Impact-abrasive Wear Behavior of ZTA and NbC Reinforced Fe60 Matrix Composites

The impact-abrasive wear behavior of ZTA(zirconia toughened alumina)particle(ZTAp)and NbC particle(NbCp)reinforced Fe60 matrix composites(ZTAp-NbCp/Fe60)were investigated.Specimens of pure Fe60 matrix material,NbCp reinforced Fe60 composite(NbCp/Fe60)and ZTAp-NbCp/Fe60 with different contents of ZTAp were prepared through vacuum sintering and tested on an MLD-10B Impact Wear Rig.As revealed by the results,NbCp could strengthen Fe60 matrix,and had fine grain strengthening effect on Fe60matrix.When the mass fraction of ZTAp was 5%-15%,the impact-abrasive wear performance of ZTAp-NbCp/Fe60 composites was better than that of Fe60 and NbCp/Fe60.When the mass fraction was 15%,the ZTApNbCp/Fe60 had the best performance.ZTAp could weaken the impact and wear effect of abrasive particles on the composite and protect the matrix.Cracks occured at the interface and at defects in the ZTAp.The former leaded to ZTAp shedding,while the latter leaded to ZTAp fracturing.In both cases,the performance of the composite material would decrease.

Effect of Si content on impact-abrasive wear resistance of Al2O3p/steel composites prepared by squeeze casting

The 40Cr steel matrix composites were reinforced with Al203 particulates （Al2O3p） through Si adding to improve the impact-abrasive wear resistance, in which Si powder ranging up to 25% of the AlzO3p weight was added into the Al2O3p preforms; then, the composites were fabricated by squeeze casting. For all composites, alumina particles are evenly distributed, and Si powder is dissolved in the matrix. Without Si powder addition, the 40Cr steel matrix contains only pearlite; however, ferrite appears and increases with Si powder addition. In the impact-abrasive wear tests, the impact frequency is 80 min^-1 and the impacting energy is 2 J. With increasing Si powder, the wear of the composites first decreases obviously, reaches the minimum at 10% and then increases. The effect of Si addition on the wear resistance can be attributed to two reasons： one is increasing the hardness of the matrix, and the other is improving the interfacial bonding between Al2O3p and steel. The wear mechanism of the composites is abrasive wear when the Si powder is 〈 10 wt%. Otherwise, it is a mixed mode of abrasive and delamination wear.

Effects of Ni content and tempering temperatures on microstructure and properties of medium-carbon cast steel

The microstructure evolution and properties of medium-carbon cast steel alloyed with different Ni contents after tempering at various temperatures have been investigated.The addition of 0.47-1.59 wt.%Ni content results in the formation of 16%-36% retained austenite(RA).The blocky and irregular-polygonal RA mainly forms along the prior austenite grain boundaries,and the tempering temperature does not affect the RA content.The hardness of medium-carbon cast steel is affected by the precipitation of carbides and the hardness of martensite.Excessive RA content is the main cause of intergranular impact rupture and low impact energy.The long-strip carbides formed after tempering at 320℃ would further reduce the impact energy of medium-carbon cast steel.When tempering at 220 and 380℃,the increase in impact energy is attributed to the formation of rod-like and spherical carbides and the low-carbon martensite.For the medium-carbon cast steel with high impact energy,its impact-abrasive wear resistance is more excellent.Micro-cutting and delamination are the primary wear mechanisms.