At present,there is limited research on the application of fuel cell power generation system technology using solid hydrogen storage materials,especially in hydrogen-assisted two-wheelers.Considering the disadvantages...At present,there is limited research on the application of fuel cell power generation system technology using solid hydrogen storage materials,especially in hydrogen-assisted two-wheelers.Considering the disadvantages of low hydrogen storage capacity and poor kinetics of hydrogen storage materials,our primary focus is to achieve smooth hydrogen ab-/desorption over a wide temperature range to meet the requirements of fuel cells and their integrated power generation systems.In this paper,the Ti_(0.9)Zr_(0.1)Mn_(1.45)V_(0.4)Fe_(0.15) hydrogen storage alloy was successfully prepared by arc melting.The maximum hydrogen storage capacity reaches 1.89 wt% at 318 K.The alloy has the capability to absorb 90% of hydrogen storage capacity within 50 s at 7 MPa and release 90% of hydrogen within 220 s.Comsol Multiphysics 6.0 software was used to simulate the hydrogen ab-/desorption processes of the tank.The flow rate of cooling water during hydrogen absorption varied in a gradient of(0.02 t x)m s^(-1)(x=0,0.02,0.04,0.06,0.08,0.1,0.12).Cooling water flow rate is positively correlated with the hydrogen absorption rate but negatively correlated with the cost.When the cooling rate is 0.06 m s^(-1),both simulation and experimentation have shown that the hydrogen storage tank is capable of steady hydrogen desorption for over 6 h at a flow rate of 2 L min^(-1).Based on the above conclusions,we have successfully developed a hydrogen-assisted two-wheeler with a range of 80 km and achieved regional demonstration operations in Changzhou and Shaoguan.This paper highlights the achievements of our team in the technological development of fuel cell power generation systems using solid hydrogen storage materials as hydrogen storage carriers and their application in twowheelers in recent years.展开更多
The effects of annealing treatment on the microstructure and electrochemical properties of low-Co LaNi 3.55 Mn 0.35 Co 0.20 Al 0.20 Cu 0.75 Fe 0.10 hydrogen storage alloys were investigated. X-ray diffraction (XRD) ...The effects of annealing treatment on the microstructure and electrochemical properties of low-Co LaNi 3.55 Mn 0.35 Co 0.20 Al 0.20 Cu 0.75 Fe 0.10 hydrogen storage alloys were investigated. X-ray diffraction (XRD) analysis indicated that annealing treatment remarkably reduced the lattice strain and defects, and increased the unit-cell volume. The optical microscope analysis showed that the as-cast alloy had a crass dendrite microstructure with noticeable composition segregation, which gradually disappeared with increasing annealing temperature, and the micro-structure changed to an equiaxed structure after annealing the alloy at 1233 K. The electrochemical tests indicated that the annealed alloys demonstrated much better cycling stability compared with the as-cast one. The capacity retention at the 100th cycle increased from 90.0% (as-cast) to 94.7% (1273 K). The annealing treatment also improved the discharge capacity. However, the high rate dischargeability (HRD) value of the annealed alloy slightly dropped, which was believed to be ascribed to the decreased exchange current density and the hydrogen diffusion coefficient in alloy bulk.展开更多
In order to investigate the effect of substituting La with Pr on structural and hydrogen storage properties of La-Mg-Ni system (AB3.5-type) hydrogen storage alloys, a series of La0.65-xPrxNd0.12Mg0.23Ni3.4Al0.1(x=0...In order to investigate the effect of substituting La with Pr on structural and hydrogen storage properties of La-Mg-Ni system (AB3.5-type) hydrogen storage alloys, a series of La0.65-xPrxNd0.12Mg0.23Ni3.4Al0.1(x=0, 0.10, 0.15, 0.2) hydrogen storage alloys were prepared. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) analyses revealed that two alloys (x=0.0 and 0.10) were composed of (La,Mg)2(Ni,Al)7 phase, La(Ni,A1)5 phase and (La,Mg)Ni2 phase, while other alloys (x=0.15 and 0.20) consisted of (La,Mg)2(Ni,A1)7 phase, La(Ni,A1)5 phase, (La,Mg)Ni2 phase and (La,Mg)(Ni,A1)3 phase. All alloys showed, however, only one pressure plateau in P-C isotherms. The Pr/La ratio in alloy composition influenced hydrogen storage capacity and kinetics properties. Electrochemical studies showed that the discharge capacity decreased from 360 mAh/g (x=-0.00) to 335 mAh/g (x=-0.20) as x increased. But the high-rate dischargeability (HRD) of alloy electrodes increased from 26% (x=0.00) to 56% (x=-0.20) at a discharge current density of Id=1800 mA/g. Anode polarization measurements were done to further understand the electrochemical kinetics properties after Pr substitution.展开更多
