An investigation was made on the influences of mechanical stirring on microstructure of hyper-eutectic Al-30%Si alloy (inmass fraction) during solidification. The primary Si crystals formed in the alloy melt were grad...An investigation was made on the influences of mechanical stirring on microstructure of hyper-eutectic Al-30%Si alloy (inmass fraction) during solidification. The primary Si crystals formed in the alloy melt were gradually changed from elongated platelets tonear-spherical shapes by mechanical stirring. The spheroidization of primary St crystals occurs by the mechanism of bending and fractureof Si platelets, wear and collision between Si crystals, and coalescence of small Si particles. The influence of under-cooling and coolingrate of the alloy melt on primary Si crystals of semi-solid processed alloys is investigated as well. The increase of under-cooling andcooling rate decreases the size of primary Si crystals.展开更多
Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found ...Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found to have finer Si particles （～5μm） compared to the squeeze-cast specimen （10-25μm）.The tensile strength and elongation of the spray-cast specimen are also higher than those of the squeeze cast one.It was considered that the increased mechanical properties of the spray-cast specimen were mainly due to finer size of the Si particles distributed in Al matrix.展开更多
文摘An investigation was made on the influences of mechanical stirring on microstructure of hyper-eutectic Al-30%Si alloy (inmass fraction) during solidification. The primary Si crystals formed in the alloy melt were gradually changed from elongated platelets tonear-spherical shapes by mechanical stirring. The spheroidization of primary St crystals occurs by the mechanism of bending and fractureof Si platelets, wear and collision between Si crystals, and coalescence of small Si particles. The influence of under-cooling and coolingrate of the alloy melt on primary Si crystals of semi-solid processed alloys is investigated as well. The increase of under-cooling andcooling rate decreases the size of primary Si crystals.
文摘Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found to have finer Si particles （～5μm） compared to the squeeze-cast specimen （10-25μm）.The tensile strength and elongation of the spray-cast specimen are also higher than those of the squeeze cast one.It was considered that the increased mechanical properties of the spray-cast specimen were mainly due to finer size of the Si particles distributed in Al matrix.