The influence of different surface coatings of NiTi shape memory allays was examined using in vitro testing methods. Plates of superelastic nickel-titanium shape memory allay （ NiTi ） were coated with calcium phosph...The influence of different surface coatings of NiTi shape memory allays was examined using in vitro testing methods. Plates of superelastic nickel-titanium shape memory allay （ NiTi ） were coated with calcium phosphates （ hydroxyapatite ） by high-temperature plasma-spraying or by dip-coating. The biocompatibility was tested in vitro by cultivation of isolated human granulocytes and whole blood cells. As substrates, pure NiTi, plasma-spray-coated NiTi and dip-coated NiTi were used. Isolated granulocytes showed an increased adhesion to both calcium phosphate-coated NiTi samples. Compared to non-coated NiTi or dip-coated NiTi, the number of dead granulocytes adherent to plasma-sprayed surfaces was significantly increased （ p 〈 0.01 ）. Whether the d/f- ferences in apoptosis of granulocytes on dip-coated vs plasma-sprayed coatings observed are due to differences in material surface morphologies has to be analyzed in further studies. Because of the cellular interactions with the coating layers, h is likely that the results obtained are not caused by the underlying NiTi but due to the coating itself.展开更多
In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc wel...In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.展开更多
文摘The influence of different surface coatings of NiTi shape memory allays was examined using in vitro testing methods. Plates of superelastic nickel-titanium shape memory allay （ NiTi ） were coated with calcium phosphates （ hydroxyapatite ） by high-temperature plasma-spraying or by dip-coating. The biocompatibility was tested in vitro by cultivation of isolated human granulocytes and whole blood cells. As substrates, pure NiTi, plasma-spray-coated NiTi and dip-coated NiTi were used. Isolated granulocytes showed an increased adhesion to both calcium phosphate-coated NiTi samples. Compared to non-coated NiTi or dip-coated NiTi, the number of dead granulocytes adherent to plasma-sprayed surfaces was significantly increased （ p 〈 0.01 ）. Whether the d/f- ferences in apoptosis of granulocytes on dip-coated vs plasma-sprayed coatings observed are due to differences in material surface morphologies has to be analyzed in further studies. Because of the cellular interactions with the coating layers, h is likely that the results obtained are not caused by the underlying NiTi but due to the coating itself.
基金Armament Research Board (ARMREB),New Delhi for funding this projectwork (Project No MAA/03/41)
文摘In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.