation range （3% -8% ） of the car body to exhibit a decreasing trend at first and then an increasing trend. The Ra value of the 8% deformation is not more than the original plate test value. When the Pc value of the original plate is in the lower range （ about 60）, it exhibits a slight increasing trend in the deformation process （3 % -8 % ）. And when the Pc value of the original plate is in the higher range （ about 120 ）, it exhibits no increasing trend in the deformation process （ 3% -8% ）. In contrast,the waviness （WCA） value in the car body＇s typical deformation range （3%-8%） shows a significant growth trend.

Development of Cr-free anti-fingerprint hot-dip galvanized sheet for household appliances

China has become the maximum household appliances manufacturing base worldwide.It is a new challenge facing the steel industry to develop the low-cost and environment-friendly sheet for household appliance industry,so Cr-free anti-fingerprint hot-dip galvanized sheet for household appliances is the upgraded product which satisfies the requirement of China household appliance industry' s nuisanceless treatment.The paper discusses the technical key points of development on Cr-free anti-fingerprint galvanized sheet for household appliances,including the development of the Cr-free anti-fingerprint chemical and the production technology of Cr-free anti-fingerprint galvanized sheet for household appliances.The paper elaborates the main compositions,physical features and properties of the Cr-free anti-fingerprint chemical, surface quality control technology,anti-fingerprint coating quality control technology,influence of anti-fingerprint film weight on corrosion resistance,conductibility,high-temperature discolouration resistance,acid resistance,alkaline resistance and solvent resistance of Cr-free anti-fingerprint hot-dip galvanized sheet, influence of anti-fingerprint coating uniformity on paintability of the sheet,influence of strip surface roughness on corrosion resistance and conductivity of the sheet and influence of strip surface quality on corrosion resistance of the sheet.Adopting the suitable Cr-free anti-fingerprint chemical and the reasonable production process parameters,the properties of the Cr-free anti-fingerprint hot-dip galvanized sheet conform to the delivery technical norms and the Cr-free anti-fingerprint hot-dip galvanized sheet becomes the new material for household appliances such as computer case.

Application of WC cermet sprayed composite coating in hot-dip galvanizing lines

With the rapid development of the automobile industry, the use of galvannealed and galvanized steel sheets in automobiles is on the rise. These sheets must meet very high surface quality requirements. The surface treatment of line rolls is known to have a great impact on strip quality. To prevent dusts such as zinc ash from pressing into the strip surface, we used a composite thermal spray surface treatment technique to treat rolls. The successfully developed tungsten carbide （WC） ＋ Ni-P composite plating technology improved the quality of the tungsten carbide thermally sprayed WC roll surface. This technique is also helpful to control defects such as adhered foreign materials in hot-dip galvanized automobile outer panel surfaces.

Investigation of Surface Damage in Forming of High Strength and Galvanized Steel Sheets

Powdering/exfoliating of coatings and scratching galvanized steels and high strength steels （HSS）, are the main forms of surface damage in the forming of which result in increased die maintenance cost and scrap rate. In this study, a special rectangular box was developed to investigate the behavior and characteristics of surface damage in sheet metal forming （SMF） processes. U-channel forming tests were conducted to study the effect of tool hardness on surface damage in the forming of high strength steels and galvanized steels （hot-dip galvanized and galvannealed steels）. Experimental results indicate that sheet deformation mode influences the severity of surface damage in SMF and surface damage occurs easily at the regions where sheet specimen deforms under the action of compressive stress. Die corner is the position where surface damage initiates. For HSS sheet, surface damage is of major interest due to high forming pressure. The HSS and hot-dip galvanized steels show improved ability of damage-resistance with increased hardness of the forming tool. However, for galvannealed steel it is not the forming tool with the highest hardness value that performs best.

The Influence of Al on the Surface Properties of the Hot-dip Galvanized Melt

Wettability of Zn-Al alloy melt on the pure iron substrate at 450℃was studied.The effect of Al content(Zn,Zn-1Al,Zn-2Al,Zn-3Al,Zn-4Al,and Zn-5Al)on the wetting behavior and interfacial reaction was investigated by high-temperature contact angle measuring device and scanning electron microscope(SEM).The results show that,with the increase of Al content,the initial contact angle of the molten alloy on the substrate decreases gradually and the wettability increases gradually.Compared with the initial contact angle,the final contact angle is slightly reduced,because the Fe-Al inhibition layer is preferentially formed at the interface when adding Al to the alloy.The presence of Al will promote the occurrence of the reactive wetting,leading to an insignificant wetting spreading process,and the final contact angle negligibly differs from the initial contact angle.The adhesion work and charge density distributions of interface systems were calculated based on the first-principles.The results show that the adhesion work of the Fe/Zn and Fe/(Zn-Al)interface model is 2.0171 J/m^(2)and 13.7944 J/m^(2),respectively.The addition of Al greatly increases the adhesion work between alloy melt and iron substrate.Compared with the Zn-Fe and Al-Fe interface models,it can be seen that a significant charge migration phenomenon occurs between the interfaces.The amount of charge migration in the Al-Fe interface model is much larger than that in the Zn-Fe interface model,indicating that the bonding between Al-Fe atoms can occur more easily and the interaction between Al-Fe interfaces is stronger.This is also the reason why the addition of Al increases the adhesion work between interfaces.