The effects of surface treatment, particle size distribution,rare earth composition and B additive on the high rate discharge performance of hydrogen storage alloys were investigated. It is found that the activity, di...The effects of surface treatment, particle size distribution,rare earth composition and B additive on the high rate discharge performance of hydrogen storage alloys were investigated. It is found that the activity, discharge capacity and high rate dischargeability of the alloys are improved after physical and chemical modification as a result of the increase of the surface area and formation of the electrocatalysis layers, which increase both the electrochemical reaction rate on the alloy surface and H diffusion rate in the alloy bulk. It is also found that both the over-coarse and over-fine particle size increase the contact resistance of the electrode, resulting in a decrease of discharge capacity, deterioration of high rate dischargeability and lower discharge plateau. In another word, a suitable particle size distribution can enhance the alloy activity, discharge capacity and high rate dischargeability. In addition, the high rate dischargeability is enhanced by increasing La content and decreasing Ce content of the alloy composition because of enlargement of the unit cell volume and the improvement of the surface activity. Moreover, B additive resultes in the formation of the second phase, and makes the alloys easier pulverization, which greatly improves the activity, discharge capacity and high rate dischargeability.展开更多
The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the ...The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the 0.2 C discharge capacity of as-cast LPCNi3.55Co0.75Mn0.4Al0.3 alloy increases with the increase of the thickness of the ingots. As-east alloy with the thickness of 10 mm shows better activation property, higher 1C discharge capacity and better cyclic stability than others. It is mainly contributed to its larger unit cell volume and less internal stress. Annealed LPCNi3.55Co0.75Mn0.4Al0.3 alloy with the thickness of 3 mm shows much better comprehensive electrochemical properties than as-east one; The cyclic. stability of the alloy with the thickness of 6 mm and the activation properties of the alloys with the thickness of 3 similar to 6 mm are improved after annealing. It is mainly owing to the great release of internal stress and the decrease of the segregation of Mn in the alloys.展开更多
Hydrogenation kinetics of MLNi3.8(Co,Mn,Al)1.2 and MLNi3.7(Co,Mn,Al)1.2Cu0.1 alloy in α + β phase at the temperatUre range of 30 ~70 ℃ has been studied. The kinetic mechanism of hydrogen absorption is not affecte...Hydrogenation kinetics of MLNi3.8(Co,Mn,Al)1.2 and MLNi3.7(Co,Mn,Al)1.2Cu0.1 alloy in α + β phase at the temperatUre range of 30 ~70 ℃ has been studied. The kinetic mechanism of hydrogen absorption is not affected by initial hydrogen pressure. Temperature does not influence the rate of hydrogen absorption obviously. In the prior and later period of hydrogen absorption the rate-controlling step is chemical reaction and hydrogen diffusion in the hydride phase respectively for MLNi3.8(Co,Mn,Al)1.2 alloy. Adding Cu, the rate-controlling step changes from chemical reaction to the nucleation and growth of β phase in the prior period and the process of hydrogen absorption still controlled by diffusion in the later period.展开更多
The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage allo...The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage alloys were compared with those of the high-Co AB_5 typehydrogen storage alloy as well. The results showed that the faster the cooling of the low-Cohydrogen storage alloy is, the better homogeneity of the chemical composition for the alloy and thelonger cycle life of the battery are, but the electrochemical discharge capacity and high-ratedischarge ability are reduced. The high-rate discharge ability and charge retention of MH-Nibatteries for the conventional as-cast annealed low-Co hydrogen storage alloy were superior to thosefor the rapidly quenched low-Co hydrogen storage alloy and the high-Co hydrogen storage alloy, buta little inferior in the cycle life.展开更多
The kinetics of liquid-phase hydrogenation of toluene catalyzed by MlNi_5 was studied by investigating the influences of the reaction temperature and pressure on the mass transfer-reaction processes inside the slurry....The kinetics of liquid-phase hydrogenation of toluene catalyzed by MlNi_5 was studied by investigating the influences of the reaction temperature and pressure on the mass transfer-reaction processes inside the slurry. The results show that the reaction rate accelerates when the reaction temperature increases, and reaches its maximum at about 490 K, but if temperature is higher than 510 K, the reaction rate decreases rapidly. The whole reaction process is controlled by the reaction at the surface of the catalyst particles. The mass transfer resistance at gas-liquid interface and that from the bulk liquid phase to the surface of the catalyst particle can be neglected. The apparent reaction rate is zero order for toluene concentration and first order for hydrogen concentration in the liquid phase. The kinetic model is obtained. The kinetic model fits the experimental data very well. The apparent activation energy of the hydrogen absorption reaction of MlNi_5-toluene slurry system is 41.01 kJ·mol^(-1).展开更多
The hydrogen storage properties of Ti1.2Fe+xCa (x=1%, 3% and 5% in mass fraction) alloys was investigated. Results stow that the modified alloys can be activated without any thermal treatment at room temperature due t...The hydrogen storage properties of Ti1.2Fe+xCa (x=1%, 3% and 5% in mass fraction) alloys was investigated. Results stow that the modified alloys can be activated without any thermal treatment at room temperature due to the addition of Ca and excess Ti in (lie alloys. Hydrogen storage properties of these modified alloys vary with Ca amount and reaction temperature. In addition, the influence mechanism of the addition of Ca and excessive Ti on the activation behavior and hydrogen storage capacity of the alloys was discussed.展开更多
