Characteristic of laser-MIG hybrid welding with filling additional cold wire for aluminum alloy

The weld appearance, deposition rate, welding efficiency, stability of arc, laser keyhole characteristic, and weld property were studied by using a novel laser-MIG hybrid welding process with filling wire of aluminum alloy. The results were also compared with those by conventional laser-MIG hybrid welding process. It was found that with the suitable process parameters this novel welding process for aluminum alloy was stable and final weld bead had fine appearance. Compared to conventional laser-MIG hybrid welding process, during this novel welding process the stability of arc, the laser keyhole characteristic and the weld property were similar, while the keyhole cycle frequency and keyhole opening area had differences of 1.23% and 15.34%, respectively, and the welding efficiency increased by about 31% without increasing heat input.

Fluorescence lifetime measurement from a designated single-bunch in the BEPCⅡ colliding mode

Fluorescence lifetime measurement in the time domain requires excitation from a well separated single bunch using synchrotron light sources. In the colliding mode of the Beijing Electron Positron Collider Ⅱ （BEPCⅡ）, a hybrid filling pattern was realized such that a single bunch was placed in the middle of a large gap between two multi-bunch groups. Detection of fluorescence lifetime, based on the excitation of the light pulse from this designated single-bunch, was established at Beamline 4B8 of the Beijing Synchrotron Radiation Facility （BSRF）. The timing signal of the BEPCII was utilized as a trigger to gate this fluorescence event. L-Tryptophan amino acid, a known lifetime standard, was selected to assess the lifetime measurement performance. The measured lifetime was consistent in both colliding and single-bunch mode with the time resolution down to 450 ps. Moreover, both the bunch purity and the fine structure of the hybrid filling pattern were characterized.