A binder phase of TiO based cermets, a kind of imitated gold materials, was developed by adding active element Si to Fe-Cr alloy, and the related mechanisms were studied. The wettability, matching in thermodynamics an...A binder phase of TiO based cermets, a kind of imitated gold materials, was developed by adding active element Si to Fe-Cr alloy, and the related mechanisms were studied. The wettability, matching in thermodynamics and interracial strength were investigated by the high temperature sessile drop method and element area scanning. The linear expansion coefficients of the materials were measured using TAH100 thermal analyzer. The results show that the wettability of Fe-Cr alloy on TiO are small, with a wetting angle about 90°. After adding some Si in Fe-Cr alloy, its wetting angle can be decreased to about 25°, the interracial reactions can be prevented effectively and high interface binding can be formed. Fe-25% Cr-1.5% Si matches the thermal expansion coefficient of TiO, so it is a kind of relatively perfect binder for TiO based cermets imitated gold.展开更多
The effect of trace amount of active element Si on the wetting and interface characteristics of 1Cr18Ni11Nb/TiO was investigated. Based on the results, a new binder phase for TiO based cermets imitated gold materials ...The effect of trace amount of active element Si on the wetting and interface characteristics of 1Cr18Ni11Nb/TiO was investigated. Based on the results, a new binder phase for TiO based cermets imitated gold materials was developed, and the related mechanisms were studied. The results indicated that there was small wet-ability of the 1Cr18Ni11Nb alloy on TiO, and the interface binding strength of 1Cr18Ni11Nb/TiO was low. 1.5%Si in 1Cr18Ni11Nb could not only make the alloy wet TiO, but also lead to mutual dissolving near the interface, forming high interface binding strength and matching with the thermal expansion coefficient of TiO.展开更多
文摘A binder phase of TiO based cermets, a kind of imitated gold materials, was developed by adding active element Si to Fe-Cr alloy, and the related mechanisms were studied. The wettability, matching in thermodynamics and interracial strength were investigated by the high temperature sessile drop method and element area scanning. The linear expansion coefficients of the materials were measured using TAH100 thermal analyzer. The results show that the wettability of Fe-Cr alloy on TiO are small, with a wetting angle about 90°. After adding some Si in Fe-Cr alloy, its wetting angle can be decreased to about 25°, the interracial reactions can be prevented effectively and high interface binding can be formed. Fe-25% Cr-1.5% Si matches the thermal expansion coefficient of TiO, so it is a kind of relatively perfect binder for TiO based cermets imitated gold.
文摘The effect of trace amount of active element Si on the wetting and interface characteristics of 1Cr18Ni11Nb/TiO was investigated. Based on the results, a new binder phase for TiO based cermets imitated gold materials was developed, and the related mechanisms were studied. The results indicated that there was small wet-ability of the 1Cr18Ni11Nb alloy on TiO, and the interface binding strength of 1Cr18Ni11Nb/TiO was low. 1.5%Si in 1Cr18Ni11Nb could not only make the alloy wet TiO, but also lead to mutual dissolving near the interface, forming high interface binding strength and matching with the thermal expansion coefficient of TiO.