In this paper,a simulation model for the temperature field in the solidification process and microstructure distribution is presented. Then, the result of simulation for the final microstructure distribution is compa...In this paper,a simulation model for the temperature field in the solidification process and microstructure distribution is presented. Then, the result of simulation for the final microstructure distribution is compared with experiment using 10-Kg ingot of MlNi3.55Al0.3Mn0.4CO0.75 (Ml: Lanthanum-rich Mischmetal) hydrogen stor- age alloy cast in a mould, which agrees with the experiment well. Finally, in order to obtain the expected as-cast microstructure distribution of 15-Kg ingot of MlNi3.55Al0.3Mn0.4Co0.75 alloy, the size of Cu mould is optimized using the model described. The optimized mould is then made and the alloy is cast in it, the expected as-cast microstructure distribution is obtained.展开更多
In order to improve the cycling stability of AB5 type alloy electrodes,rapid quenching technology and new alloy composition design were employed.A hydrogen storage alloy with nominal composition La0.6Ce0.4Ni3.6Co0.65M...In order to improve the cycling stability of AB5 type alloy electrodes,rapid quenching technology and new alloy composition design were employed.A hydrogen storage alloy with nominal composition La0.6Ce0.4Ni3.6Co0.65Mn0.4Al0.2Ti0.05(FeB)0.1 was prepared by vacuum magnetic levitation melting under high purity argon atmosphere,followed by rapid quenching at different cooling rates.XRD results show that all alloys exhibit the single-phase CaCu5-type structure.Electrochemical tests indicate that rapid quenching can slightly improve the cycling life of the alloy.Nevertheless,the high-rate dischargeability of the quenched alloys is lower than that of the as-cast alloy.展开更多
Rare earth-Mg-Ni-based alloys with superlattice structures are new generation negative electrode materials for the nickel metal hydride batteries.Among them,the novel AB_(4)-type superlattice structure alloy is suppos...Rare earth-Mg-Ni-based alloys with superlattice structures are new generation negative electrode materials for the nickel metal hydride batteries.Among them,the novel AB_(4)-type superlattice structure alloy is supposed to have superior cycling stability and rate capability.Yet its preparation is hindered by the crucial requirement of temperature and the special composition which is close to the other superlattice structure.Here,we prepare rare earth-Mg-Ni-based alloy and study the phase transformation of alloys to make clear the formation of AB_(4)-type phase.It is found Pr_(5)Co_(19)-type phase is converted from Ce_(5)Co_(19)-type phase and shows good stability at higher temperature compared to the Ce_(5)Co_(19)-type phase in the range of 930-970℃.Afterwards,with further 5℃increasing,AB_(4)-type superlattice structure forms at a temperature of 975℃by consuming Pr_(5)Co_(19)-type phase.In contrast with A_(5)B_(19)-type alloy,AB_(4)-type alloy has superior rate capability owing to the dominant advantages of charge transfer and hydrogen diffusion.Besides,AB_(4)-type alloy shows long lifespan whose capacity retention rates are 89.2%at the 100;cycle and 82.8%at the 200;cycle,respectively.AB_(4)-type alloy delivers 1.53 wt.%hydrogen storage capacity at room temperature and exhibits higher plateau pressure than Pr_(5)Co_(19)-type alloy.The work provides novel AB_(4)-type alloy with preferable electrochemical performance as negative electrode material to inspire the development of nickel metal hydride batteries.展开更多
The hydriding/dehydriding thermodynamic properties of the slurry system formed by suspending La rich mischmetal nickel hydrogen storage alloy (MlNi 5) in Benzene (C 6H 6) were investigated. The pressure compositi...The hydriding/dehydriding thermodynamic properties of the slurry system formed by suspending La rich mischmetal nickel hydrogen storage alloy (MlNi 5) in Benzene (C 6H 6) were investigated. The pressure composition isotherms for both the alloy powder and the slurry suspended with MlNi 5 were measured at several temperatures(10, 20, 30, 40 ℃). The standard enthalpy of formation Δ H ° and standard entropy of formation Δ S ° for the alloy powder with and without benzene were determined respectively. The experimental results show that the values of Δ H ° and Δ S ° for the hydriding reaction of hydrogen storage alloy (MlNi 5) of the slurry system and the gas solid system are all very close.展开更多
Surface-treated MmNi3.55Co0.75Mn0.4Al0.3 alloy as negative electrode material of nickel-metal hydride battery was employed to improve the high-rate dischargeability. Surface treatment was realized by dipping and stirr...Surface-treated MmNi3.55Co0.75Mn0.4Al0.3 alloy as negative electrode material of nickel-metal hydride battery was employed to improve the high-rate dischargeability. Surface treatment was realized by dipping and stirring the alloy into a HCl aqueous solution with various concentrations at room temperature. The microstructure of the alloy before and after surface treatment was analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The electrochemical properties before and after surface treatment were compared, and the alloy treated in 0.025 mol/L HCl solution showed the optimal high-rate dischargeability.展开更多
