The degradation of partially hydrolyzed polyacrylamide(HPAM) found in alkaline/surfactant/polymer flooding sewage was investigated using Fenton-type reagents. Different Fenton reagent treatments for HPAM degradation w...The degradation of partially hydrolyzed polyacrylamide(HPAM) found in alkaline/surfactant/polymer flooding sewage was investigated using Fenton-type reagents. Different Fenton reagent treatments for HPAM degradation were compared. The effects of pH, hydrogen peroxide(H_(2)O_(2)), ferrous ion(Fe^(2+)), and tartaric ion(C_(4)H_(4)O_(6)^(2-)) concentrations were studied. The degradation reaction occurred within a wide range of pH(3–9). The HPAM degradation performance of photo-Fenton processes using solar light and UV were compared with that of the Fenton process. The degradation rate was found to be strongly dependent on the H_(2)O_(2)/Fe^(2+)/C_(4)H_(4)O_(6)^(2-)molar ratio. The HPAM degradation efficiency was 90%, and the chemical oxygen demand removal efficiency was 85%. HPAM could be degraded into a compound with a lower molecular weight, but it was difficult to achieve complete mineralization to CO_(2). The presence of intermediate products hindered further oxidation in the Fenton process.展开更多
The effect of salt solutions(NaCl,Na2SO4 and CaCl2) on the conformational properties of partially hydrolyzed polyacrylamide(HPAM) was investigated by using static laser light scattering(SLLS).The special interaction b...The effect of salt solutions(NaCl,Na2SO4 and CaCl2) on the conformational properties of partially hydrolyzed polyacrylamide(HPAM) was investigated by using static laser light scattering(SLLS).The special interaction between CaCl2 solution and HPAM was also researched.Experimental results show that the chain structure of HPAM is interrelated with the charge density,the kind and the concentration of salt solutions.The mean-square radius of gyration(Rz) and the second virial coefficient(A2) of HPAM decrease with increasing concentration of salt solutions,and the salt effect tends towards the maximum when the concentration of salt solution is increased to some amount.展开更多
Selective flocculation is a new method to solve the problem of China's bauxite de-silication besides flotation and reverse flotation. The method of selective flocculation of bauxite using hydrolyzed polyacrylamide...Selective flocculation is a new method to solve the problem of China's bauxite de-silication besides flotation and reverse flotation. The method of selective flocculation of bauxite using hydrolyzed polyacrylamide as flocculant was experimented and evaluated. The results of diaspore and kaolinite single mineral settling tests show that the difference between settlement yield of kaolinite(settling 15 min) and diaspore(settling 3 min) increases from 16% to 60% by adding flocculant at pH=7. Results of selective flocculation experiment of bauxite show that the higher concentrate grade(65.75) and Al-Si ratio(7.34) could be obtained with sodium carbonate as dispersant compared with sodium hexametaphosphate; under the action of flocculating agent, the concentrate grade and Al-Si ratio increase to 67.99 and 9.01. These results could meet the requirements of Bayer production, and the simpler process was expected to cost far less than traditional flotation method and a promising de-silication method of bauxite.展开更多
The IFTs(Interfacial tension)of petroleum carboxylate/alkaline/HPAM(Hydrolyzed polyacrylamide)flooding system with Daing crude oil and the effects of petroleum carboxylate and alkaline on viscoaity of HPAM solution we...The IFTs(Interfacial tension)of petroleum carboxylate/alkaline/HPAM(Hydrolyzed polyacrylamide)flooding system with Daing crude oil and the effects of petroleum carboxylate and alkaline on viscoaity of HPAM solution were studied.There exists remarkable synergism between HPAM and petroleum carboxylate,and the introduction of HPAM into petroleum carboxylate/alka- line system leads the lowering of IFTs against Daqing crude oil,The introduction of petroleum carboxylate into solution of HPAM also leads the decreasing of viscosity,but the extent of viscosity decreasing is much lower than that caused by inorganic salts such as NaCl and CaCl_2.展开更多
基金the Northeast Petroleum University Youth Science Foundation (No. 2019QNL-35)Guiding Science and Technology Plan Project of Daqing (No. zd-2021-39)。
文摘The degradation of partially hydrolyzed polyacrylamide(HPAM) found in alkaline/surfactant/polymer flooding sewage was investigated using Fenton-type reagents. Different Fenton reagent treatments for HPAM degradation were compared. The effects of pH, hydrogen peroxide(H_(2)O_(2)), ferrous ion(Fe^(2+)), and tartaric ion(C_(4)H_(4)O_(6)^(2-)) concentrations were studied. The degradation reaction occurred within a wide range of pH(3–9). The HPAM degradation performance of photo-Fenton processes using solar light and UV were compared with that of the Fenton process. The degradation rate was found to be strongly dependent on the H_(2)O_(2)/Fe^(2+)/C_(4)H_(4)O_(6)^(2-)molar ratio. The HPAM degradation efficiency was 90%, and the chemical oxygen demand removal efficiency was 85%. HPAM could be degraded into a compound with a lower molecular weight, but it was difficult to achieve complete mineralization to CO_(2). The presence of intermediate products hindered further oxidation in the Fenton process.
基金Project(50673033) supported by the National Natural Science Foundation of China
文摘The effect of salt solutions(NaCl,Na2SO4 and CaCl2) on the conformational properties of partially hydrolyzed polyacrylamide(HPAM) was investigated by using static laser light scattering(SLLS).The special interaction between CaCl2 solution and HPAM was also researched.Experimental results show that the chain structure of HPAM is interrelated with the charge density,the kind and the concentration of salt solutions.The mean-square radius of gyration(Rz) and the second virial coefficient(A2) of HPAM decrease with increasing concentration of salt solutions,and the salt effect tends towards the maximum when the concentration of salt solution is increased to some amount.
基金Project(2005CB623701)supported by the National Key Basic Research Program(973)of China
文摘Selective flocculation is a new method to solve the problem of China's bauxite de-silication besides flotation and reverse flotation. The method of selective flocculation of bauxite using hydrolyzed polyacrylamide as flocculant was experimented and evaluated. The results of diaspore and kaolinite single mineral settling tests show that the difference between settlement yield of kaolinite(settling 15 min) and diaspore(settling 3 min) increases from 16% to 60% by adding flocculant at pH=7. Results of selective flocculation experiment of bauxite show that the higher concentrate grade(65.75) and Al-Si ratio(7.34) could be obtained with sodium carbonate as dispersant compared with sodium hexametaphosphate; under the action of flocculating agent, the concentrate grade and Al-Si ratio increase to 67.99 and 9.01. These results could meet the requirements of Bayer production, and the simpler process was expected to cost far less than traditional flotation method and a promising de-silication method of bauxite.
文摘The IFTs(Interfacial tension)of petroleum carboxylate/alkaline/HPAM(Hydrolyzed polyacrylamide)flooding system with Daing crude oil and the effects of petroleum carboxylate and alkaline on viscoaity of HPAM solution were studied.There exists remarkable synergism between HPAM and petroleum carboxylate,and the introduction of HPAM into petroleum carboxylate/alka- line system leads the lowering of IFTs against Daqing crude oil,The introduction of petroleum carboxylate into solution of HPAM also leads the decreasing of viscosity,but the extent of viscosity decreasing is much lower than that caused by inorganic salts such as NaCl and CaCl_2.