The immobilization of Co(Ⅱ) in various cement matrices was investigated by using the solidification/stabilization(S/S) technique.The different cement pastes used in this study were ordinary Portland cement in abs...The immobilization of Co(Ⅱ) in various cement matrices was investigated by using the solidification/stabilization(S/S) technique.The different cement pastes used in this study were ordinary Portland cement in absence and presence of water reducing-and water repelling-admixtures as well as blended cement with kaolin.Two ratios of Co(Ⅱ) were used(0.5% and 1.0% by weight of the solid binder).The hydration characteristics of the used cement pastes were tested via the determination of the combined water content,phase composition and compressive strength at different time intervals up to 180 d.The degree of immobilization of the added heavy metal ions was evaluated by determining the leached ion concentration after time intervals extended up to 180 d.The leachability experiments were carried out by using two modes:the static and the semi-dynamic leaching processes.It was noticed that the concentration of the leached Co2+ ions in the static mode of leachability was lower than the solubility of its hydroxide in all the investigated cement pastes.展开更多
文摘The immobilization of Co(Ⅱ) in various cement matrices was investigated by using the solidification/stabilization(S/S) technique.The different cement pastes used in this study were ordinary Portland cement in absence and presence of water reducing-and water repelling-admixtures as well as blended cement with kaolin.Two ratios of Co(Ⅱ) were used(0.5% and 1.0% by weight of the solid binder).The hydration characteristics of the used cement pastes were tested via the determination of the combined water content,phase composition and compressive strength at different time intervals up to 180 d.The degree of immobilization of the added heavy metal ions was evaluated by determining the leached ion concentration after time intervals extended up to 180 d.The leachability experiments were carried out by using two modes:the static and the semi-dynamic leaching processes.It was noticed that the concentration of the leached Co2+ ions in the static mode of leachability was lower than the solubility of its hydroxide in all the investigated cement pastes.