The crystal structure, phase abundance and the electrochemical properties of Zr(Mn1-x Nix)2 (0.40 ≤x≤0.75) alloys were investigated by means of XRD, Rietveld refinement method and electrochemical measurements. The a...The crystal structure, phase abundance and the electrochemical properties of Zr(Mn1-x Nix)2 (0.40 ≤x≤0.75) alloys were investigated by means of XRD, Rietveld refinement method and electrochemical measurements. The alloys are multiphase. C15 Laves phase occurs as a main phase accompanying with C14 phase and other minor phases, indicating that Ni element is C15-stabilized element for ZrMn2 alloy. The phase abundance and lattice parameters of Laves phase are influenced significantly by Ni substitution. The Zr(Mn0.45 Ni0.55)2 alloy with the highest amount of C15 phase exhibits the maximum electrochemical capacity of 242m Ah/g. C14 phase occurring in Zr-Mn-Ni alloys is beneficial for the electrochemical kinetics of hydride electrodes.展开更多
The effects of rapid solidification on the microstructure and electrochemical properties of Nd0.8Mg0.2(Ni0.8Co0.2)3.8 alloy were systematically investigated.The microstructure of alloys was characterized by scanning e...The effects of rapid solidification on the microstructure and electrochemical properties of Nd0.8Mg0.2(Ni0.8Co0.2)3.8 alloy were systematically investigated.The microstructure of alloys was characterized by scanning electron microscopy(SEM),X-ray diffractometer(XRD) and transmission electron microscopy(TEM).It was found that the melt-spun Nd0.8Mg0.2(Ni0.8Co0.2)3.8 ribbons became thinner and the average grain size of the ribbons became smaller with increasing wheel speed.A fraction of amorphous phase was obs...展开更多
Investigation of alloy structure shows that La2-xMgxNi7 (x = 0.3 - 0.8) alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is ...Investigation of alloy structure shows that La2-xMgxNi7 (x = 0.3 - 0.8) alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is great, resulting in a linear decrease of the unit cell parameters of main phases and increase of hydrogen absorption/desorption plateau as Mg content increases. Electrochemical measurements show that as the Mg content increases, the discharge capacity of alloy electrodes first increases and then decreases. The cyclic stability presents a deteriorative trend. La1.4Mg0.6 Ni7 alloy electrode exhibits the maximum electrochemical discharge capacity (378 mAh·g^-1), and the La1.6Mg0.4Ni7 alloy electrode shows the best cyclic stability (S270 = 81%).展开更多
In ordertoimprovethe dischargecapacity of Ti2 Ni hydrogen storage alloy, the phases and effecton the property for Ti Nialloy with alittle La( La contentisbetween 5 25 wt% and12 62 wt%) were investigated in this pa...In ordertoimprovethe dischargecapacity of Ti2 Ni hydrogen storage alloy, the phases and effecton the property for Ti Nialloy with alittle La( La contentisbetween 5 25 wt% and12 62 wt%) were investigated in this paper. It is found that La exists in the form ofLaNi5 ,thesecond phase,in Ti Nialloy when La> 8 wt% . LaNi5 phasecaneffectivelyim provethe activity property and discharge capacity of Ti Ni alloy. While the soluble Ti inmain phase Ti2 Niisadverseto hydrogen adsorption desorption cycle and itshould be dimin ished .展开更多
Rare earth compositions, La, Ce and Pr in Mm(NiCoMnAl)(5) hydrogen storage alloy, were arranged by uniform design method. The discharge performances and kinetics parameters including capacity, exchange current density...Rare earth compositions, La, Ce and Pr in Mm(NiCoMnAl)(5) hydrogen storage alloy, were arranged by uniform design method. The discharge performances and kinetics parameters including capacity, exchange current density, symmetry factor and hydrogen diffusion coefficient of the alloy at -40degreesC, were tested in standard tri-electrode cell. And linear regression method was used to analyze the effect of rare earth compositions on the performances of hydrogen storage alloys. The results show that the capacities of the alloys are positively correlative to the square of Ce content at -40degreesC and under both 0.4 and 0.2C rate. The kinetics parameters and hydrogen diffusion coefficient indicate that the low-temperature performances of the alloys are mainly controlled by hydrogen diffusion process, and the surface electrochemical reaction affects the low-temperature performances to a certain extent. The low-temperature discharge capacities of the battery were also tested. The results show excellent low-temperature performances. The battery delivers 69.6% of its room-temperature capacity at -40degreesC and 0.2C rate, 77.7% at -40degreesC and 0.4C rate, 59.1% at -45degreesC and 0.2C rate.展开更多
基金financed by the National Key Research and Development Program of China[grants number 2022YFB3803800]the National Natural Science Foundation of China[grants number 52071141,52271212,52201250,51771056]Interdisciplinary Innovation Program of North China Electric Power University[grants number XM2112355].
