The structure, chemical bonds and hydra-tion activity of C12A were studied by SCC-DV-Xa method of computational quantum chemistry. The calculated results show that Ca-O bond will be first broken off when C12A hydrates...The structure, chemical bonds and hydra-tion activity of C12A were studied by SCC-DV-Xa method of computational quantum chemistry. The calculated results show that Ca-O bond will be first broken off when C12A hydrates, the reactivity of Al(2)O4 tetrahedron is superior to that of Al(1)O4 tet, thedron and the rupture of the Al-O-Al chain composed of two types of AlO4 tetrahedra under the action of water lies in the very weak Al(2)-O(2) bonds. the Al-O bond strength of C12A7 is between C3A and C11A7·CaF2.展开更多
Red mud was firstly used as a raw material in sintering field road cement. Then, the radioactive element distribution characteristics of red mud based field road cement(RFC) before and after hydration were comparati...Red mud was firstly used as a raw material in sintering field road cement. Then, the radioactive element distribution characteristics of red mud based field road cement(RFC) before and after hydration were comparatively investigated. The experimental results indicated that the specific activity of ^(226)Ra and ^(232)Th increased after sintering process from raw material to clinker, as a result of concentrating effect on ^(226)Ra and ^(232)Th during sintering process, but the specific activity of ^(40)K decreased after sintering process as a result of volatilization effect. Radionuclide ^(226)Ra mainly distributed in RFC silicate phases(C_xS), ^(232)Th distributed more in RFC interstitial phases than RFC silicate phases(C_xS), ^(40)K mainly distributed in RFC interstitial phases. With increasing hydration ages of RFC pastes, the specific activity of ^(226)Ra kept increasing, ^(232)Th remained consistency all the same and ^(40)K declined. The radioactivity of RFC was in the recommended safe limit of Chinese National Standards GB6566-2010 during its preparation and application process.展开更多
Calcined magnesite is a binding additive and an MgO-bearing flux for pellets production. The effects of cal- cination temperature and time on the characteristics of calcined magnesite were investigated. Experimental r...Calcined magnesite is a binding additive and an MgO-bearing flux for pellets production. The effects of cal- cination temperature and time on the characteristics of calcined magnesite were investigated. Experimental results in dicated that the best calcination condition was 850℃ and 1h. Under this condition, the hydration activity of the eal cined magnesite was 80.56%, and the average diameter of crystal grain D, specific surface area S and the medium particle size D50 were 25.4 nm, 45.40 m2/g and 3.41μm, respectively. This kind of calcined magnesite was a good binding additive for pellets production. At the same proportion of calcined magnesite, the effects of activities of cal cined magnesite on metallurgical properties of green pellet and indurated pellet showed that calcined magnesite with high activity could improve the dropping strength and compressive strength of green pellet and enhance the burst temperature of green pellet; however, the effects of activity on compressive strength, low-temperature reduction degradation index, reduction swelling index and reduction index of indurated pellet were not obvious.展开更多
文摘The structure, chemical bonds and hydra-tion activity of C12A were studied by SCC-DV-Xa method of computational quantum chemistry. The calculated results show that Ca-O bond will be first broken off when C12A hydrates, the reactivity of Al(2)O4 tetrahedron is superior to that of Al(1)O4 tet, thedron and the rupture of the Al-O-Al chain composed of two types of AlO4 tetrahedra under the action of water lies in the very weak Al(2)-O(2) bonds. the Al-O bond strength of C12A7 is between C3A and C11A7·CaF2.
基金Funded by the National Natural Science Foundation of China(No.51172155)
文摘Red mud was firstly used as a raw material in sintering field road cement. Then, the radioactive element distribution characteristics of red mud based field road cement(RFC) before and after hydration were comparatively investigated. The experimental results indicated that the specific activity of ^(226)Ra and ^(232)Th increased after sintering process from raw material to clinker, as a result of concentrating effect on ^(226)Ra and ^(232)Th during sintering process, but the specific activity of ^(40)K decreased after sintering process as a result of volatilization effect. Radionuclide ^(226)Ra mainly distributed in RFC silicate phases(C_xS), ^(232)Th distributed more in RFC interstitial phases than RFC silicate phases(C_xS), ^(40)K mainly distributed in RFC interstitial phases. With increasing hydration ages of RFC pastes, the specific activity of ^(226)Ra kept increasing, ^(232)Th remained consistency all the same and ^(40)K declined. The radioactivity of RFC was in the recommended safe limit of Chinese National Standards GB6566-2010 during its preparation and application process.
基金Item Sponsored by National Natural Science Foundation of China(51074206,51074040)
文摘Calcined magnesite is a binding additive and an MgO-bearing flux for pellets production. The effects of cal- cination temperature and time on the characteristics of calcined magnesite were investigated. Experimental results in dicated that the best calcination condition was 850℃ and 1h. Under this condition, the hydration activity of the eal cined magnesite was 80.56%, and the average diameter of crystal grain D, specific surface area S and the medium particle size D50 were 25.4 nm, 45.40 m2/g and 3.41μm, respectively. This kind of calcined magnesite was a good binding additive for pellets production. At the same proportion of calcined magnesite, the effects of activities of cal cined magnesite on metallurgical properties of green pellet and indurated pellet showed that calcined magnesite with high activity could improve the dropping strength and compressive strength of green pellet and enhance the burst temperature of green pellet; however, the effects of activity on compressive strength, low-temperature reduction degradation index, reduction swelling index and reduction index of indurated pellet were not obvious.