PANI/ZnPcCl_（16）（polyaniline doped with sulfosalicylic acid/hexadecachloro zinc phthalocyanine） powders were vacuum co-deposited onto Si substrates,where Pt interdigitated electrodes were made by micromachining.Th...PANI/ZnPcCl_（16）（polyaniline doped with sulfosalicylic acid/hexadecachloro zinc phthalocyanine） powders were vacuum co-deposited onto Si substrates,where Pt interdigitated electrodes were made by micromachining.The PANI/ZnPcCl_（16） films were characterized and analyzed by SEM,and the influencing factors on its intrinsic performance were analyzed and sensitivities of the sensors were investigated by exposure to chlorine（Cl_2） gas.The results showed that powders prepared with a stoichiometric ratio of（ZnPcCl_（16））_（0.6）（PANI）_（0.4） had a preferential sensitivity to Cl_2 gas, superior to those prepared otherwise;the optimal vacuum co-deposition conditions for the films are a substrate temperature of 160℃,an evaporation temperature of 425℃and a film thickness of 75 nm;elevating the operation temperature （above 100℃） or increasing the gas concentration（over 100 ppm） would improve the response characteristics,but there should be upper levels for each.Finally,the gas sensing mechanism of PANI/ZnPcCl_（16） films was also discussed.展开更多
基金Project supported by the National Natural Science Foundation of China(Nos.60772019,50675184)the National Hi-Tech Research and Development Program of China(No.2007AA04Z308)the National Science Foundation for Post-doctoral Scientists of China(No. 20080440839).
文摘PANI/ZnPcCl_（16）（polyaniline doped with sulfosalicylic acid/hexadecachloro zinc phthalocyanine） powders were vacuum co-deposited onto Si substrates,where Pt interdigitated electrodes were made by micromachining.The PANI/ZnPcCl_（16） films were characterized and analyzed by SEM,and the influencing factors on its intrinsic performance were analyzed and sensitivities of the sensors were investigated by exposure to chlorine（Cl_2） gas.The results showed that powders prepared with a stoichiometric ratio of（ZnPcCl_（16））_（0.6）（PANI）_（0.4） had a preferential sensitivity to Cl_2 gas, superior to those prepared otherwise;the optimal vacuum co-deposition conditions for the films are a substrate temperature of 160℃,an evaporation temperature of 425℃and a film thickness of 75 nm;elevating the operation temperature （above 100℃） or increasing the gas concentration（over 100 ppm） would improve the response characteristics,but there should be upper levels for each.Finally,the gas sensing mechanism of PANI/ZnPcCl_（16） films was also discussed.