文摘At present,there is limited research on the application of fuel cell power generation system technology using solid hydrogen storage materials,especially in hydrogen-assisted two-wheelers.Considering the disadvantages of low hydrogen storage capacity and poor kinetics of hydrogen storage materials,our primary focus is to achieve smooth hydrogen ab-/desorption over a wide temperature range to meet the requirements of fuel cells and their integrated power generation systems.In this paper,the Ti_(0.9)Zr_(0.1)Mn_(1.45)V_(0.4)Fe_(0.15) hydrogen storage alloy was successfully prepared by arc melting.The maximum hydrogen storage capacity reaches 1.89 wt% at 318 K.The alloy has the capability to absorb 90% of hydrogen storage capacity within 50 s at 7 MPa and release 90% of hydrogen within 220 s.Comsol Multiphysics 6.0 software was used to simulate the hydrogen ab-/desorption processes of the tank.The flow rate of cooling water during hydrogen absorption varied in a gradient of(0.02 t x)m s^(-1)(x=0,0.02,0.04,0.06,0.08,0.1,0.12).Cooling water flow rate is positively correlated with the hydrogen absorption rate but negatively correlated with the cost.When the cooling rate is 0.06 m s^(-1),both simulation and experimentation have shown that the hydrogen storage tank is capable of steady hydrogen desorption for over 6 h at a flow rate of 2 L min^(-1).Based on the above conclusions,we have successfully developed a hydrogen-assisted two-wheeler with a range of 80 km and achieved regional demonstration operations in Changzhou and Shaoguan.This paper highlights the achievements of our team in the technological development of fuel cell power generation systems using solid hydrogen storage materials as hydrogen storage carriers and their application in twowheelers in recent years.
基金supported by the National Natural Science Foundation of China (No. 20673093)the Natural Science Foundation of Hebei Province, China (No. B2007000303)
文摘The effects of annealing treatment on the microstructure and electrochemical properties of low-Co LaNi 3.55 Mn 0.35 Co 0.20 Al 0.20 Cu 0.75 Fe 0.10 hydrogen storage alloys were investigated. X-ray diffraction (XRD) analysis indicated that annealing treatment remarkably reduced the lattice strain and defects, and increased the unit-cell volume. The optical microscope analysis showed that the as-cast alloy had a crass dendrite microstructure with noticeable composition segregation, which gradually disappeared with increasing annealing temperature, and the micro-structure changed to an equiaxed structure after annealing the alloy at 1233 K. The electrochemical tests indicated that the annealed alloys demonstrated much better cycling stability compared with the as-cast one. The capacity retention at the 100th cycle increased from 90.0% (as-cast) to 94.7% (1273 K). The annealing treatment also improved the discharge capacity. However, the high rate dischargeability (HRD) value of the annealed alloy slightly dropped, which was believed to be ascribed to the decreased exchange current density and the hydrogen diffusion coefficient in alloy bulk.