Laser brazing with filler wire for galvanized steel sheets

The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the appearance quality of the brazing seams, the roles of the processing parameters, such as brazing speed, wire feeding rate, inclination and feeding direction of the wire, laser power, spot diameter and heating position, were assessed. The further investigation indicates that the behavior of the active elements Si, Mn and Zn are significantly influenced by energy input. At the interface, the microstructure of the base metal was composed of columnar crystals and the acicular α solid solution was found on the filler metal side.

Analysis of causes and influence factors of small black spot defects in hot-dip galvanized pure Zn products

In this study,the factors affecting the formation of small black spot defects on the surface of a hot-dip galvanized pure zinc strip are analyzed. These defects are primarily formed w hen the iron-aluminum inhibition layer is incompletely formed or fails to form or when foreign matter adheres to the surface or embeds in the zinc layer.The defects can be reduced by controlling the cleanliness and activity of the strip base before coating,regulating the zinc pot process parameters,and ensuring the cleanliness of the passline and workshop.

Effect of surface roughness on the surface lubrication performance of galvanized steel sheets with a self-lubricated coating

Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication performance of the steel sheets were examined using a friction coefficient tester. Results revealed large dynamic friction coefficients for the galvanized steel sheets, which increased remarkably with surface roughness. Once the self-lubricated coating was applied, significant drops in the dynamic friction coefficients were measured. After the first stage of the friction test,the coefficients were almost unchanged, which reflected a weak dependence on the surface roughness of the self-lubricated steel sheets. However, the dynamic friction coefficients gradually increased as the test progressed, where these increase clearly correlated with the surface roughness of the self-lubricated steel sheets.

Surface topography evolvement of galvanized steels in sheet metal forming

U-channel forming tests were performed to investigate the surface topography evolvement of hot-dip galvanized(GI) and galvannealed(GA) steels and the effects of die hardness on sheet metal forming(SMF). Experimental results indicate that the surface roughness values of the two galvanized steels increase with the number of forming,i.e.,the surface topographies of galvanized steels are roughened in SMF. Moreover,GI steel has a better ability of damage-resistance than GA steel. The mechanisms of topography evolvement are different in the forming of GI and GA steels. Scratch is the main form of surface damage in the forming of GI steels. The severity of scratch can be decreased by increasing die hardness. GA steel results in exfoliating of the coating firstly and then severe scratching. The surface topography of galvannealed steels can be improved by increasing die hardness. However,the hardness should not be too high.

Effect of Variable Blank Holder Force on Rectangular Box Drawing Process of Hot-galvanized Sheet Steel

At first, a series of finite element method （FEM） simulation tests were used to find the critical forming conditions of hot-galvanized sheet steel during the rectangular box drawing processing when constant blank holder forces were applied. According the test results, the reasonable alteration scope of initial variable blank holder force （VBHF） was as 1.9-2.3 T. Then, based on the test productions of blank holder force, 12 typical VBHF curves were applied to perform the simulation tests by the simulation software of DYNAFORM. The simulation test results showed that VBHF had great effects on drawing formability of hot-galvanized sheet steel during the rectangular box drawing. However, the different VBHF curves were applied to control the whole drawing and it would get great different effects. At the same tine, the VBHF had great effects on the maximum thick thinning ratio, but had little effect on the maximum thick incrassation ratio. So, reasonable application of the VBHF would greatly decrease the fractures. When the VBHF profile is taken as curve L, the best effect of drawing formability could be obtained. When curve I is used, contrary effect could be gotten. The other types of curves would cause effects between above two types of VBHF curves. Finally, the actual tests were applied to check the validity of the FEM simulation tests. The results show that the FEM simulation tests are good ways for predicting and optimizing the VBHF.

Properties of Baosteel inorganic-lubricant-coated galvanized steel sheet for automotive body panels

An inorganic lubrication treatment for a galvanized steel sheet was developed to improve the press formability of automotive body panels. The properties and application of Baosteel＇s inorganic-lubricant-coated galvanized steel sheet are demonstrated. Compared with galvanized steel sheets without the inorganic lubricant coating,the Baosteel inorganic-lubricant-coated galvanized steel sheet has a lower friction coefficient and excellent lubricating ability,more homogeneous tribological and stamping behaviors,lower sensitivity to stamping parameters,excellent spot weldability,good adhesivity,and perfect phosphate compatibility and paintability. These results verify that the Baosteel inorganic-lubricant-coated galvanized steel sheet has excellent press formability and a huge market application potential.