基金supported by the Key Projects in International Science and Technology Cooperation from Ministry of Science and Technology of the PRC (2006DFB52550, 2007DFA51020)the National Natural Science Foundation of China (20363001)
文摘In order to investigate the effect of substituting La with Pr on structural and hydrogen storage properties of La-Mg-Ni system (AB3.5-type) hydrogen storage alloys, a series of La0.65-xPrxNd0.12Mg0.23Ni3.4Al0.1(x=0, 0.10, 0.15, 0.2) hydrogen storage alloys were prepared. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) analyses revealed that two alloys (x=0.0 and 0.10) were composed of (La,Mg)2(Ni,Al)7 phase, La(Ni,A1)5 phase and (La,Mg)Ni2 phase, while other alloys (x=0.15 and 0.20) consisted of (La,Mg)2(Ni,A1)7 phase, La(Ni,A1)5 phase, (La,Mg)Ni2 phase and (La,Mg)(Ni,A1)3 phase. All alloys showed, however, only one pressure plateau in P-C isotherms. The Pr/La ratio in alloy composition influenced hydrogen storage capacity and kinetics properties. Electrochemical studies showed that the discharge capacity decreased from 360 mAh/g (x=-0.00) to 335 mAh/g (x=-0.20) as x increased. But the high-rate dischargeability (HRD) of alloy electrodes increased from 26% (x=0.00) to 56% (x=-0.20) at a discharge current density of Id=1800 mA/g. Anode polarization measurements were done to further understand the electrochemical kinetics properties after Pr substitution.
文摘The effects of surface treatment, particle size distribution,rare earth composition and B additive on the high rate discharge performance of hydrogen storage alloys were investigated. It is found that the activity, discharge capacity and high rate dischargeability of the alloys are improved after physical and chemical modification as a result of the increase of the surface area and formation of the electrocatalysis layers, which increase both the electrochemical reaction rate on the alloy surface and H diffusion rate in the alloy bulk. It is also found that both the over-coarse and over-fine particle size increase the contact resistance of the electrode, resulting in a decrease of discharge capacity, deterioration of high rate dischargeability and lower discharge plateau. In another word, a suitable particle size distribution can enhance the alloy activity, discharge capacity and high rate dischargeability. In addition, the high rate dischargeability is enhanced by increasing La content and decreasing Ce content of the alloy composition because of enlargement of the unit cell volume and the improvement of the surface activity. Moreover, B additive resultes in the formation of the second phase, and makes the alloys easier pulverization, which greatly improves the activity, discharge capacity and high rate dischargeability.
文摘The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the 0.2 C discharge capacity of as-cast LPCNi3.55Co0.75Mn0.4Al0.3 alloy increases with the increase of the thickness of the ingots. As-east alloy with the thickness of 10 mm shows better activation property, higher 1C discharge capacity and better cyclic stability than others. It is mainly contributed to its larger unit cell volume and less internal stress. Annealed LPCNi3.55Co0.75Mn0.4Al0.3 alloy with the thickness of 3 mm shows much better comprehensive electrochemical properties than as-east one; The cyclic. stability of the alloy with the thickness of 6 mm and the activation properties of the alloys with the thickness of 3 similar to 6 mm are improved after annealing. It is mainly owing to the great release of internal stress and the decrease of the segregation of Mn in the alloys.
文摘Hydrogenation kinetics of MLNi3.8(Co,Mn,Al)1.2 and MLNi3.7(Co,Mn,Al)1.2Cu0.1 alloy in α + β phase at the temperatUre range of 30 ~70 ℃ has been studied. The kinetic mechanism of hydrogen absorption is not affected by initial hydrogen pressure. Temperature does not influence the rate of hydrogen absorption obviously. In the prior and later period of hydrogen absorption the rate-controlling step is chemical reaction and hydrogen diffusion in the hydride phase respectively for MLNi3.8(Co,Mn,Al)1.2 alloy. Adding Cu, the rate-controlling step changes from chemical reaction to the nucleation and growth of β phase in the prior period and the process of hydrogen absorption still controlled by diffusion in the later period.
文摘The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage alloys were compared with those of the high-Co AB_5 typehydrogen storage alloy as well. The results showed that the faster the cooling of the low-Cohydrogen storage alloy is, the better homogeneity of the chemical composition for the alloy and thelonger cycle life of the battery are, but the electrochemical discharge capacity and high-ratedischarge ability are reduced. The high-rate discharge ability and charge retention of MH-Nibatteries for the conventional as-cast annealed low-Co hydrogen storage alloy were superior to thosefor the rapidly quenched low-Co hydrogen storage alloy and the high-Co hydrogen storage alloy, buta little inferior in the cycle life.
文摘The kinetics of liquid-phase hydrogenation of toluene catalyzed by MlNi_5 was studied by investigating the influences of the reaction temperature and pressure on the mass transfer-reaction processes inside the slurry. The results show that the reaction rate accelerates when the reaction temperature increases, and reaches its maximum at about 490 K, but if temperature is higher than 510 K, the reaction rate decreases rapidly. The whole reaction process is controlled by the reaction at the surface of the catalyst particles. The mass transfer resistance at gas-liquid interface and that from the bulk liquid phase to the surface of the catalyst particle can be neglected. The apparent reaction rate is zero order for toluene concentration and first order for hydrogen concentration in the liquid phase. The kinetic model is obtained. The kinetic model fits the experimental data very well. The apparent activation energy of the hydrogen absorption reaction of MlNi_5-toluene slurry system is 41.01 kJ·mol^(-1).
基金This research was financially supported by the State Key Project for Fundamental Research (G2 000026406).]
文摘The hydrogen storage properties of Ti1.2Fe+xCa (x=1%, 3% and 5% in mass fraction) alloys was investigated. Results stow that the modified alloys can be activated without any thermal treatment at room temperature due to the addition of Ca and excess Ti in (lie alloys. Hydrogen storage properties of these modified alloys vary with Ca amount and reaction temperature. In addition, the influence mechanism of the addition of Ca and excessive Ti on the activation behavior and hydrogen storage capacity of the alloys was discussed.
文摘In this paper,a simulation model for the temperature field in the solidification process and microstructure distribution is presented. Then, the result of simulation for the final microstructure distribution is compared with experiment using 10-Kg ingot of MlNi3.55Al0.3Mn0.4CO0.75 (Ml: Lanthanum-rich Mischmetal) hydrogen stor- age alloy cast in a mould, which agrees with the experiment well. Finally, in order to obtain the expected as-cast microstructure distribution of 15-Kg ingot of MlNi3.55Al0.3Mn0.4Co0.75 alloy, the size of Cu mould is optimized using the model described. The optimized mould is then made and the alloy is cast in it, the expected as-cast microstructure distribution is obtained.
基金supported by the National High-Tech Research and Development Program of China (No.2006AA11A159)
文摘In order to improve the cycling stability of AB5 type alloy electrodes,rapid quenching technology and new alloy composition design were employed.A hydrogen storage alloy with nominal composition La0.6Ce0.4Ni3.6Co0.65Mn0.4Al0.2Ti0.05(FeB)0.1 was prepared by vacuum magnetic levitation melting under high purity argon atmosphere,followed by rapid quenching at different cooling rates.XRD results show that all alloys exhibit the single-phase CaCu5-type structure.Electrochemical tests indicate that rapid quenching can slightly improve the cycling life of the alloy.Nevertheless,the high-rate dischargeability of the quenched alloys is lower than that of the as-cast alloy.
基金financially supported by the Natural Science Foundation of Hebei Province(Nos.E2019203414,E2020203081 and E2019203161)the National Natural Science Foundation of China(Nos.51701175 and 51971197)+1 种基金the Innovation Fund for the Graduate Students of Hebei Province(No.CXZZBS2020062)the Doctoral Fund of Yanshan University(No.BL19031)
文摘Rare earth-Mg-Ni-based alloys with superlattice structures are new generation negative electrode materials for the nickel metal hydride batteries.Among them,the novel AB_(4)-type superlattice structure alloy is supposed to have superior cycling stability and rate capability.Yet its preparation is hindered by the crucial requirement of temperature and the special composition which is close to the other superlattice structure.Here,we prepare rare earth-Mg-Ni-based alloy and study the phase transformation of alloys to make clear the formation of AB_(4)-type phase.It is found Pr_(5)Co_(19)-type phase is converted from Ce_(5)Co_(19)-type phase and shows good stability at higher temperature compared to the Ce_(5)Co_(19)-type phase in the range of 930-970℃.Afterwards,with further 5℃increasing,AB_(4)-type superlattice structure forms at a temperature of 975℃by consuming Pr_(5)Co_(19)-type phase.In contrast with A_(5)B_(19)-type alloy,AB_(4)-type alloy has superior rate capability owing to the dominant advantages of charge transfer and hydrogen diffusion.Besides,AB_(4)-type alloy shows long lifespan whose capacity retention rates are 89.2%at the 100;cycle and 82.8%at the 200;cycle,respectively.AB_(4)-type alloy delivers 1.53 wt.%hydrogen storage capacity at room temperature and exhibits higher plateau pressure than Pr_(5)Co_(19)-type alloy.The work provides novel AB_(4)-type alloy with preferable electrochemical performance as negative electrode material to inspire the development of nickel metal hydride batteries.
文摘The hydriding/dehydriding thermodynamic properties of the slurry system formed by suspending La rich mischmetal nickel hydrogen storage alloy (MlNi 5) in Benzene (C 6H 6) were investigated. The pressure composition isotherms for both the alloy powder and the slurry suspended with MlNi 5 were measured at several temperatures(10, 20, 30, 40 ℃). The standard enthalpy of formation Δ H ° and standard entropy of formation Δ S ° for the alloy powder with and without benzene were determined respectively. The experimental results show that the values of Δ H ° and Δ S ° for the hydriding reaction of hydrogen storage alloy (MlNi 5) of the slurry system and the gas solid system are all very close.