Lead and Cadmium Distribution in Tubes of Galvanized Steel by Hot-Dip Used for Drinking Water Supply

The main objective of this work was to evaluate the presence of lead and cadmium in galvanized steel tubes by hot-dip used exclusively for drinking water supply.In this research,samples of galvanized tubes were removed from walls of residential buildings with 30 years of use.In the process of hot galvanizing,the manufacturing standards allow or for low cost conveniences,and the use of primary zinc ingot with 1.6%metallic impurities,such as lead and cadmium,is allowed,enabling the incorporation of these metals into the zinc coating deposited on the carbon steel.The associated corrosion of these tubes can release these toxic metals,contaminating the drinking water used by residents.The samples taken from the tubes were evaluated by a square-wave anodic stripping voltammetry technique,and the results for lead and cadmium suggested randomly distributed levels,indicating that the contents of these contaminants depend mainly on the quality of the added primary zinc and the operational conditions of the immersion bath.The metallographic evaluations performed on the samples of the galvanized tubes showed irregularities in thickness and even a lack of the zinc layer deposited on the carbon steel surface.These facts suggest that galvanized tubes should not be used for drinking water.

The development of advanced Cr-free organic composite coated electrogalvanized steel sheet with excellent grounding property

In recent years,the concern about environmental protection is increasing on a world scale.Major manufacturers of home appliances and OA equipment have introduced so-called 'green procurement schemes' for reducing environmentally harmful substances in manufacturing process and end products. Under such background,a new type of chromate-free organic composite coated electro-galvanized steel sheet with high conductivity was developed by Baosteel,which meets the EU RoHS Directive(Restriction of the Hazardous Substances) and other related laws and regulations on environmental safety.It also provides excellent surface electrical conductivity,corrosion resistance,fingerprint resistance,solvent resistance,coating adhesion, heat resistance,formability and other special properties to meet the demand of manufacture's process of OA machine. Compared with previously developed anti-fingerprinting coated electro-galvanized steel sheet,this newly developed product has a good balance between high corrosion resistance(time to 5%white rust in salt spray test is 120 h for flat panel and 72 h for worked potion) and conductivity(surface electro-resistivity in accordance with LOREAST is less than 0.1 milliohm ) due to the special design of coating's structure.Besides,It also provides the properties of grounding and shielding against electromagnetic waves.The evaluation of surface performances of new product showed that it is comparable or even better than the similar products. Currently,the newly developed product has been commercialized. In this paper,the major properties are discussed,such as corrosion resistance,surface electrical conductivity, fingerprint resistance,solvent resistance,coating adhesion(ink/melamine alkyd paint),heat resistance and formability.Furthermore,the application is also briefly described.

锌铝镁冲压后表面黑点缺陷原因分析

针对唐钢镀锌铝镁板在冲压过程中出现的表面黑点现象,使用光学显微镜(OM)、扫描电子显微镜(SEM)及能谱仪等检测仪器进行检测,分析其冲压后表面出现黑点的原因,结果表明,在锌铝镁镀层钢板冲压过程中,镀层开裂,润滑油夹杂着异物颗粒在宽裂纹处聚集,表现为黑点缺陷。

锌铝镁镀层和纯锌镀层在典型大气环境中初期腐蚀行为研究

目的增加对不同大气环境中锌铝镁镀层钢腐蚀行为的了解,研究中国地区不同气候条件下1a内锌铝镁镀层钢腐蚀产物的组成和腐蚀速率。方法采用SEM、GDS、XRD研究了纯锌(GI)镀层材料和锌铝镁合金(ZM)镀层材料的结构,对比研究了GI镀层和ZM镀层在吐鲁番、江津、青岛以及万宁4个大气试验站的腐蚀试验。结果万宁GI的腐蚀速率为ZM的4.56倍,江津GI的腐蚀速率为ZM的3.76倍,青岛GI的腐蚀速率为ZM的2.84倍,吐鲁番GI的腐蚀速率为ZM的2.42倍,对于GI镀层和ZM镀层,按腐蚀速率从大到小的顺序依次为万宁、青岛、江津、吐鲁番。江津和万宁GI镀层的自腐蚀电流密度较小,万宁ZM镀层的自腐蚀电流密度最小。锌的大气腐蚀速率主要受相对湿度、氯离子含量、SO_(2)含量等影响,主要通过影响腐蚀产物组成来影响锌的腐蚀速率。腐蚀产物的保护性受其化学组成、导电性、黏附性、致密性、溶解性、厚度、形态和亲水性等因素影响,不同的锈层结构对阴极氧还原的抑制作用不一样,高氯环境对GI的保护性腐蚀产物Zn_(5)(CO_(3))_(2)(OH)_(6)有较大的破坏性,在高碱性环境下,容易使腐蚀产物转变成疏松导电的ZnO。在高氯环境中,由于镀层中MgZn_(2)的阳极溶解,释放出可与OH反应的Mg^(2+)以形成氢氧化镁(Mg(OH)_(2))。在ZM表面用Mg(OH)_(2)代替氧化锌被认为可以降低阴极氧还原反应(ORR),具有缓冲阴极位置的pH值升高的作用,能使碱式碳酸锌变得稳定,显著提升耐腐蚀性。结论ZM镀层材料在高盐高湿环境下能形成稳定的腐蚀产物,降低阴极氧还原速率,在典型大气环境下具有广阔的应用前景。