基金supported by Hi-Tech Research and Development Program (863) of China (2006AA11A159)
文摘Surface-treated MmNi3.55Co0.75Mn0.4Al0.3 alloy as negative electrode material of nickel-metal hydride battery was employed to improve the high-rate dischargeability. Surface treatment was realized by dipping and stirring the alloy into a HCl aqueous solution with various concentrations at room temperature. The microstructure of the alloy before and after surface treatment was analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The electrochemical properties before and after surface treatment were compared, and the alloy treated in 0.025 mol/L HCl solution showed the optimal high-rate dischargeability.
基金the National Advanced Materials Committee of China andthe National Natural Science Foundation of China(Grunt NO.5
文摘The crystal structure, phase abundance and the electrochemical properties of Zr(Mn1-x Nix)2 (0.40 ≤x≤0.75) alloys were investigated by means of XRD, Rietveld refinement method and electrochemical measurements. The alloys are multiphase. C15 Laves phase occurs as a main phase accompanying with C14 phase and other minor phases, indicating that Ni element is C15-stabilized element for ZrMn2 alloy. The phase abundance and lattice parameters of Laves phase are influenced significantly by Ni substitution. The Zr(Mn0.45 Ni0.55)2 alloy with the highest amount of C15 phase exhibits the maximum electrochemical capacity of 242m Ah/g. C14 phase occurring in Zr-Mn-Ni alloys is beneficial for the electrochemical kinetics of hydride electrodes.
基金supported by the National Natural Science Foundation of China (50471011, 50525101)
文摘The effects of rapid solidification on the microstructure and electrochemical properties of Nd0.8Mg0.2(Ni0.8Co0.2)3.8 alloy were systematically investigated.The microstructure of alloys was characterized by scanning electron microscopy(SEM),X-ray diffractometer(XRD) and transmission electron microscopy(TEM).It was found that the melt-spun Nd0.8Mg0.2(Ni0.8Co0.2)3.8 ribbons became thinner and the average grain size of the ribbons became smaller with increasing wheel speed.A fraction of amorphous phase was obs...
文摘Investigation of alloy structure shows that La2-xMgxNi7 (x = 0.3 - 0.8) alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is great, resulting in a linear decrease of the unit cell parameters of main phases and increase of hydrogen absorption/desorption plateau as Mg content increases. Electrochemical measurements show that as the Mg content increases, the discharge capacity of alloy electrodes first increases and then decreases. The cyclic stability presents a deteriorative trend. La1.4Mg0.6 Ni7 alloy electrode exhibits the maximum electrochemical discharge capacity (378 mAh·g^-1), and the La1.6Mg0.4Ni7 alloy electrode shows the best cyclic stability (S270 = 81%).
文摘In ordertoimprovethe dischargecapacity of Ti2 Ni hydrogen storage alloy, the phases and effecton the property for Ti Nialloy with alittle La( La contentisbetween 5 25 wt% and12 62 wt%) were investigated in this paper. It is found that La exists in the form ofLaNi5 ,thesecond phase,in Ti Nialloy when La> 8 wt% . LaNi5 phasecaneffectivelyim provethe activity property and discharge capacity of Ti Ni alloy. While the soluble Ti inmain phase Ti2 Niisadverseto hydrogen adsorption desorption cycle and itshould be dimin ished .
文摘Rare earth compositions, La, Ce and Pr in Mm(NiCoMnAl)(5) hydrogen storage alloy, were arranged by uniform design method. The discharge performances and kinetics parameters including capacity, exchange current density, symmetry factor and hydrogen diffusion coefficient of the alloy at -40degreesC, were tested in standard tri-electrode cell. And linear regression method was used to analyze the effect of rare earth compositions on the performances of hydrogen storage alloys. The results show that the capacities of the alloys are positively correlative to the square of Ce content at -40degreesC and under both 0.4 and 0.2C rate. The kinetics parameters and hydrogen diffusion coefficient indicate that the low-temperature performances of the alloys are mainly controlled by hydrogen diffusion process, and the surface electrochemical reaction affects the low-temperature performances to a certain extent. The low-temperature discharge capacities of the battery were also tested. The results show excellent low-temperature performances. The battery delivers 69.6% of its room-temperature capacity at -40degreesC and 0.2C rate, 77.7% at -40degreesC and 0.4C rate, 59.1% at -45degreesC and 0.2C rate.